The examination of total amounts of heavy metals (Hg, Cd, Cu, Pb, Cr, Ni, Zn) was conducted in the outflow from a sewage treatment plant and in the waters and sediments of ponds supplied with them. As the water passed through the pond system, a decrease of heavy metal concentrations in the post-treatment sewage water supplying the ponds was observed. The highest concentrations of heavy metals were found in the outflow from the sewage treatment plant and lower concentrations were observed in the water of pond 1 (except for Zn), which was the direct receiver of post-treatment sewage, while the lowest values were noted in the final pond. The concentration of heavy metals in the sediments decreased in consecutive ponds. The highest concentrations were determined in the sediment of pond 1 that received the post-treatment sewage directly from the sewage treatment outflow, whereas the lowest values were estimated in the sediments of pond number 4, which was the final pond in the system.
Kompozyty polimerowo-ceramiczne są powszechnie stosowane jako opakowania elektroniczne. W artykule przedstawiono właściwości dielektryczne kompozytów złożonych z termoplastycznych polimerów PET i PPS i napełniacza w postaci cząstek ceramicznych tytanianu baru (BT). Określono wpływ stężenia napełniacza na przenikalność elektryczną oraz stratność dielektryczną tych kompozytów.
EN
Polymer/ceramic nanocomposites designed for electronic packaging. The dielectric properti of the composites made from polyethylene terephthalate (PET), polyphenylene sulphide (PPS) an barium titanate (BT) were studied as a function of BaTi03 fraction. Processing parameters ε optimized in order to obtain the composites with appropriate dielectric properties like dielectri permittivity e' and dielectric losses ε.
4
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
W badaniach z plastizolem PVC składającym się z ftalanu di(2-etyloheksylowego) i modyfikatora, jakim był glikol poli(tlenku etylenowego) o masie cząsteczkowej 400, 1000, 2000, 4000 i 6000 wprowadzony do plastizolu w ilości od 1 do 14% wag, wyznaczono: współczynnik dylatancyjny, parametr wewnętrznego strukturowania i energię aktywacji lepkiego płynięcia. Na podstawie otrzymanych wyników stwierdzono, że optymalna ilość dodatku modyfikującego w plastizolu PVC powinna wynosić od 1 do 2% wag. Badania fizykochemiczne i mechaniczne określające stopień wymywania substancji rozpuszczalnych w wodzie z błony, temperaturę mięknięcia, wytrzymałość na rozerwanie, wydłużenie względne przy rozerwaniu oraz twardość, potwierdziły jednoznacznie najlepsze właściwości błon zawierających ok. 2% wag. PEO-4000 lub PEO-6000.