Workability behavior of hybrid copper matrix composites synthesized by powder metallurgy technique

Ilayaraja K., Ranjith Kumar P., Anandakrishnan V., Sathish N., Ravichandran V., Ravikumar R.

Mechanics and Mechanical Engineering

2017

Vol. 21, nr 2

207--216

Copper based hybrid composite materials with 5wt.% of titanium dioxide and 0wt.%, 2wt.% and 4wt.% of graphite were produced using powder metallurgy technique. The presence and distribution of titanium dioxide and graphite reinforcements were examined in the copper matrix using scanning electron microscopic and energy dispersive spectroscopic analysis. To investigate the workability behavior of the sintered composite preforms, cold upset tests were conducted and various stresses and forming parameters were determined and using that various stress ratio parameters such as the true axial stress versus the true effective stress, the true hoop stress versus the true effective stress, the true hydrostatic stress versus the true effective stress and the true hoop stress versus the true hydrostatic stress were calculated and correlated with the true axial strain. From the studies, the workability of the composite is found to increase with increasing graphite content due to increase in lubricating affect by graphite addition.

Badanie odkształceń sieci krystalicznej w implantowanej warstwie epitaksjalnej GaN osadzonej metodą MOCVD na podłożu szafirowym o orientacji [001]

Wójcik M., Gaca J., Wierzbicka E., Turos A., Strupiński W., Caban P., Sathish N., Pągowska K.

Materiały Elektroniczne

2011

T. 39, nr 4

22-31

W pracy zbadano warstwy epitaksjalne GaN o grubości 1000 nm implantowane jonami Ar++ w zakresie dawek od 7 ⋅ 1013 cm-2 do 1 ⋅ 1015 cm-2. Wyznaczono zakres proporcjonalności pomiędzy dawką a średnią zmianą odległości pomiędzy płaszczyznami równoległymi do powierzchni swobodnej implantowanego kryształu GaN. Wyznaczono korelację pomiędzy wielkością dawki jonów a rozkładem odkształceń sieci krystalicznej występujących w kierunku [001] w warstwie epitaksjalnej. Stwierdzono, że odkształcane są płaszczyzny sieciowe równolegle do interfejsu, a komórka elementarna warstwy implantowanej ulega tetragonalizacji.

In the present work 1000 nm epitaxial GaN layer implanted with Ar++ ions in the dose range from 7 ⋅ 1013 cm-2 to 1 ⋅ 1015 cm-2 was investigated. The range of linearity between dose and the average change of interplanar spacing of planes parallel to the surface of the implanted GaN crystal was determined. It was found a correlation between the distribution of displaced atoms and lattice deformation occurring in the [001] direction in the epitaxial layer. It was also observed the tetragonalization of unit cell due to implantation.

Badanie heterostruktur związków AIIIN zawierających warstwy ultracienkie

Wójcik M., Gaca J., Turos A., Strupiński W., Caban P., Borysiuk J., Pathak A. P., Sathish N.

Materiały Elektroniczne

2008

T. 36, nr 4

61-84

Niedopasowanie sieciowe pomiędzy szafirowym podłożem i warstwą epitaksjalną GaN prowadzi do powstawania naprężeń i dyslokacji niedopasowania. Jest ono także główną przyczyną trudności, na jakie napotyka wzrost epitaksjalny warstw związków AIIIN. Próby rozwiązania tego problemu polegają m.in. na stosowaniu warstwy buforowej [1-3]. Niekiedy może ona zawierać supersieć o bardzo krótkiej fali modulacji składu chemicznego, która obniża gęstość dyslokacji, a także poprawia strukturę docelowej warstwy epitaksjalnej [4-5]. W artykule prezentowane są wyniki badań systemów epitaksjalnych związków AIIIN, odkładanych na podłożu szafirowym o orientacji 001, dotyczące struktury warstw AlN, AlGaN oraz GaN o bardzo małej grubości, a także cech budowy krystalicznej warstwy buforowej i jej wpływu na wzrost i strukturę docelowej warstwy epitaksjalnej GaN.

The lattice misfit between Al2O3 substrate and epitaxial GaN layer generates stresses and numerous misfit dislocations. This leads to difficulties in the epitaxial growth of the GaN layer. The attempts to resolve this growth problems consist in employing the buffer layer with the ultra thin period AlGaN/GaN superlattice. This superlattice is expected to reduce the dislocations density and improve the structure of epitaxial GaN layer. In this work we present the results of the investigation of the structure of AlGaN/GaN superlattice used as a buffer layer on the crystalline and chemical order of the extremely thin AlN, GaN and AlGaN layers