The study of the evolution of the microstructure and creep properties of Super 304H austenitic stainless steel after aging for up to 50,000 h

Zieliński A., Wersta R., Sroka Marek

Archives of Civil and Mechanical Engineering

|

2022

|

Vol. 22, no. 2

art. no. e89, 1--24

EN

The paper discusses several aspects of degradation of Super 304H steel subjected to long-term aging up to 50,000 h at 650 and 750°C. The study includes microstructure examination by scanning and transmission electron microscopy along with X-ray microanalysis of a wide range of precipitates. The Super 304H steel has a structure characteristic for austenitic steels with annealing twins and single primary NBX precipitates of various sizes. Long-term aging leads to precipitation of several phases such as M23C6, MX carbides, σ phases, Z phase and ε-Cu phase. The precipitation processes lead to changes in the creep strength of the tested steel, the value of which strongly depends on the aging temperature used, which is measurably shown by the creep tests carried out with the elongation measured during the test.

2

Struktura stali S304H po 10 000 godzin starzenia

Zieliński A., Wersta R.

Energetyka

|

2018

|

nr 11

648--650

PL

Stal S304H stosowana jest w budowie elementów ciśnieniowych kotłów o nadkrytycznych parametrach pracy. Zaprezentowano wyniki badań mikrostruktury po starzeniu przez 1000 i 10000 godzin w temperaturze 650 i 700°C. Badania mikrostruktury wykonano wykorzystując skaningową i transmisyjną mikroskopię elektronową. Identyfikację występujących wydzieleń przeprowadzono przy użyciu transmisyjnej mikroskopii elektronowej. Opisano wpływ czasu starzenia na zmiany mikrostruktury i proces wydzieleniowy badanej stali. Zaprezentowane wyniki badań stanowią element charakterystyk materiałowych stali nowej generacji, które wykorzystane są w pracach projektowych urządzeń ciśnieniowych kotłów parowych oraz w pracach diagnostycznych podczas eksploatacji.

EN

S304H steel is used in the construction of pressure elements of boilers with supercritical operation parameters. The paper presents the results of microstructure testing after aging for 1000 and 10 000 hours at 650 and 700°C. Microstructure research was performed using scanning and transmission electron microscopy. Identification of precipitates occurring was carried out using transmission electron microscopy. The influence of aging time on microstructure changes and the precipitation process of the tested steel is described. The presented research results are an element of material characteristics of the new generation of steel, which are used in the design work of pressure devices of steam boilers and in diagnostic work during operation.

3

Charakterystyka różnoimiennego złącza spawanego P91+ 15HM po 240 000 godzinach eksploatacji

Hernas A., Wersta R., Luczys T.

Energetyka

|

2015

|

nr 10

662--664

PL

Przedstawiono warunki i parametry spawania i obróbki cieplnej grubościennego różnoimiennego złącza składającego się z rury w gatunku P91 w stanie dostawy z elementem w gatunku 15HM (13CrMo4-5) po 240 000 godzinach eksploatacji. Jako spoiwo zastosowano eksperymentalnie drut w gatunku WMoVSi / EMoVB42H5 stosowany do spawania stali 13HMF(14MoV6-3). Wykonane złącze poddano kompleksowej ocenie jakości z zastosowaniem metod nieniszczących oraz niszczących. Przedstawiono wyniki badań własności mechanicznych złącza oraz jego charakterystykę strukturalną. Uzyskane wyniki badań spełniają wymagania jakościowe PN-EN ISO 15614-1:2008 i były podstawą kwalifikacji technologii spawania przez UDT.

EN

The paper presents some results of microstructure and hardness analysis of dissimilar welded joint made of P91 steel in initial state with 13CrMo4-5 steel after 240 000 hrs of service. Technological conditions, welding and thermal treatment parameters of welded joint pipes with diameter φ 323.9 mm and thickness 33.3 mm are presented. As a additional welding material used to wire WMoVSi / EMoVB42H5 usually designated to welding of 14MoV6-3 steel. The proper macro and microstructure with the use of the light and scanning microscopy as well as hardness distribution was found. The quality of welded joint complying with requirements of Polish technical supervision (UDT).