Content available The role of β(Al12Mg17) phase on corrosion behavior of the AZ91 alloy in NaCl aqueous solution
Hatakeyama M., Shimono K., Iwashima D., Saikawa S., Sunada S.
Archives of Metallurgy and Materials
|
2017
|
Vol. 62, iss. 1
155--158
EN
The effect of the β phase (Al12Mg17) on the corrosion resistance in a NaCl solution was investigated by electro chemical methods.Volume fraction of β phase in each specimen was controlled systematically by isothermal annealing at 473 K as 0%, 4%, 22% and 100 %, respectively. Although α phase shows lower corrosion current density than that of β phase, the α/β mixed phase specimen showed higher corrosion current density than that of α phase.It strongly suggests that β phase act as cathodic electrode in the alloys.
2
Content available Tem Observation Of Age-Hardening Precipitation In Mg-Gd-Y Alloys As Different Gd/Y Ratio
Matsuoka Y., Watanabe K., Nakamura J., Lefebvre W., Saikawa S., Ikeno S., Matsuda K.
Archives of Metallurgy and Materials
|
2015
|
Vol. 60, iss. 2A
971--972
EN
In this study, the early stage of aging in Mg-Gd-Y alloys has been observed by transmission electron microscopy (TEM), high angle annular dark field – scanning transmission electron microscopy (HAADF-STEM) and calculations of images and electron density and bond overlap population (BOP) by first principal to understand the origin of precipitation in this alloy. The small hexagon of 0.37 nm is the first precipitate in this alloy, and this is the evidence of short range ordering of D019 structure. This is referred as the pre β”-phase. In the peak aged condition, β’ phase with bco structure was mainly observed.
PL
W pracy przedstawiono mikroskopowe obserwacje TEM wczesnego etapu starzenia stopów Mg-Gd-Y. Ponadto badania prowadzono z użyciem skaningowej transmisyjnej mikroskopii elektronowej. Wykorzystano zjawisko niekoherentnego rozpraszania w ciemnym polu i materiał obrazowano przy pomocy detektora pierścieniowego, który zbiera elektrony rozproszone pod dużymi kątami (HAADF-STEM). Przeprowadzono także analizę obrazów, obliczenie gęstości elektronowej i ilości nakładających się wiązań w celu zrozumienia źródła wydzieleń w ww. stopie. Pierwszym wytrąceniem w stopie jest mały sześciokąt o wielkości 0,37 nm, a dowodem tego jest uporządkowanie krótkiego zasięgu struktury D019.
3
Content available Microstructure And Mechanical Properties Of An Al-Zn-Mg-Cu Alloy Produced By Gravity Casting Process
Saikawa S., Aoshima G., Ikeno S., Morita K., Sunayama N., Komai K.
Archives of Metallurgy and Materials
|
2015
|
Vol. 60, iss. 2A
871--874
EN
High-strength aluminum alloy are widely used for structural components in aerospace, transportation and racing car applications. The objective of this study is to enhance the strength of the Al-Zn-Mg-Cu alloy used for gravity casting process. All alloys cast into stepped-form sand mold (Sand-mold Casting; SC) and Y-block shaped metal mold(Permanent mold Casting; PC) C and then two –step aged at 398-423 K after solution treated at 743 K for 36 ks. The tensile strength and total elongation of the two-step aged SC alloys were 353-387 MPa and about 0.4% respectively. This low tensile properties of the SC alloys might be caused by remaining of undissolved crystallized phase such as Al2CuM, MgZn2 and Al-Fe-Cu system compounds. However, good tensile properties were obtained from PC alloys, tensile strength and 0.2% proof stress and elongation were 503-537 MPa, 474-519 MPa and 1.3-3.3%. The reason of the good properties in PM alloys, is the lowed amount of undissolved crystallized phase than that of SC ones and primary crystallized alpha-Al phase was finer due to high cooling rate at solidification in casting.
PL
Stopy glinu o wysokiej wytrzymałości są szeroko stosowane jako elementy konstrukcyjne w lotnictwie, w transporcie oraz w samochodach wyścigowych. Celem badań prezentowanych w niniejszej pracy jest zwiększenie wytrzymałości stopu Al-Zn-Mg-Cu przy zastosowaniu metody odlewania grawitacyjnego. Stopy odlewano w formie piaskowej (ang. Sand-mold Casting; SC) oraz w formie metalowej w kształcie Y (ang. Permanent mold Casting; PC), a następnie poddawano dwustopniowemu starzeniu w zakresie temperatur 398-423 K po przesycaniu w 743 K w czasie 36 ks. Wytrzymałość na rozciąganie stopów SC po dwustopniowym starzeniu wyniosła 353-387 MPa, natomiast całkowite wydłużenie – ok. 0,4%. Niska wytrzymałość stopów SC na rozciąganie może być spowodowana pozostałościami faz krystalicznych, tj. związków Al2CuM, MgZn2 i Al-Fe-Cu. Natomiast stopy PC charakteryzowały się dobrymi właściwościami mechanicznymi. Wytrzymałość na rozciąganie, umowna granica plastyczności R0.2, plastyczność oraz wydłużenie wyniosły odpowiednio 503-537MPa, 474-519MPa oraz 1,3-3,3%. Lepsze właściwości mechaniczne stopów PC można wytłumaczyć mniejszą ilością nierozpuszczonych faz krystalicznych w porównaniu ze stopami SC oraz mniejszą grubością głównej fazy krystalicznej alfa-Al wynikającej z wysokiej szybkości chłodzenia do punktu krzepnięcia przy odlewaniu.
4
Content available Effect of Mn contents on age-hardening and microstructure in AM60 magnesium alloys
Tsuchiya T., Kawabata T., Saikawa S, Isizuki H, Takeda S., Ikeno S., Matsuda K.
Archives of Metallurgy and Materials
|
2013
|
Vol. 58, iss. 2
327--328
EN
The thixotropy phenomenon is strongly connected with the change of viscosity in time, while the of Navier-Stockes equation. The micro- and macroscale models are coupled using CAFE approach.
PL
Zjawisko tiksotropii polega na zmianie lepkości cieczy przy ustalonej prędkości ścinania i temperaturze. W komputerowym modelowaniu zachowania się materiału wykazującego skończonych.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.