Influence of geometry and annealing temperature in argon atmosphere of TiO2 nanotubes on their electrochemical properties

Nycz Marta, Paradowska Ewa, Arkusz Katarzyna, Pijanowska Dorota Genowefa

Acta of Bioengineering and Biomechanics

|

2020

|

Vol. 22, no. 1

165--177

EN

In this paper, electrochemical properties of the as-formed and thermally treated titanium dioxide (TiO2) nanotubes with diameter in the range of 20–100 nm and height in the range of 100–1000 nm were presented. In addition, the effects of annealing temperature (450–550 °C) on the electrochemical characteristics of these structures, as well as the influence of diameter and height of TiO2 nanotubes on these properties were examined. The results were referred to a compact TiO2 layer (100 nm thick). Methods: The electrochemical test included open circuit potential, impedance spectroscopy and cyclic voltammetry measurements. The scanning electron microscope with energy dispersive spectroscopy analyser, x-ray photoelectron spectroscopy, and x-ray diffraction analysers were used for surface morphology characterisation as well as elemental, phase and chemical composition of TiO2 layers. Results: It was found that nanotubes with the diameter of 50 and 75 nm (height of 1000 nm) annealed at 550 °C exhibit the lowest impedance and phase angle values. However, the voltammetric detection of potassium ferricyanide indicated that the closest to 1 Ipc /Ipa ratio were shown by nanotubes with a diameter of 50 and 75 nm annealed at 450 °C. Conclusions: On the basis of performed analysis, it can be stated that the TiO2 layer with nanotubes of 50 nm in diameter and of 1000 nm in height, annealed in 450 °C may be indicated as the ones having the most favourable sensing and biosensing properties.

2

Badanie wpływu modyfikacji termicznej na zachowanie elementów rozciąganych w podwyższonych temperaturach

Ogrodnik P., Tatka B.

Zeszyty Naukowe SGSP / Szkoła Główna Służby Pożarniczej

|

2014

|

Nr 50 (2)

43--51

PL

W artykule przedstawiono wyniki badań wpływu rodzaju modyfikacji termicznej na wytrzymałość drewna przy rozciąganiu podczas oddziaływania termicznego. W badaniach wykorzystano próbki o kształtach i wymiarach zgodnych z obowiązującą normą. Modyfikacja termiczna próbek drewnianych została przeprowadzona w dwóch różnych procesach do temperatury maksymalnej wynoszącej odpowiednio 165°C oraz 210°C. Badania wytrzymałościowe zostały wykonane na uniwersalnej maszynie typu FPZ 100/1 z jednoczesnym ogrzewaniem próbek do 200°C. Wyniki badań przedstawione w formie tabelarycznej wykazały istotny wpływ modyfikacji termicznej na wytrzymałość drewna zarówno w temperaturze normalnej po ochłodzeniu próbek do temperatury otoczenia, jak i w podwyższonej. Wykazano również różnice, które występują podczas badań wytrzymałościowych w zakresie zniszczenia próbek. W przypadku badań prowadzonych w 200°C zniszczenie próbek jest równomierne i następuje w środku ich długości, natomiast w temperaturze normalnej 20°C rozciągane drewno rozrywało się w sposób nierównomierny.

EN

The article presents the results of tests on the influence of the thermal modification on wood strength while being spread during thermal interaction. The shape and size of the samples used in the tests are compatible with the standard in force. The wood thermal modification has been done in two different processes up to max temperatures of 165°C and of 210°C. The strength tests have been made in the universal machine of the FPZ 100/1 type with the simultaneous heating the samples up to 200°C. The tests results ,presented in a tabular way, have shown the considerable influence of the thermal modification on wood strength, both in normal temperature after cooling the samples to surrounding temperature and in higher. Some differences which occur during the strength tests and during the failure of the test samples have been presented. During the tests conducted in the temp of 200°C ,the failure of the test samples is at a uniform rate and occurs inside their length while in the normal temperature of 20°C the spreading wood was tearing itself in a non-uniform way.

3

The effect of thermal modification of ash wood on granularity and homogeneity of sawdust in the sawing process on a sash gang saw prw 15-M in view of its technological usefulness

Dzurenda L., Orlowski K. A.

Drewno : prace naukowe, doniesienia, komunikaty

|

2011

|

vol. 54, nr 186

27-37

EN

This paper presents the results of granulometric analyses of sawdust of unmodified and thermally- modified ash wood (Fraxinus exelsior L.) sawed on a narrow-kerf sash gang saw. The sawdust of dry thermally-modified ash produced in the sawing process on a frame sawing machine PRW15-M at a feed speed in the range of 0.36-1.67 mźmin-1 has chip granularity ranging from 33.5 micro m to 9.9 mm; whereas unmodified ash wood sawdust consists of chips in a granularity range from 35.6 micro m to 13.8 mm. It was observed that thermally-modified ash sawdust is finer, with a distinctly larger share of the fraction in the granularity range a = 125-500 micro m and a slightly increased share of the fraction in the range a = 32-125 ěm. Changes in mechanical characteristics of modified wood were also observed in the technological usefulness of a part of dry sawdust chip in the granularity range a = 250 micro m-2.4 mm. While the homogenous share of chips in sawdust produced in the process of sawing of dry ash wood was HSCha = 81-84 %, the demonstrated homogenous share of chips in ash sawdust formed in the process of sawing of dry thermally-modified wood was lower by 4-6 %.

PL

Przedstawiono wyniki analiz granulometrycznych trocin, drewna jesionowego niemodyfikowanego (Fraxinus exelsior L.) i modyfikowanego termicznie, otrzymanych w procesie przecinania drewna na pilarce ramowej wielopiłowej PRW15-M. Przecinanie drewna prowadzono dla dwu prędkości posuwu 0,36 mźmin-1 oraz 1,67 mźmin-1. Ziarnistość powstających trocin dla drewna jesionowego modyfikowanego termicznie zawierała się w przedziale od 33,5 micro m do 9,9 mm, podczas gdy dla drewna niemodyfikowanego ziarnistość trocin mieściła się w przedziale od 35,6 micro m do 13,8 mm. Stwierdzono, iż trociny otrzymywane z drewna modyfikowanego termicznie są bardziej miałkie, z większym udziałem frakcji o ziarnistości w przedziale a = 125 – 500 micro m, z nieznacznie większym udziałem frakcji z zakresu a = 32 – 125 micro m. Zaobserwowano również, że przydatność technologiczna trocin mieszczących się w zakresie ziarnistości a = 250 micro m – 2.4 mm dla drewna jesionowego niemodyfikowanego termicznie zawiera się w przedziale 81 – 84 %, zaś dla drewna jesionowego modyfikowanego termicznie jest mniejsza o około 4 – 6%.

4

Influence of initial heat treatment on the fatigue life of austenitic Fe-Ni alloy

Ducki K., Cieśla M.

Archives of Materials Science and Engineering

|

2008

|

Vol. 29, nr 2

89-92

EN

Purpose: The paper addresses the problem of determining the dependence between initial heat treatment of an austenitic Fe–Ni alloy and its mechanical properties and fatigue life at room temperature. Design/methodology/approach: For the investigated Fe–Ni alloy after solution heat treatment, two variants of specimen ageing were applied for comparison, i.e. typical single-stage ageing and novel two-stage ageing. Specimens that underwent heat treatment were subjected to a static tensile test and low-cycle fatigue tests (LCF), carried out at room temperature. Findings: It has been found that, the specimens of Fe–Ni alloy after two-stage ageing are distinguished by higher strength properties with a little lower plastic properties. In a case of low-cycle fatigue tests, specimens after singlestage ageing were characterized by higher fatigue life. Lower fatigue life of the alloy after two-stage ageing can be explained by increased brittleness of material in boundary areas. Practical implications: The fatigue life results obtained in LCF conditions can be used in predicting the duration of operation of products made out of Fe–Ni alloy at room temperature. Originality/value: The significance of the applied ageing variants’ effect on the mechanical properties and fatigue life of the tested austenitic Fe–Ni alloy is shown in the paper.

5

Analiza wybranych czynników wpływających na rozwój nowych produktów spożywczych

Wierzbicka A.

Inżynieria Rolnicza

|

2006

|

R. 10, nr 7(82)

449-455

PL

W pracy prezentowane są wyniki analizy wybranych czynników (surowcowych i aparaturowych), wpływających na rozwój nowych nadziewanych produktów spożywczych. Stabilizacja struktury nadzień owocowych przeprowadzona została w oparciu o pektyny wysoko i niskometylowane termicznie modyfikowane. Ocenę właściwości fizycznych przeprowadzono w oparciu o badanie właściwości reologicznych masy zewnętrznej i zagęszczenia półproduktów owocowych. Teksturę gotowych wyrobów oceniano w oparciu o instrumentalny test penetracji i test oceny sensorycznej.

EN

The study presents the results of an analysis of chosen factors (materials and machines) which influence development on new foods with filling. Stabilisation of the structure of fruit fillings was done on the basis low and high methyl content pectins, thermally modified. Physical properties were assessed on the basis of an analysis of rheological properties of external mass and compaction of fruit semiproducts. The texture of finished products was assessed on the basis of instrumental penetration test and a sensory assessment test.

6

Wpływ wysokotemperaturowej modyfikacji węgla aktywnego na sorpcję anionów Cr(VI) i kationów Cr(III) z roztworów wodnych

Lach J., Ociepa E.

Ochrona Środowiska

|

2003

|

R. 25, nr 3

57-60

PL

Omówiono wyniki badań dotyczących wysokotemperaturowej modyfikacji krajowego węgla aktywnego WG-12. Odpopielony kwasem solnym węgiel modyfikowano w temperaturach 700¸900 oC przez 1¸3 godz. z niewielkim dopływem powietrza. Rezultaty modyfikacji oceniono na podstawie efektywności sorpcji chromu(VI) i (III). Dla wszystkich badanych temperatur i czasów utleniania lepsze rezultatu sorpcji chromu otrzymano dla węgli zmodyfikowanych. Oprócz zmian w chemicznym charakterze powierzchni węgla nastąpiła także zmiana w strukturze porowatej węgla aktywnego, czego wynikiem było zmniejszenie gęstości nasypowej węgla. Prawdopodobnie nastąpiło zwiększenie nie tylko objętości porów, ale także ich powierzchni, o czym świadczył wzrost wartości liczby metylenowej. Wykazano, że modyfikując węgiel aktywny WG-12 w temperaturze 900 oC można uzyskać preparat węglowy o większych pojemnościach, zarówno w stosunku do anionów Cr(VI) jak i kationów Cr(III).

EN

Samples of home-made activated carbon of WG 12 type (after ash removal with hydrochloric acid) were modified in a rotary furnace at 700, 800 and 900 oC for 1, 2 and 3 hours in the presence of air (the system was insufficiently hermetic). The results were assessed using sorption isotherms of chromium(VI) and chromium(III) and described in therms of Freundlich and Langmuir equations. Sorption of chromium(VI) was investigated at pH=7. For all the investigated temperatures and oxidation times, higher sorption capacity values were obtained with modified than non-modified carbon. Besides the change in the chemistry of the carbon surface, changes were also observed in the porous structure, which accounted for the decrease in the bulk density of the activated carbon. There might have been an increase not only in pore volume but also in pore surface, as it can be inferred from the methylene number. The investigations have shown that the modification of the WG 12 activated carbon at 900 oC enhances its sorption capacity with respect to both Cr(VI) anions and Cr(III) cations.

7

Otrzymywanie i termiczna modyfikacja warstw kompozytowych Ni+Al

Napłoszek-Bilnik I., Budniok A.

Kompozyty

|

2002

|

R. 2, nr 3

52-57

PL

Badano wpływ zawartości proszku glinu w kąpieli galwanicznej na skład chemiczny warstw kompozytowych Ni+Al, otrzymywanych elektrolitycznie w warunkach galwanostatycznych (1170 C x cm-2) na podłożu stalowym. Kąpiel galwaniczna zawierała proszek glinu w ilości: 20, 40, 60, 80, 100 g/dm3. Stwierdzono, że wraz ze wzrostem zawartości Al w kąpieli jego zawartość w warstwie osiąga 16%, po czym maleje do około 11%. Dla optymalnego składu kąpieli galwanicznej zapewniającego otrzymanie warstw o zawartości 16% Al określono wpływ wartości gęstości prądowej na ilość wbudowywanego Al do warstwy. Następnie warstwy te były wygrzewane w piecu elektrycznym, do którego doprowadzany był argon. Badania składu fazowego przeprowadzono za pomocą rentgenowskiej analizy fazowej, a analizę składu chemicznego metodą atomowej absorpcji. Przeprowadzone badania wykazały możliwość otrzymywania warstw kompozytowych na osnowie Ni z zabudowanymi ziarnami Al. Warstwy poddane modyfikacji termicznej w temperaturze 873 K, obok obecności krystalitów niklu i glinu, wykazują obecność związków międzymetalicznych Ni2Al3 i Ni3Al4.

EN

Electrolytic nickel layers are typified by good corrosion resistance and electrochemical activity in the processes of cathodic hydrogen evolution and anodic oxygen evolution. In order to improve of utilizable properties of the nickel layers, the coatings were co-deposited from baths containing metal oxides (Al2O3, Al3O4, NiO). Incorporating into a metallic matrix of composite component as metallic powder and its embedding into the matrix structure follows to obtain a new kind of composite material. Therefore, the present study was undertaken in order to obtain the electrolytic composite layers containing embedded aluminum grains into a nickel matrix. The structure and properties of Ni+AI alloys were determined using different methods. Composite Ni+AI layers were prepared by simultaneous electrodeposition of nickel and aluminum on a steel substrate in which 20, 40, 60, 80, 100 g/dm3 of Al powder were suspended. The electrodeposition was carried out under galvanostatic conditions at a temperature of 293 K and the current density of jD = 300 mA/cm2 for 1 h. The phase composition of the layers was investigated by the X-ray diffraction method. The surface morphology of the coatings was examined by means of a stereoscopic microscope Nicon. The obtained Ni+AI layers are of mat, rough metallic surface. There are a visible Al grains on the layer surface (Fig. 1). X-ray analysis of Ni+AI layers revealed their two phase composition (Fig. 2a). It was found that the phase structure of obtained layers depends on phosphorous content in the layer only. Atomic absorption spectroscope was used for chemical characterization of the layers. The influence of aluminum powder content in an electroplating bath on the chemical composition of Ni+AI layers was examined. Chemical analysis of the Ni+AI layers confirms the co-deposition of Ni and Al. It was ascertained that the increase aluminum powder amount in the bath causes the rise in Al content embedded into the composite layers. In the layers of Ni+Al-a linear increase of Al content in the layer from 15% to about 20% was observed (Tab. 1). It was assumed that mechanism of Al embedding into the layer based on the adsorption phenomena and migration of the charged suspension-micelles towards the cathode. The chemical composition of the layers depends also on current density deposition (Tab. 2). It was showed that from the bath containing 40 g Al/dm3 at the current density equal 320 mA/cm2 composite layer containing about 16% Al was obtained. In this case the average mass increment has also maximal value. The result of that process is possibility to obtain considerable thickness and good adhesivity of those composite layers. The thickness of composite layers increase linearly with the increasing of Al content in the bath. It is equal 120 and 150 micrometers for Ni+AI. The heat treatment of the layer at 873 K was done. It was ascertained that after the thermal treatment the obtained layers are of mat, rough metallic surface (Fig. 3). Depending on time of heat treatment the different surface morphology are obtained. This indicates on chemical reaction in solid state of the layer. Markedly different X-ray spectra were obtained for the electrocoatings heated in the argon atmosphere. The main peaks corresponding to the Ni and Al coexist with the new ones corresponding to new phases: Ni2jAl3, Ni3Al4 (Fig. 2b). Such phases can take part in hydrogen electroevolution.

8

Wpływ modyfikacji termicznej i chemicznej na właściwości paku węglowego

Kaczmarska H., Więcek I.

Karbo

|

1999

|

Nr 11

375-379

PL

Pak węglowy z surowej smoły koksowniczej oraz otrzymane z niego drogą modyfikacji termicznej i chemicznej paki rozdzielono metodą ekstrografii na frakcje o różnym charakterze chemicznym. Zbadano tek-sturę optyczną półkoksów oraz właściwości produktów grafityzacji pół-koksów kalcynowanych, otrzymanych z tych paków. Zasadniczą przemianą stwierdzoną w procesie modyfikacji termicznej był wzrost ilości wysokocząsteczkowych , mezogennych składników. Modyfikacja che-miczna powodowała obniżenie aromatyczności i zawartości składników mezogennych. Wykazano większą podatność na grafityzację paku mo-dyfikowanego termicznie w porównaniu z pakiem otrzymanym w procesie modyfikacji chemicznej.

EN

Coal - tar pitch from the raw coking tar and pitch obtained from it on the way of thermal and chemical modification pitches were separated by extrography method into fractions of different chemical character. Optic texture of semi-cokes has been investigated and the properties of the products of calcinated semi-cokes graphitisation obtained from tho-se pitches. The basic transformation determined in the process of ther-mal modification consisted in the increase of high element mesogenic components. Chemical modification resulted in decrease of aromatic properties and the content of mesogenic components. Greater suscepti-bility to graphitisation of the thermally modified pitch as against the pitch obtained in the process of chemical modification.