Wyniki wyszukiwania - BazTech

1

The Effect of Extrusion in the Complex Strain State on the Microstructure and Mechanical Properties of MgAlZn Magnesium Alloys

Bednarczyk I., Kuc D., Tomaszewska A., Tkocz M.

Archives of Metallurgy and Materials

|

2020

|

Vol. 65, iss. 3

1121--1128

EN

The paper presents the results of tests concerning the effect of the extrusion process in the complex strain state on the microstructure and properties of one of magnesium alloy with aluminium, zinc and manganese, designated AZ61. Due to its specific gravity, it is increasingly being used in the automotive and aerospace industries to reduce the weight of structural elements. As a result of plastic deformation processes, rods with a diameter of 8, 6 and 4 mm were obtained from AZ61 magnesium alloy. The microstructure analysis was performed using light and electron microscopy (STEM) techniques in the initial state and afterplastic deformation. Microstructure studies were supplemented with a quantitative analysis using the Metilo program. A number of stereological parameters were determined: average diameter of grain, shape factor. A static tensile test was carried out at 250ºC and 300ºC, at deformation rates of 0.01, 0.001 and 0.0001 m·s-1. Better plastic properties after deformation using KoBo methodwere obtained than with conventional extrusion.

2

The evaluation of platinum group metals (PGMs) and their recovery from car catalytic converters

Trębacz H., Michno P.

Structure and Environment

|

2017

|

Vol. 9, no. 2

133--147

EN

Car catalysts significantly reduce air pollution - by reducing NOx and oxidizing CO and HC. Every car put on the market must be equipped with a catalytic reactor in which the noble metals platinum, palladium and rhodium have a catalytic function. With the rapid development of the automotive industry and stringent emission regulations, the demand for platinum group metals is steadily increasing. PGM is used in many industries. The resources of these metals are constantly shrinking with increasing demand. Operation of catalysts causes the emission of PGMs to the environment. The recovery of platinum group metals from car catalysts has increased over the past decade, but is still insufficient. Processing 2 tons of used catalysts avoids the extraction of 150 tons of ore. At present, the world’s used catalysts are processed by hydrometallurgical or pyrometallurgical way. Both methods allow for recovery of about 95% of platinum and palladium and 70% of rhodium. PGMs recovered from car catalysts is becoming an important source of these metals. There are ideas for platinum group metals mining in the solar system. It is significant that gases from catalytic reactors cause emissions to the environment of harmful platinum, which accumulates in street sediments, soil, plants, water and in animals. The results of studies on monoliths derived from catalysts were carried out using a XRF Niton fluorescence spectrometer and electron microscope. In addition, the life cycle analysis of the catalytic reactor has been carried out from the moment of platinum extraction to operation and recycling.

PL

Katalizatory samochodowe pozwalają w znacznym stopniu ograniczyć zanieczyszczenie powietrza poprzez redukcję NOx oraz utlenienie CO i HC. Każdy samochód wprowadzany na rynek musi być wyposażony w reaktor katalityczny, w którym metale szlachetne: platyna, pallad i rod pełnią funkcje katalityczne. Wraz z gwałtownym rozwojem motoryzacji i surowymi regulacjami dotyczącymi emisji spalin, stale wzrasta zapotrzebowanie na platynowce. PGM są wykorzystywane w wielu gałęziach przemysłu. Zasoby tych metali stale się kurczą przy zwiększającym się popycie. Eksploatacja katalizatorów powoduje emisję platynowców do środowiska. Odzysk platynowców z katalizatorów samochodowych w ciągu ostatnich dziesięciu lat wzrósł, ale wciąż jest niewystarczający. Przerób 2 Mg wyeksploatowanych katalizatorów pozwala uniknąć wydobycia 150 Mg rudy. Aktualnie na świecie zużyte katalizatory przerabia się na drodze hydrometalurgicznej lub pirometalurgicznej. Obie metody pozwalają na odzyskanie ok. 95% platyny i palladu oraz 70% rodu. Platynowce odzyskiwane z katalizatorów samochodowych stają się więc istotnym źródłem tych metali. Pojawiają się pomysły wydobycia platynowców w Układzie Słonecznym. Należy pamiętać, że gazy z reaktorów katalitycznych powodują emisję do środowiska szkodliwej platyny, która kumuluje się w osadach ulicznych, glebie, roślinach, wodzie oraz w zwierzętach. W publikacji przedstawiono wyniki badań monolitów pochodzących z katalizatorów przeprowadzone spektrometrem fluorescencyjnym XRF Niton oraz mikroskopem elektronowym. Ponadto przeprowadzono analizę cyklu życia reaktora katalitycznego od momentu wydobycia platynowców po eksploatację i recykling.

3

Powstawanie struwitu podczas nanofiltracji odcieków z fermentacji metanowej

Domańska M., Dragański P., Wiercik P., Łomotowski J., Konieczny T.

Czasopismo Inżynierii Lądowej, Środowiska i Architektury / Journal of Civil Engineering, Environment and Architecture

|

2016

|

z. 63, nr 2/II

77--86

PL

Jednym z problemów występujących na oczyszczalniach ścieków jest wytrącanie się struwitu. Kontrola procesu wytrącania się struwitu stwarza możliwości ochrony instalacji technologicznych przed jego negatywnymi skutkami, a powstały struwit może być wykorzystany jako nawóz mineralny. W pracy omówiono przyczyny tworzenia się struwitu w przewodach do transportu odcieków z odwadniania ustabilizowanych beztlenowo osadów ściekowych. W pracy podjęto próbę sprawdzenia, czy w warunkach zmiennego składu odcieków z fermentacji metanowej o obniżonej zawartości amoniaku jest możliwe odzyskiwanie fosforu w postaci struwitu. Badania prowadzono z wykorzystaniem membrany nanofiltracyjnej. Nadawę stanowiły odcieki pochodzące z odwadniania ustabilizowanych na drodze mezofilnej fermentacji metanowej osadów ściekowych, w których jony amonowe usuwano na drodze nitryfikacji w reaktorach SBR. Odcieki przed skierowaniem na membranę nanofiltracyjną były poddane wstępnemu oczyszczaniu z zawiesin w procesie mikrofiltracji. Przeprowadzono dwa eksperymenty z różnym składem nadawy. W obu eksperymentach podczas zatężania odcieków na membranie nanofiltracyjnej odczyn retentatu wzrastał przy równoczesnym obniżaniu się stężenia jonów.

EN

Struvite is one of the main problem appearing at sewage installations of sludge processing. The ability to control the process of struvite precipitation provides opportunities for protection of technological installations against its negative effects. The product obtained in a form of struvite can be used as a fertilizer. In this paper, conditions of struvite formation in pipes to transport the leachate from dewatering of anaerobically stabilized sludge were discussed. The aim of this paper was to verify whether it is possible to recover phosphorus in the form of struvite in the conditions of variable composition of leachate from methane fermentation with reduced ammonium content. Studies were carried out using nanofiltration membranes. The feed constituted leachate stabilized with mesophilic dehydration by anaerobic digestion of sewage sludge, in which the ammonium were reduced by nitrification in SBR reactor. Two experiments with different composition of leachate were conducted. The leachate before nanofiltration was pretreated of suspensions in the microfiltration process. In both experiments, the reaction of retentate recirculated on nanofiltration membrane was increasing while magnesium was decreasing. During the whole experiment low ammonium concentration was being observed. The images of the scanning electron microscope revealed that the crystals were light brown and had an orthorhombic structure. Pilot studies have shown that there is the possibility of precipitation of struvite with leachate from the dewatering of anaerobically stabilized sludge on nanofiltration membranes. It can be relatively simple to remove mechanically the precipitate cake from the membrane provided that the flat sheet membrane systems are applied.

4

Characteristic features of fine-grained coatings deposited on magnesium alloys

Tański T., Dobrzański L. A., Rusz S., Matysiak W., Kraus M.

Archives of Materials Science and Engineering

|

2014

|

Vol. 66, nr 1

13--20

EN

Purpose: This work presents the research results on the structure of gradient/monolithic coatings (Ti/Ti(C,N)/CrN, Cr/CrN/TiN) deposited onto the magnesium alloy substrate by cathodic arc evaporation method. Design/methodology/approach: The investigations were performed using scanning and transmission electron microscopy (with different image techniques) for the microstructure determination. The morphology was studied as well as the lattice parameters for the layer matrix and substrate phase identification using diffraction methods. Findings: A thin metallic layer (Ti and Cr) was deposited prior to deposition of gradient coatings to improve adhesion. It was found out that the microstructure of the PVD coatings deposited by the cathodic arc evaporation method is composed of fine crystallites and that their average size is in the range of 15-200 nm, depending on the coating type. SEM micrographs showed that the deposited coatings are characterized by compact structure without delamination or defects and they closely adhere to each other. Investigations confirm also that the Ti(C,N)/CrN and CrN/TiN coatings reveal a clearly visible transition zone between the gradient Ti(C,N) and CrN layers and the wear resistant CrN and TiN layers, obtained as a result of the separately applied metal vapour sources. Practical implications: Achieved coatings with good adhesion and without the disadvantage of delamination was made possible by cathodic arc evaporation method. Obtained properties of gradient/monolithic coatings (Ti/Ti(C,N)/CrN, Cr/CrN/TiN) deposited onto the magnesium alloy substrate and the study of them can contribute to development in a given group of materials used for different surface engineering processes. Originality/value: The original value of the work is that it applied the PVD method for a common material like magnesium alloy.

5

Opracowanie metodyki badań struktury stali wielofazowej z wykorzystaniem elektronowego mikroskopu skaningowego wyposażonego w detektor EBSD

Radwański K., Kuziak R., Molenda R., Krztoń H., Wojtas J.

Prace Instytutu Metalurgii Żelaza

|

2011

|

T. 63, nr 2

79-82

PL

Celem pracy było opracowanie metodyki preparatyki próbek oraz badań stali wielofazowych stosowanych w przemyśle samochodowym z wykorzystaniem metod mikroskopii świetlnej oraz wysokorozdzielczej mikroskopii skaningowej z uwzględnieniem metody EBSD. W ramach pracy przeprowadzono badania aplikacyjne opracowanej metodyki badań stali wielofazowych typu TRIP, DP i CP. Opracowana metodyka badań pozwala na kompleksową charakterystykę struktury stali wielofazowych uwzględniającą jakościową i ilościową charakterystykę składników struktury. W pracy wykazano przydatność parametrów IQ, CI i KAM wyznaczanych w metodzie EBSD w badaniach stali wielofazowych.

EN

The purpose of the work was to develop the methodology for sample preparation and investigations of multi-phase steels used in the automotive industry using light microscopy and high-resolution scanning microscopy methods, including the EBSD method. As a part of the work the application tests of the developed methodology for investigations of multi-phase TRIP, DP and CP steels were carried out. The developed investigation methodology allows the comprehensive structural characteristics of multi-phase steels taking into consideration the qualitative and quantitative characteristics of the structural components. In the work, the suitability of IQ, CI and KAM parameters determined in the EBSD method during multi-phase steel investigations was shown.

6

Możliwości dopasowujących się algorytmów w analizie parametrów obrazów medycznych

Gilewska G.

Przegląd Elektrotechniczny

|

2010

|

R. 86, nr 10

190-192

PL

W artykule zostaną przedstawione stosowane metody obrazowania obiektów medycznych z szczególnym wykorzystaniem struktur szkliwa nazębnego. Badane obrazy były analizowane filtrami kontekstowymi, gradientowymi oraz przekształceniami morfologicznymi. Pierwszym ograniczeniem podczas przetwarzania obrazów szkliwa był problem jednoznacznego wyodrębnienia występujących na obrazach pryzmatów zaś kolejnym pomiar ich parametrów geometrycznych bez nadmiarowych składowych. W celu zmniejszenia tych ograniczeń zastosowano wybrane przekształcenia morfologiczne.

EN

The methods of medical objects imaging will be presented in this article using the enamel structure. Examined images were analysed by context, gradients filters and morphological transformations. Main limitations were unequivocal separation structures of image and measurement their geometric parameters without redundancy components. To decrease this limits were used selected morphological operations.

7

Analiz rynkowa i przeprowadzenie badań weryfikacyjnych współczesnych mikroskopów elektronowych prześwietleniowych

Maciosowski A., Arabasz S., Wiedermann J.

Prace Instytutu Metalurgii Żelaza

|

2009

|

T. 61, nr 4

44-46

PL

Celem pracy było rozpoznanie propozycji rynkowych w dziedzinie mikroskopów elektronowych prześwietleniowych oraz rozwiązań technicznych i analitycznych stosowanych w nowoczesnej elektronowej mikroskopii prześwietleniowej, a także zweryfikowanie możliwości badawczych na próbach własnych. Wskazano model mikroskopu wraz z wyposażeniem i oprzyrządowaniem do preparatyki próbek najlepiej spełniający potrzeby badawcze w metalurgii. Praca związana była z przewidywanym zakupem nowoczesnego elektronowego mikroskopu prześwietleniowego przez Instytut Metalurgii Żelaza.

EN

The purpose of this paper was to recognise the market proposals in the field of transmission electron microscopes and technical and analytical solutions used in modern transmission electron microscopy as well as to verify the research capabilities by own tests. The model of microscope with equipment and instrumentation for preparation of samples that best satisfy the research needs in metallurgy was selected. This paper was related to the expected purchase of modern transmission electron microscope by the Institute for Ferrous Metallurgy.

8

Badania strukturalne żeliwa ADI w transmisyjnym mikroskopie elektronowym

Kaczorowski M., Myszka D.

Archiwum Odlewnictwa

|

2003

|

R. 3, nr 9

266--273

PL

W pracy przedstawiono wyniki badań strukturalnych żeliwa ADI (ang. Austempered Ductile Iron) z wykorzystaniem transmisyjnej mikroskopii elektronowej – TEM (ang. Transmission Electron Microscopy). Celem badań była obserwacja struktury w nanoskali, w szczególności otrzymanie podstawowej informacji czy rzeczywiście osnowa żeliwa ADI składa się z mieszaniny ferrytu austenitu i ewentualnie pewnej ilości martenzytu, czy też zawiera również ultradyspersyjne węgliki, których ujawnienie metodami klasycznej metalografii jest niemożliwe. W rezultacie szczegółowych obserwacji przeprowadzonych z wykorzystaniem techniki cienkich folii ustalono, że w osnowie znajdują się drobne wydzielenia koherentne z osnową, które mogą dawać istotny wkład w umocnienie.

EN

The results of TEM investigation of ADI were presented. The aim of these investigations was to study the structure of ADI matrix, especially looking for the carbides which we suspected should appear in metallic matrix, and were not discovered yet using conventional metallography observations. On the basis of very careful observations it was concluded that except ferrite, austenite and some martensite grains, very small coherent spherical precipitates were found the size of which was approximately 5nm.

9

TEM observations of faulted dipoles in deformed copper and copper alloys.

Niewczas M., Basinski Z.S., Basinski S.J., Embury J.D.

Inżynieria Materiałowa

|

1998

|

R. XIX, nr 4

1244-1247

EN

The general properties of the deformation substructure are by now well-documented in the literature, but some of the more detailed properties still remain to be studied. In the present work we examine more closely the structures known as Frank dipoles or faulted dipoles, which are recognized in electron micrographs as faint lines terminating within the crystal and running in two <110> directions in the primary glide plane but not in the primary glide direction. The presence of faulted dipoles in formed materials was reported in some of the early transmission electron microscope (TEM) investigations of the 1960s and 1970s e.g., Cu single crystals [1,2], Ni-Co single crystals [3], Ag [4], Cu-2%Al single crystals [5], and in Ge [6]. In these studies, faulted dipoles were detected only in lightly deformed material in regions of the crystal relatively free of other dislocations. The present work takes advantage of the improved resolution available with today's electron microscopic techniques to examine the occurence of faulted dipoles in copper and copper alloy single crystals deformed to various stages in tension.