1
Content available Evaluation of a capacity increase in AG milling of copper slag
Can N. Metin, Mercan Orberk
Physicochemical Problems of Mineral Processing
|
2023
|
Vol. 59, iss. 6
art. no. 175181
EN
The verification of the desired capacity increase in the grinding circuits is performed by simulation studies as they suggest accurate and fast alternatives compared to expensive and labor-intensive methods, particularly for the evaluation of situations that require investment. In this study, simulation was used to evaluate the alternatives that can be made to increase the capacity from 38.86 tph to 90 tph in a grinding circuit where copper slag is autogenously milled. The slag sample was characterized by drop weight and abrasion tests to describe the breakage in autogenous (AG) milling. The performances of the existing circuit and equipment were determined by a comprehensive sampling study, and modeling studies were carried out to form the basis of the simulations. Simulation scenarios were evaluated as investment free and investment requiring alternatives. In the investment free option changing fresh feed size distribution was examined however, capacity could be increased up to only 42 tph. In investment option, increasing the mill motor capacities was simulated and 90 tph target throughput was provided. This result was validated in the plant by replacement of mill motors of AG and pebble mill for 1000 kW and 750 kW, respectively.
2
Content available remote Stan wiedzy dotyczącej wykorzystania żużla miedziowego w kompozytach cementowych
Nieświec Martyna
Materiały Budowlane
|
2023
|
nr 5
26--29
PL
Artykuł dotyczy wykorzystania żużla pomiedziowego w kompozytach cementowych, który jest produktem ubocznym wytopu miedzi. Pomimo rosnącego zainteresowania tym tematem, nadal brakuje odpowiednich badań właściwości świeżej zaprawy i mieszanek z wykorzystaniem kruszyw pomiedziowych, głównie zawartości powietrza i gęstości. Wśród badań stwardniałego betonu i zapraw brakuje rzetelnych informacji o wpływie kruszywa pomiedziowego na nasiąkliwość, mrozoodporność, skurcz oraz mikrostrukturę. Dodatkowo większość prac bazuje na zastąpieniu cementu lub kruszywa drobnego, pomijając zastąpienie kruszywa grubego. W artykule podkreślono ograniczenia i możliwości oraz określono luki badawcze. Skupienie się na nich może mieć kluczowe znaczenie w przypadku dalszych badań w Polsce, która jest w czołówce państw o największych zasobach miedzi.
EN
The article is about the use of copper slag, which is a by-product of copper smelting, in cement composites. Despite the fact that the interest in this direction of research is growing, there is still a lack of adequate research on the properties of the fresh mortar and concrete mixes with the use of copper slag aggregates, mainly on the air content and density. Among the tests of hardened concrete and mortars, there is no reliable information about the influence of copper aggregate on their water absorption, frost resistance, shrinkage and microstructure. In addition, most of the works focus on the replacement of cement or fine aggregate, omitting the replacement of coarse aggregate. This paper highlighted limitations and opportunities and identified some research gaps. Focusing on them might be of key importance for further research activity in Poland, as it is among the countries with the largest copper resources.
3
Content available The Use of Coffee Waste in the Reduction of Metallurgical Slags
Matula Tomasz, Kortyka Łukasz, Myćka Łukasz, Łabaj Jerzy, Wojtal Tomasz
Archives of Foundry Engineering
|
2023
|
Vol. 23, iss. 1
103--109
EN
Coffee is grown in over 50 countries around the world, and its sale is the largest in the world trade after crude oil. In the case of coffee beans, after consumption remains a solid waste in the form of a waste plant extract. At present, coffee waste is not fully managed, which means that it is often deposited in landfills. Taking into account their availability on the market and the content of significant amounts of carbon in them, it was proposed to use them as a reducing agent in the processing of copper slags. The use of Solid Coffee Grounds (SCG) as an alternative reducing agent for coke and coke breeze can be beneficial in two aspects. The first is the reduction of carbon dioxide emissions in the process, and the second is due to the possible release of hydrocarbons from these wastes at high temperatures, which, apart from participating in the reduction process itself, causes also mixing of the bath in the melting unit, which facilitates the process of copper sedimentation in the slag. The experiments carried out on a laboratory scale showed the possibility of reducing the copper content in the slag after the reduction process from 10.3 to 0.41 % by mass. The obtained values of the relative degree of copper splashing for all experiments ranged from 88.4 to 96.0 %. The presented solution is an innovative approach to the use of SCG in the processing of copper slags.
4
Content available remote Wpływ żużla pomiedziowego na właściwości mechaniczne i wytrzymałość różnych betonów
Velumani M., Kumar K. Nirmal
Cement Wapno Beton
|
2021
|
R. 26, nr 2
156--166
PL
W pracy zbadano wpływ żużla pomiedziowego na właściwości mechaniczne i wytrzymałość mieszanek betonowych o normalnej wytrzymałości [BNW] betonu o wysokiej wytrzymałości [BWW] i betonu ultra wysokowytrzymałego [BUWW]. Żużlem pomiedziowym, który jest produktem ubocznym z produkcji miedzi, zastępuje się kruszywo drobne w różnych proporcjach. Z badań wynika, że wytrzymałość na ściskanie ulega znacznej poprawie w przypadku zastąpienia do 60% kruszywa drobnego tym żużlem, we wszystkich mieszankach. Ponadto stwierdzono, że nawet całkowite zastąpienie kruszywa drobnego żużlem pomiedziowym zwiększa wytrzymałość na ściskanie i jest ona większa niż w przypadku mieszanki wzorcowej. Badania wytrzymałości, szybki pomiar penetracji chlorków, badanie sorpcji i nasiąkliwości wykazały znaczną odporność na penetrację chlorków, sorpcję i nasiąkliwość. Przyczynę znacznej poprawy wytrzymałości na ściskanie i trwałości betonu można przypisać zarówno aktywności pucolanowej tego żużla, jak i efektowi wypełniacza matrycy cementowej.
EN
In the present study, the effect of copper slag on mechanical properties and durability aspects for Normal Strength Concrete [NSC], High Strength Concrete [HSC] and Ultra-High Strength Concrete [UHSC] mixes have been investigated. Copper slag, which is the by-product discharged from the copper manufacturing industry is replaced by fine aggregate in different proportions. It is observed from the studies that compressive strength has been significantly improved up to 60% replacement of fine aggregate by copper slag for all the mixes. Further, it is noted that even with 100% replacement of fine aggregate by copper slag, the compressive strength is higher than for the control mix. Durability studies such as rapid chloride penetration test, water sorptivity test and water absorption test showed significant resistance to chloride penetration, sorptivity and water absorption. The reason for significant improvement in compressive strength and durability aspects could be attributed to both pozzolanic activity and filler effect over the cementitious matrix effectively.
5
Content available Chemical and Mineralogical Analysis of Reformed Slag During Iron Recovery from Copper Slag in the Reduction Smelting
Erdenebold Urtnasan, Wang Jei-Pil
Archives of Metallurgy and Materials
|
2021
|
Vol. 66, iss. 3
809--818
EN
Copper slag is usually a mixture of iron oxide and silicon dioxide, which exist in the form of fayalite (2FeO·SiO2), and contains ceramic components as the SiO2, Al2O3 and CaO depending on the initial ore quality and the furnace type. Our present study was focused on manufacture of foundry pig iron with Cu content from copper slag using high-temperature reduction smelting and investigate utilization of by-products as a reformed slag, which is giving additional value to the recycling in a replacement of raw material of Portland cement. Changes of the chemical and mineralogical composition of the reformed slag are highly dependent on the CaO concentration in the slag. The chemical and mineralogical properties and microstructural analysis of the reformed slag samples were determined through X-ray Fluorescence spectroscopy, X-Ray diffractometer and Scanning Electron Microscopy connected to the dispersive spectrometer studies.
6
Content available Thermal and mechanical properties of lightweight concrete with waste copper slag as fine aggregate
Jaskulski Roman, Dolny Piotr, Yakymechko Yaroslav
Archives of Civil Engineering
|
2021
|
Vol. 67, nr 3
299--318
EN
The article presents the results of investigation of mechanical and thermal properties of lightweight concrete with waste copper slag as fine aggregate. The obtained results were compared with the results of concrete of the same composition in which natural fine aggregate (river sand) was used. The thermal properties tests carried out with the ISOMET 2114 device included determination of the following values: thermal conductivity coefficient, thermal volume capacity and thermal diffusivity. After determining the material density, the specific heat values were also calculated. The thermal parameters were determined in two states of water saturation: on fully saturated material and dried to constant mass at 65°C. Compressive strength, open porosity and bulk density are given as supplementary values. The results of the conducted research indicate that replacing sand with waste copper slag allows to obtain concrete of higher ecological values, with similar mechanical parameters and allowing to obtain significant energy savings in functioning of cubature structures made of it, due to a significantly lower value of thermal conductivity coefficient.
PL
W badaniach opisanych w niniejszej pracy określono właściwości termiczne betonu lekkiego oraz jego właściwości mechaniczne (wytrzymałość na ściskanie i rozciąganie). W części serii zamiast piasku jako kruszywo drobne zastosowano odpadowy żużel pomiedziowy, co umożliwiło określenie wpływu tego materiału na właściwości cieplne betonu lekkiego oraz ocenę, czy wpływ ten jest równie wyraźny jak w przypadku betonu zwykłego i ciężkiego. Zbadano również wpływ ilości użytego cementu (200 kg/m3 i 300 kg/m3) oraz stosunku woda/cement (0,50, 0,55 i 0,60). Wykonano łącznie dwanaście serii betonu. W sześciu z nich jako kruszywo drobne zastosowano piasek rzeczny, a w kolejnych sześciu zastąpiono go odpadowym żużlem pomiedziowym. Wymiany dokonano w stosunku masowym 1:1. Zastosowano cement portlandzki wieloskładniowy CEM II/B-M (V-LL) 32,5 R. Kruszywo grube składało się z dwóch frakcji kruszywa lekkiego. Frakcją 4-8 mm był kruszywo Certyd, a frakcję 8-16 mm stanowił keramzyt. Całkowita ilość wody zastosowanej w recepturach uwzględniała chłonność kruszywa lekkiego, którą badano przed przygotowaniem receptur. Właściwości cieplne badano na próbkach o średnicy 150 mm i grubości ok. 25-30 mm. W celu zbadania właściwości betonu w dwóch różnych stanach granicznego nasycenia, część próbek przechowywano w wodzie do momentu przeprowadzenia badań, a pozostałą część umieszczono w suszarce w temperaturze 65°C do momentu osiągnięcia stabilnej masy. Wytrzymałość na ściskanie badano na kostkach 100 mm. Wpływ rodzaju zastosowanego kruszywa drobnego nie był w tym przypadku jednoznaczny, gdyż w przypadku połowy serii, wymiana piasku na odpadowy żużel pomiedziowy spowodowała wzrost wytrzymałości, a w przypadku pozostałych serii jej spadek. Określono również porowatość materiału. Analiza wyników wykazała, że zwiększa się ona wraz z ilością cementu w betonie i współczynnikiem w/c. Ponadto beton wykonany z wykorzystaniem odpadowego żużla pomiedziowego wykazuje nieco wyższą porowatość niż beton wykonany z wykorzystaniem piasku o tych samych pozostałych parametrach (stosunek w/c i ilość cementu). Właściwości cieplne zmierzono metodą niestacjonarną za pomocą urządzenia ISOMET 2114 wyposażonego w sondę powierzchniową. Uzyskane wartości właściwości cieplnych poddano analizie statystycznej. Ze względu na dużą ilość danych analizę ograniczono do jednoczynnikowej analizy wariancji (ANOVA). Ponieważ w przypadku każdego z rozpatrywanych wariantów analiza wykazała, że otrzymane różnice między seriami są istotne statystycznie, przeprowadzono następnie analizę post hoc. Niezależnie od wymienionych powyżej czynników różnicujących poszczególne serie analizie poddano również wartości otrzymane w przypadku próbek nasyconych wodą i wysuszonych do stałej masy. Wyniki badania współczynnika przewodności cieplnej wskazują na istotne różnice w wartościach tego parametru w zależności od nasycenia betonu. Próbki wysuszone charakteryzują się niższą wartością współczynnika przewodnictwa cieplnego. Większe zróżnicowanie tego parametru w zależności od poziomu nasycenia betonu wodą dało się zaobserwować w przypadku serii z wykorzystaniem piasku. W tej grupie nie ma również korelacji pomiędzy porowatością a zróżnicowaniem wyników uzyskanych na próbkach nasyconych i wysuszonych. Serie betonu wykonane z wykorzystaniem odpadowego żużla pomiedziowego wykazują korelację pomiędzy spadkiem przewodności cieplnej a porowatością. Korelacja ta jest jednak przeciwna od tej, jakiej należałoby się spodziewać. Wraz ze wzrostem porowatości zmniejsza się wpływ stanu nasycenia próbek.
7
Content available Manufacture of Low Sulphur Pig Iron from Copper Slag
Erdenebold Urtnasan, Sung Choi Moo, Wang Jei-Pil
Archives of Metallurgy and Materials
|
2020
|
Vol. 65, iss. 1
349--355
EN
Copper slag differs by chemical composition and structure, depending on the type of processing. Copper slag typically contains about 1 wt.% copper and 40 wt.% iron depending upon the initial ore quality and type of furnace used. The aim is to produce a typical foundry pig iron with the chemical composition of C > 3.40 wt.%, Si 1.40 to 1.80 wt.%, Mn 0.30 to 0.90 wt.%, P < 0.03 wt.% and S < 0.03 wt.% from copper slag. But foundry pig iron manufactured from copper slag contains a high sulphur content. Therefore, this study examines how to conduct desulphurization. Desulphurization roasting and reduction smelting with desulphurization additives used to remove sulphur from the copper slag. The results showed that desulphurization effect of desulphurization roasting is poor but when combined with reduction smelting with CaO addition is possible to manufacture low sulphur pig iron from copper smelting slag.
8
Content available Recovery of Pig Iron from Copper Smelting Slag by Reduction Smelting
Erdenebold U., Choi M.-H., Wang J.-P.
Archives of Metallurgy and Materials
|
2018
|
Vol. 63, iss. 4
1793--1798
EN
Copper slag is a by-product obtained during smelting and refining of copper. Copper smelting slag typically contains about 1 wt.% copper and 40 wt.% iron depending upon the initial ore quality and the furnace type. Main components of copper slag are iron oxide and silica. These exist in copper slag mainly in the form of fayalite (2FeO ·SiO2 ). This study was intended to recover pig iron from the copper smelting slag by reduction smelting method. At the reaction temperature of below 1400°С the whole copper smelting slag was not smelted, and some agglomerated, showing a mass in a sponge form. The recovery behavior of pig iron from copper smelting slag increases with increasing smelting temperature and duration. The recovery rate of pig iron varied greatly depending on the reaction temperature.
9
Content available Recovery of Iron from Copper Slag by Carbothermic Reduction and Magnetic Separation in the Presence of CaO
Chun T., Mu G., Di Z., Long H., Ning C., Li D.
Archives of Metallurgy and Materials
|
2018
|
Vol. 63, iss. 1
299--305
EN
The carbothermic reduction of copper slag at the different binary basicity (CaO/SiO2 ) was carried out for recovering iron by wet magnetic separation. Calcium carbonate is found to be capable of improving the iron recovery, as well as increasing the particle size of metallic iron significantly. Experimental evidence showed that CaO reacted with SiO2 to form calcium silicate and FeO was liberated from the 2FeO.SiO2 , decreased the content of Fe in the slags, which improved the iron recovery during the magnetic separation. The final product, assaying 90.23%Fetotal (representing a metallization degree of 93.94%) and 0.58% Cu at the iron recovery of 85.70% was achieved at the basicity of 0.60, which can be briquetted as a burden material for weathering resistant steel making by electric arc furnace to replace part of scrap.
10
Content available The Decopperization and Coagulation by Use the Carbon-N-Ox Method
Bydałek A., Migas P., Wołczyński W., Karwan-Baczewska J.
Archives of Metallurgy and Materials
|
2017
|
Vol. 62, iss. 4
2375--2380
EN
This paper discusses the impact of complex chemical reagents during the process of decopperisation of slag. The beneficial effect of carbide response factors with the participation of nitrogen was indicated as well as the role of stimulators surfactants. Based on the results of the research the basic structure of the slag during decopperisation was systematized. The effects of coagulation of droplets of copper in the slag were shown in this paper.
11
Content available remote Surface blast-cleaning waste as a replacement of fine aggregate in concrete
Kubissa W., Jaskulski R., Simon T.
Architecture Civil Engineering Environment
|
2017
|
Vol. 10, no. 3
89--94
EN
In the article the possibility of using a surface blast-cleaning waste as a replacement of fine aggregate in concrete manufacturing was presented. Concretes with w/c ratio 0.6 and 300 kg/m3 dosage of cements: CEMI 32.5R and CEMII/B-V 32.5N were tested. The quite high value of the w/c ratio resulted in good compactibility of the mixtures without use of plasticizer. The replacement rate of the fine aggregate (0-2 mm) with copper slag (CS) was 33%, 66% and 100% respectively. Concretes of the same composition served for reference except for with river sand as fine aggregate instead of slag. The performed tests focused on: compressive and tensile strength (both after 28 days), sorptivity, free water absorption capacity and abrasion resistance. The obtained results showed that the strength and some other tested properties of concretes with copper slag as sand replacement were similar or even better than that of the control mixtures.
PL
W artykule zaprezentowano badania na temat możliwości zastąpienia całości lub części drobnego kruszywa w betonie żużlem pomiedziowym - odpadem z piaskowania. Badano beton z w/c = 0.6 i zawartością cementów CEM I 32.5 R i CEM II/B-V 32.5N 300 kg/m3. Stosunkowo wysoka wartość współczynnika w/c pozwoliła na dobre zagęszczenia mieszanek bez użycia plastyfikatora. Stopień zastąpienia drobnego kruszywa (0-2 mm), żużlem pomiedziowym wyniósł odpowiednio 33%, 66% i 100%. Beton o tym samym składzie ze 100% piasku rzecznego jako kruszywa drobnego służył jako referencyjny. Przeprowadzone badania koncentrowały się na: wytrzymałości na ściskanie i rozciąganie (po 28 dniach), sorpcyjności, nasiąkliwości i odporności na ścieranie. Uzyskane wyniki wykazały, że wytrzymałość i niektóre inne badane właściwości betonów z odpadem jako zamiennikiem piasku były podobne lub nawet lepsze niż właściwości betonu referencyjnego.
12
Content available Spoiwo bezklinkierowe otrzymane w wyniku alkalicznej aktywacji zeszklonego żużla pomiedziowego
Kuterasińska J., Król A.
Szkło i Ceramika
|
2016
|
R. 67, nr 2
16--19
PL
W artykule przedstawiono wyniki badań dotyczące nowego rodzaju spoiwa bezklinkierowego powstałego w wyniku aktywacji alkalicznej granulowanego żużla pomiedziowego. Ważnym elementem przeprowadzonych badań było określenie wpływu standardowych i przyspieszonych warunków dojrzewania na właściwości mechaniczne otrzymanych kompozytów.
EN
The article presents the results of research on a new type of non-clinker binder obtained as a result of alkaline activation of a granular copper slag. An important element of the study was determination of the maturation conditions effect (standard or accelerated) on the mechanical properties of the composites.
13
Content available Kruszywa z żużla powstającego przy produkcji miedzi i możliwości ich wykorzystania w świetle wymagań ochrony środowiska
Rajczyk K., Rolka G., Gambal P.
Prace Instytutu Ceramiki i Materiałów Budowlanych
|
2016
|
R. 9, nr 27
84--94
PL
W pracy przedstawiono wyniki badań promieniotwórczości naturalnej kruszyw wyprodukowanych w KGHM Metraco S.A. z żużla powstającego przy produkcji miedzi. Porównano poziom aktywności promieniotwórczej kruszyw naturalnych i sztucznych oraz surowców i materiałów budowlanych. Zwrócono szczególną uwagę na właściwości kruszyw z żużla pomiedziowego w świetle wymagań ochrony środowiska oraz pod kątem jego przydatności dla budownictwa drogowego. Oceniono możliwość zastosowania odpowiednich frakcji kruszyw pomiedziowych jako substytutu kruszyw naturalnych do produkcji betonów samozagęszczalnych.
EN
In this elaboration, the results of testing the aggregates natural radioactivity, produced by KGHM Metraco form slag originated from production of copper, were shown. The level of natural and artificial aggregates as well as raw and building materials radioactivity was compared. The attention was focused on the properties of copper slag aggregates in terms of environmental protection as well as their utility in road engineering. The possibility of using appropriate copper slag aggregates fractions against natural aggregates to SCC was evaluated.
14
Content available Recovery of copper from copper slag and copper slag flotation tailings by oxidative leaching
Urosevic D. M., Dimitrijevic M. D., Jankovic Z. D., Antic D. V.
Physicochemical Problems of Mineral Processing
|
2015
|
Vol. 51, iss. 1
73--82
EN
Copper smelter slag and copper smelter slag flotation tailings were leached using sulphuric acid solutions, without or with the addition of either ferric sulphate or hydrogen peroxide. Copper extraction from the slag was typically found to be twice as high as that from the slag flotation tailings. Hydrogen peroxide was determined to be the best lixiviant. Thus, copper and iron extractions were 63.4% and 48.6%, respectively, when leaching the slag with 3 M H2O2, after 120 minutes of reaction at room temperature. Copper dissolution was generally found to be the dominant process within the first 60 minutes of reaction, whereas iron dissolution dominated afterwards.
15
Content available remote Mechanical properties of alkali-acivated binders based on copper slag
Kuterasińska J., Król A.
Architecture Civil Engineering Environment
|
2015
|
Vol. 8, no. 3
61--67
EN
The paper describes the possibility of using copper slag, an industrial waste from smelting of copper as a basic component of hydraulic binders obtained by means of the alkaline activation. For the purpose, the aqueous sodium silicate and technical sodium metasilicate were used. Mortars, having undergone the activation process were cured under laboratory conditions (temp. 20±1°C and relative humidity approx. 60%) and were subjected to low pressure heat treatment at a temperature of 80°C. Research over the alkaline activation of slag proved that the desirable quality of alkali-activated binders is achievable just in case of using granulated copper slag, where 98% of the base mass constitutes of glassy phase, and water glass with the lowest value of silicate modulus (Mk = 1.75).
PL
W artykule przedstawiono możliwości wykorzystania odpadowego żużla pomiedziowego pochodzącego z hutnictwa miedzi jako podstawowego składnika spoiw hydraulicznych otrzymanych na drodze aktywacji alkalicznej. W procesie stosowano szkło wodne sodowe o zmiennym module krzemianowym oraz techniczny metakrzemian sodu. Zaprawy po procesie aktywacji dojrzewały w warunkach laboratoryjnych (temp. 20±1°C i wilgotność względna ok. 60%) oraz były poddane niskociśnieniowej obróbce cieplnej w temperaturze 80°C. Badania nad aktywacją alkaliczną żużla dowiodły, że możliwe jest uzyskanie pożądanej jakości spoiw aktywowanych alkalicznie tylko w przypadku stosowania granulowanego żużla pomiedziowego, w którym 98% masy zasadniczej stanowi faza szklista oraz przy użyciu szkła wodnego o najniższym module krzemianowym (Mk = 1.75).
16
Content available Żużel pomiedziowy jako surowiec w produkcji alkalicznie aktywowanych spoiw żużlowych
Kuterasińska J., Król A.
Prace Instytutu Ceramiki i Materiałów Budowlanych
|
2014
|
R. 7, nr 17
21--36
PL
W artykule opisano badania, których celem było opracowanie nowej rodziny spoiw hydraulicznych na bazie żużla pomiedziowego, stanowiącego odpad przemysłowy z hutnictwa miedzi. Granulowany i szybowy żużel pomiedziowy nie wykazuje aktywności hydraulicznej, dlatego w badaniach podjęto próby ich alkalicznej aktywacji. W tym celu wykorzystano 5 rodzajów aktywatorów alkalicznych w postaci sodowego szkła wodnego oraz technicznego metakrzemianu sodowego o zmiennym module krzemianowym. Badania nad aktywacją alkaliczną żużla dowiodły, że najlepsze właściwości mechaniczne (wytrzymałość na ściskanie po 90 dniach wynosiła 53,5 MPa) osiągalne są tylko w przypadku stosowania granulowanego żużla pomiedziowego (100% masy zasadniczej żużla stanowi faza szklista) oraz przy użyciu szkła wodnego o najniższym module krzemianowym (Mk=1,79). Wraz z malejącym modułem krzemianowym zastosowanego szkła wodnego sodowego, widoczny był wzrost wytrzymałości.
EN
The article describes research aimed at developing a new family of hydraulic binders based on copper slag, which is industrial waste from smelting of copper. Granulated and lump copper slags do not show hydraulic activity, so the studies were based on their alkaline activation. For this purpose the five types of alkaline activators in the form of aqueous sodium silicate and technical sodium metasilicate were used. All activators were varied in terms of silicate modulus value. Studies on the alkaline activation of slags showed that the best mechanical properties (compressive strength after 90 days amounted even 53.5 MPa) is achievable only in case of using granulated copper slag (100% of the slag constitutes the glassy phase) and water glass with the lowest value of silicate modulus (Mk = 1.79). Along with decreasing silicate module of used water glass there is a significant increase in strength.
17
Content available A study of the optimal model of the flotation kinetics of copper slag from copper mine Bor
Stanojlovic R. D., Sokolovic J. M.
Archives of Mining Sciences
|
2014
|
Vol. 59, no. 3
821--834
EN
In this study the effect of mixtures of copper slag and flotation tailings from copper mine Bor, Serbia on the flotation results of copper recovery and flotation kinetics parameters in a batch flotation cell has been investigated. By simultaneous adding old flotation tailings in the ball mill at the rate of 9%, it is possible to increase copper recovery for about 20%. These results are compared with obtained copper recovery of pure copper slag. The results of batch flotation test were fitted by MatLab software for modeling the first-order flotation kinetics in order to determine kinetics parameters and define an optimal model of the flotation kinetics. Six kinetic models are tested on the batch flotation copper recovery against flotation time. All models showed good correlation, however the modified Kelsall model provided the best fit.
PL
W pracy badano wpływ mieszanin żużla miedziowego i odpadów poflotacyjnych w kopalni miedzi Bor na efektywność odzysku miedzi na drodze flotacji oraz parametry kinetyki flotacji w urządzeniu do flotacji pracującego w trybie cyklicznym. Poprzez równoczesne wprowadzenie starych odpadów poflotacyjnych rozdrobnionych w młynie kulowym w ilości 9%, możliwe jest podniesienie poziomu odzysku miedzi o około 20%. Wyniki te porównać można z poziomem odzysku miedzi z czystego żużla. Wyniki badań flotacji porcji wsadu zostały dopasowane przy użyciu oprogramowania MatLab do modelowania kinetyki flotacji (model pierwszego rzędu) w celu określenia parametrów kinetycznych i dla zdefiniowania optymalnego modelu kinetyki procesu flotacji. Przebadano sześć modeli kinetyki, analizując wielkość odzysku miedzi ze wsadu w stosunku do czasu flotacji. Wszystkie modele wykazywały dużą korelację, a najlepsze dopasowanie wykazywał zmodyfikowany model Kelsalla.
18
Content available Wykorzystanie odpadu przemysłowego - zużytego ścierniwa POLGRIT do produkcji cementu
Janecka L., Weryński B.
Prace Instytutu Szkła, Ceramiki, Materiałów Ogniotrwałych i Budowlanych
|
2008
|
R. 1, nr 2
39-50
PL
W artykule omówiono możliwości wykorzystania żużla pomiedziowego, stanowiącego odpad ścierniwa POLGRIT, w przemyśle cementowym jako składnika cementu. Stwierdzono, że odpad ten z uwagi na wysoką zawartość fazy szklistej oraz krzemionki reaktywnej posiada właściwości pucolanowe. Odpad ścierniwa POLGRIT można stosować jako dodatek do produkcji cementów klasy 32,5.
EN
The article describes possibility of cupric slag utilization which is waste of POLGRIT abrasive used as cement component in cement industry. There was stated that this waste has pozzolanic properties caused by high content of glassy phase and reactive silica. Waste of POLGRIT abrasive can be used as additive to production of cements class 32,5.
19
Zwilżalność w układzie: ciało stałe-ciekła faza żużlowa
Łabaj J., Siwiec G.
Rudy i Metale Nieżelazne
|
2007
|
R. 52, nr 6
307-310
PL
Przestawiono wyniki badań kąta zwilżania ciekłych żużli syntetycznych i żużli pochodzących z przemysłu miedziowego. Badania prowadzono metodą kropli leżącej z wykorzystaniem mikroskopu wysokotemperaturowego sprzężonego z kamerą i komputerem. w zakresie temperatur 1423÷1623 K. Przeprowadzone badania zwilżalności wzorcowego podłoża platynowego przez żużle wykazują dobrą zwilżalność metalu. W przypadku części badanych próbek po osiągnięciu temperatury topnienia całkowicie zwilżały one materiał podkładki. W przypadku pozostałych próbek uzyskanie całkowitego zwilżenia materiału podkładki wymagało wyższych temperatu
EN
In the paper, the results of the study on the contact angles of liquid synthetic slags and the copper industry slags have been presented. In the study, the sessile drop method was used and a high-temperature microscope coupled with a camera and a computer were employed, in the temperature range of 1423÷1623 K. The results of the study on the wettability of the system: standard platinum substrate-slag showed good metal wettability properties. In a part of the studied samples, after reaching the melting point, the complete wettability of the substrate material was noticed. In the other samples, the complete wettability of the substrate material required higher temperatures.
first rewind previous Strona / 1 next fast forward last
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.