Effect of Sintering Holding Time and Cooling Rate on the Austenite Stability and Mechanical Properties of Nanocrystalline FeCrC Alloy

Kim Gwanghun, Jeon Junhyub, Seo Namhyuk, Choi Seunggyu, Oh Min-Suk, Son Seung Bae, Lee Seok-Jae

Archives of Metallurgy and Materials

|

2021

|

Vol. 66, iss. 3

759--763

EN

The effects of the sintering holding time and cooling rate on the microstructure and mechanical properties of nanocrystalline Fe-Cr-C alloy were investigated. Nanocrystalline Fe-1.5Cr-1C (wt.%) alloy was fabricated by mechanical alloying and spark plasma sintering. Different process conditions were applied to fabricate the sintered samples. The phase fraction and grain size were measured using X-ray powder diffraction and confirmed by electron backscatter diffraction. The stability and volume fraction of the austenite phase, which could affect the mechanical properties of the Fe-based alloy, were calculated using an empirical equation. The sample names consist of a number and a letter, which correspond to the holding time and cooling method, respectively. For the 0A, 0W, 10A, and 10W samples, the volume fraction was measured at 5.56, 44.95, 6.15, and 61.44 vol.%. To evaluate the mechanical properties, the hardness of 0A, 0W, 10A, and 10W samples were measured as 44.6, 63.1, 42.5, and 53.8 HRC. These results show that there is a difference in carbon diffusion and solubility depending on the sintering holding time and cooling rate.

2

The Characterization Of Cast Fe-Cr-C Alloy

Wieczerzak K., Bała P., Stępień M., Cios G., Kozieł T.

Archives of Metallurgy and Materials

|

2015

|

Vol. 60, iss. 2A

779--782

EN

The paper presents the results of the characterization of alloy from Fe-Cr-C (carbon content 0.79 wt.%) system including the microstructure, phase analysis, morphology and hardness in as cast state. The chemical composition was designed to create chromium-rich ferritic matrix with high volume fraction of carbides in form of interdendritic eutectics. The research was carried out on the cross section of the ingot, synthesized in an arc furnace under high purity argon atmosphere and crystallized on water-cooled copper mould. Microstructural characterization was carried out by light microscopy and scanning electron microscopy (SEM). Phase identification was performed by X-Ray diffraction (XRD). The microstructure of the investigated alloy is composed of primary and secondary dendrites Fe-Cr solid solution and complex M23C6 and M7C3 carbides in interdendritic areas. Segregation of Cr and C during crystallization causes precipitation of M7C3 carbides. The average hardness of the alloy is 205±12 HV10.

PL

W pracy dokonano analizy mikrostruktury, faz oraz wybranych właściwości stopu w stanie lanym z układu Fe-Cr-C (stężenie węgla 0,79% mas.). Skład chemiczny zaprojektowano tak, aby uzyskać osnowę ferrytyczną bogatą w chrom z dużym udziałem objętościowym węglików eutektycznych. Badania przeprowadzono na przekroju poprzecznym wlewka wykonanego w piecu łukowym w atmosferze ochronnej argonu, krystalizującego na miedzianym łożu, chłodzonym wodą. Obserwacje mikrostruktury przeprowadzono z wykorzystaniem mikroskopii świetlnej oraz skaningowej mikroskopii elektronowej (SEM). Identyfikację faz wykonano za pomocą rentgenowskiej analizy fazowej. Mikrostruktura badanego stopu składa się z dendrytów pierwszo i drugorzędowych roztworu stałego chromu w żelazie α oraz węglików złożonych M23C6 i M7C3, powstałych w obszarach międzydendrytycznych. Segregacja Cr i C podczas krystalizacji, sprzyja wydzielaniu węglików typu M7C3. Średnia twardość stopu wynosi 205±12 HV10.

3

Diffusion of C and Cr During Creation of Surface Layer on Cast Steel Casting

Szajnar J., Dulska A., Wróbel T., Suchoń J.

Archives of Metallurgy and Materials

|

2014

|

Vol. 59, iss. 3

1085--1087

EN

In paper a method of improvement in utility properties of unalloyed cast steel casting in result of diffusion of C and Cr in process of creation of surface layer is presented. The aim of paper was determination of diffusion range of basic elements of alloyed surface layer. Moreover a quantitative analysis of carbides phase strengthens alloyed surface layer of casting was carried out. The results of studies shown that important factors of surface layer creation are maximal temperature Tmax on granular insert – cast steel boundary dependent of pouring temperature, granularity Zw of Fe-Cr-C alloy insert and thickness of casting wall gśo. On the basis of obtained results was affirmed that with increase of thickness of casting wall increases range of diffusion in solid state in Fe-Cr-C grains and in liquid state. Moreover the range of Tmax = 13001500°C favours creation of the proper alloyed surface layers on cast steel.

PL

W pracy przedstawiono metodę poprawy własności użytkowych odlewów ze staliwa niestopowego w wyniku dyfuzji C i Cr występującej w procesie wytwarzania warstwy wierzchniej. Zasadniczym celem badań było określenie zasięgu dyfuzji podstawowych składników wierzchniej warstwy stopowej. Badania obejmowały również analizę ilościową powstałej fazy węglikowej umacniającej warstwę wierzchnią odlewu. Wyniki badań oraz ich analiza wykazały, że istotnymi zmiennymi czynnikami procesu powstawania warstwy są maksymalna temperatura Tmax osiągana na granicy ziarnista wkładka – staliwo zależna od temperatury zalewania, ziarnistość Zw wkładki z stopu Fe-Cr-C i grubość ścianki odlewu gśo. Na podstawie uzyskanych wyników stwierdzono, że wraz ze wzrostem grubości ścianki odlewu rośnie zasięg procesów dyfuzyjnych zarówno w stanie stałym w ziarnach Fe-Cr-C jak i w stanie ciekłym. Ponadto zakres Tmax = 13001500°C sprzyja powstaniu prawidłowej powierzchniowej warstwy stopowej na staliwie.

4

Wpływ krzemu na krystalizację stopów typu Fe-Cr-C

Granat K.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 43

207--213

PL

Z powodu znacznych strat w gospodarce spowodowanych tarciem, uzasadnione jest podejmowanie badań mających na celu zwiększenie odporności na zużycie części maszyn poprzez zastosowanie do ich budowy nowych materiałów lub poprawę odporności na zużycie obecnie stosowanych tworzyw. [...]

5

Prognozowanie zużycia stopów Fe-Cr-C w temperaturze 450ºC na podstawie wykresów ATD

Drotlew A.

Krzepnięcie Metali i Stopów

|

2000

|

R. 2, nr 44

87--95

PL

W pracy zaprezentowano możliwość przewidywania charakterystyki zużycia strumieniem ścierniwa na podstawie parametrów ATD stopu. Informacja taka daje podstawę do ewentualnej korekty składu chemicznego wytapianych materiałów zmierzającej do poprawy ich właściwości. Krótki czas oczekiwania na niezbędne informacje stwarza możliwości uzyskania zarówno korzyści ekonomicznych, jak i dotyczących jakości metalu.

EN

The work carried out has allowed to elaborate regression equation with good statistical parameters. It gives possibility to determine the expected wear of material on the base of Thermal Derivative Analysis parameters (solidus temperature and self cooling time) for any angle of abrasive incidence in the range of 15÷60º. The obtained equation can be applied for thin-walled castings (wall thickness up to 6 mm) made of chromium alloys from the ferritic range of Fe-Cr-C equilibrium system and after homogenising treatment. The level of wear is forecasted for the work under conditions of loose abrasive incidence at 450ºC. Since the obtainment of ATD curve takes less time than the execution of chemical analysis, there is possible to shorten the time of keeping metal in furnace. Therefore the economical benefit and an advantage relating to the quality of material (melting loss of alloying elements or an increase of Si content in alloy) can be achieved.