Test stand for the examination of steel cyclic properties under the condition of temperature changes

• Autorzy: Mroziński S. , Marciniak B.

Warianty tytułu

PL

Stanowisko do badań właściwości cyklicznych stali w warunkach zmian temperatury

• Języki publikacji: EN

Abstrakty

EN

In this study, a stand for tests of technical objects under the conditions of thermal and mechanical fatigue is presented. Temperature and load changes and the interrelations between them cause difficulties in controlling and recording basic parameters of fatigue tests in laboratory conditions. The article presents the design and creation of a system for temperature change control and adjustment during fatigue tests under the conditions of thermal loading. The test stand was built through the modernization of a standard strength-testing machine.

PL

W pracy przedstawiono stanowisko do badań w warunkach zmęczenia cieplnego oraz mechanicznego. Zmiany temperatury i obciążenia oraz występujące pomiędzy nimi interakcje powodują, że w warunkach laboratoryjnych występują trudności w zakresie sterowania i rejestracji podstawowych parametrów prób zmęczeniowych. W artykule opisano projekt i wykonanie układu sterowania oraz kontroli zmian temperatury podczas badań zmęczeniowych w warunkach obciążeń cieplnych. Stanowisko badawcze zostało stworzone poprzez modernizację standardowej maszyny wytrzymałościowej.

Słowa kluczowe

EN

mechanical fatigue; thermal fatigue; service load; control; fatigue specimen

PL

zmęczenie mechaniczne; zmęczenie cieplne; obciążenie eksploatacyjne; sterowanie; próba zmęczeniowa

• Wydawca: Wydawnictwo Naukowe Instytutu Technologii Eksploatacji - Państwowego Instytutu Badawczego
• Czasopismo: Problemy Eksploatacji
• Rocznik: 2014
• Tom: no. 3
• Strony: 5--16
• Opis fizyczny: Bibliogr. 9 poz., rys., tab., wykr.

Twórcy

autor

Mroziński S.

• UTP University of Science and Technology, Bydgoszcz

autor

Marciniak B.

• UTP University of Science and Technology, Bydgoszcz

Bibliografia

• 1. Nagode M.; Zingsheim M.: An online algorithm for temperature influenced fatigue life estimation: strain-life approach International Journal of Fatigue 26 (2004), pp. 155–161.
• 2. Mroziński S., Golański G., Low cycle fatigue and cyclic softening behaviour of martensitic cast steel, Engineering Failure Analysis, EFA 2086 November 2013 pp. 692–702.
• 3. Byrne J.; Kan N.Y.K.; Hussey I.W.; Harrison G.F.: Influence of sub-surface defects on low-cycle fatigue life in a gas turbine disc alloy at elevated temperature. International Journal of Fatigue 21 (1999) pp.195–206.
• 4. Nagesha A.; Valsan M.; Kannan R.; Bhanu Sankara Rao K.; Mannan S.L.: Influence of temperature on the low cycle fatigue behaviour of a modified 9Cr-1 Mo ferritic steel International Journal of Fatigue 24 (2002), pp. 1285–1293.
• 5. Mroziński S.; Skocki R.: Influence of temperature on the cyclic properties of martensitic cast steel. Materials Science Forum Vol. 726 (2012) pp. 150-–155.
• 6. Junak G., Cieśla M., Low-cycle fatigue of P91 and P92 steels used in the power engineering industry, Archiv. of Mater. Sc. Eng., 2011, 48 (1), pp. 19–24.
• 7. Marciniak T., Lutowski Z., Bujnowski S., Boroński D., Giesko T., „Application of Digital Image Correlation in Fatigue Crack Analysis”, Materials Science Forum Vol. 726 – Fatigue Failure and Fracture Mechanics p. 218–222, 2012 Trans Tech Publications.
• 8. Marciniak T., Lutowski Z., Bujnowski S., Boroński D., Czajka P., „Dual- Band Experimental System For subsurface Cracks Testing”, Materials Science Forum Vol. 726 - Fatigue Failure and Fracture Mechanics p. 222-226, 2012 Trans Tech Publications.
• 9. Boroński D., Giesko T., Marciniak T., Lutowski Z., Bujnowski S. „Detekcja i pomiar długości pęknięcia zmęczeniowego z zastosowaniem systemu FatigueVIEW”, Przegląd Mechaniczny 4/2014, s. 21–27, 2014 IMBiGS.