Lead and zinc determination in cooper alloys by sequential metal vapor elution analysis with an improved column

• Autorzy: Ohta K. , Kawaguti K. , Uegomori H. , Mizuno T.

Warianty tytułu

PL

Oznaczanie ołowiu i cynku w stopach miedzimetodą sekwencyjnego wydzielania par metali przy użyciu udoskonalonej kolumny

• Języki publikacji: EN

Abstrakty

EN

The determinatjon of lead and zinc in copper alloys by sequential metal vapor elution analysis (SMVEA) using an improved column is reported. An improved molybdenum column ( open column, I.D. 1.22 mm) with three ring supporters was developed. An optimum flow rate of the carrier gas (pure argon), the column and vaporization tempe-ratures for separation of the metal vapors were 0.5 ml min-l, 1260°C, and 1470°C, respectively. Under the optimal experimental conditions, Pb and Zn peaks are comple-tely separated from Al, Cd, Cr, Cu, Fe, Ti and Zr peaks. The interferences of matrix elements observed in the determination by GFAAS could be eliminated and an accurate determination of lead and zinc in copper alloys is possible just after only acid-digestion.

PL

Opracowano metodę oznaczania ołowiu i cynku w stopach miedzi metod'l sekwencyj-nego wydzielania par metali przy użyciu udoskonalonej kolumny. Zastosowano mołibdenow'l, udoskonaloną kolumnę (kołumna otwarta, I.D. 122 mm) z trzema wspieraj'lcymi pierścieniami. Optymalna szybkość przepływu gazu nośnego (czysty argon) wynosi 0.5 ml min-l, temperatury -kolumny i odparowania (stosowane do rozdzieIania par metali) wynosz'l odpowiednio 1260°C i 1470°C W optymalnych warunkach doświadczalnych piki Pb i Zn zostały całkowicie oddzielone od pików Al, Cd, Cr, Cu, Fe, Ti and Zr. Wpływy pierwiastków matrycy, obserwowane przy oznacza-niu metodą GFAAS, mogły być usunięte umożliwiaj'lc dokładne oznaczenie ołowiu i cynku w stopach miedzi jedynie po roztworzeniu ich w kwasie.

Słowa kluczowe

EN

SMVEA; load; zinc; copper alloy; absorption spectrometry; molybdenum column

PL

sekwencyjne wydzielanie par metali; ołów; cynk; stop miedzi; spektrometria absorpcyjna; kolumna molibdenowa

• Wydawca: Komitet Chemii Analitycznej PAN
• Czasopismo: Chemia Analityczna
• Rocznik: 1999
• Tom: Vol. 44, No. 2
• Strony: 187--194
• Opis fizyczny: Bibliogr. 16 poz.

Twórcy

autor

Ohta K.

• Department of Chemistry for Materials, Faculty of Engineering, Mie University, Mie, Tsu, 514, Japan

autor

Kawaguti K.

• Department of Chemistry for Materials, Faculty of Engineering, Mie University, Mie, Tsu, 514, Japan

autor

Uegomori H.

• Department of Chemistry for Materials, Faculty of Engineering, Mie University, Mie, Tsu, 514, Japan

autor

Mizuno T.

• Department of Chemistry for Materials, Faculty of Engineering, Mie University, Mie, Tsu, 514, Japan

Bibliografia

• 1. Sokolov D.N., Baidarovtseva M.A. and Vakin N.A., Izv. Akad. Nauk SSSR, Ser. Khim., 1396 (1968).
• 2. Ohta K., Smith B.W., Suzuki M. and Winefordner J.D., Spectrochim. Acta, 37B, 343 (1982).
• 3. Ohta K., Nakajima N., Inui S., Winefordner J.D. and Mizuno T., Talanta, 39, 1643 (1992).
• 4. Ohta K., Taniguti H., Itoh S. and Mizuno T., Mikrochim. Acta, 127, 51 (1997).
• 5. Shaw F. and Ottaway J.M., At. Absorp. Newsl., 13, 77 (1974).
• 6. Baker A.A. and Headridge J.B., Anal. Chim. Acta, 125, 93 (1981).
• 7. Brune D., Gjerdet N. and Paulsen G., Scand. J. Dent. Res., 91, 66 (1983).
• 8. Takada K. and Hirokawa K., Talanta, 30, 329 (1983).
• 9. Lundberg E. and Frech W., Anal. Chim. Acta, 104, 67 (1979).
• 10. Bedard M. and Kerbyson J.D., Anal. Chem., 47, 1441 (1975).
• 11. Fudagawa N., Hioki S., Kubota M. and Kawase A., Bunseki Kagaku, 35, T62 (1986).
• 12. Handbook of Chemistry and Physics [Lide D.R., Ed.], 72nd Edn., pp. 4-36, 46, 53, 56, 64, 67, 108, 111, 113, CRC Press, Boston 1991.
• 13. Suzuki M., Ohta K., Yamakita T. and Katsuno T., Spectrochim. Acta, 35B, 679 (1981).
• 14. Suzuki M. and Ohta K., Anal. Chim. Acta, 151, 401 (1983).
• 15. Ohta K. and Mizuno T., Anal. Chim. Acta, 217, 377 (1989).
• 16. Ohta K., Itoh S. and Mizuno T., Anal. Sci., 7(Sup.), 457 (1991).