Hard anodic coatings on aluminum alloys

• Autorzy: Kwolek P.

Identyfikatory

DOI

10.2478/amst-2017-0016

Warianty tytułu

PL

Wytarzanie twardych powłok anodowych na podłożu stopów aluminium

• Języki publikacji: EN

Abstrakty

EN

The review of the literature concerning hard anodizing of aluminium alloys was performed. The main features of the process was described as well as the influence of the anodizing parameters on the properties of hard anodic coatings. The most common industrial processes of hard anodizing applied for cast and wrought aluminium alloys were presented. The application of hard anodic coatings as well as the possibilities of improvement of their tribological properties were described.

PL

W artykule prowadzono analizę zagadnień dotychczasowych procesów wytwarzania twardych powłok anodowych o dużej odporności na zużycie ścierne. Przedstawiono charakterystykę anodowania twardego oraz wpływ parametrów tego procesu na właściwości powłok tlenkowych. Omówiono najczęściej stosowane procesy wytwarzania twardych powłok anodowych na podłożu stopów aluminium odlewniczych i do przeróbki plastycznej stosowanych m. in. w konstrukcjach lotniczych. Przedstawiono podstawowe zastosowania takich powłok tlenkowych oraz scharakteryzowano możliwości ulepszenia ich właściwości tribologicznych.

Słowa kluczowe

EN

hard anodizing; abrasion resistance; aluminium alloys

PL

anodowanie twarde; odporność na zużycie ścierne; stopy aluminium

• Wydawca: Komitet Budowy Maszyn PAN ; De Gruyter
• Czasopismo: Advances in Manufacturing Science and Technology
• Rocznik: 2017
• Tom: Vol. 41, nr 3
• Strony: 35--46
• Opis fizyczny: Bibliogr. 33 poz., fot., rys., tab.

Twórcy

autor

Kwolek P.

• Rzeszow University of Technology, Faculty of Mechanical Engineering and Aeronautics, Department of Materials Science, Powstancow Warszawy 12, 35-959 Rzeszow

Bibliografia

• [1] T.J. BROWN, N.E. IDOINE, E.R. RAYCRAFT, R.A. SHAW, E.A. DEADY, J. RIPPINGALE, T. BIDE, C.E. WRIGHTON, J. RODLEY: World mineral production 2001-2005. Halston & Co Ltd. Amersham 2007.
• [2] F. HABASHI: Handbook of extractive metallurgy. Wiley-VCH. Weinheim 1997.
• [3] W.D. CALLISTER: Materials Science And Engineering: An Introduction. 7th ed. John Wiley & Sons. New York 2010.
• [4] R.W. REVIE: Uhlig’s corrosion handbook. John Wiley & Sons. New York 2011.
• [5] T. BIESTEK, J. WEBER: Powłoki konwersyjne. Wydawnictwo Naukowo-Techniczne. Warszawa 1968.
• [6] H. DONG: Surface engineering of light alloys. Woodhead Publishing Ltd. Cambridge 2010.
• [7] P.G. SHEASBY, R. PINNER, S. WERNICK: The surface treatment and finishing of aluminium and its alloys. ASM International. Ohio 2011.
• [8] V.F. HENLEY: Anodic oxidation of aluminum and its alloys. Pergamon Press. New York 1982.
• [9] L. HAO, R. CHENG: Sealing processes of anodic coatings-past, present, and future. Metal Finishing, 98(2000), 8-18.
• [10] D.R. GABE: Hard anodizing-what do we mean by hard?, Metal Finishing, 100(2002), 52-58.
• [11] MIL-A-8625F (1993), Anodic coatings for aluminum and aluminum alloys.
• [12] ASTM D4060-09 (2009), Standard test method for abrasion resistance of organic coatings by the Taber abraser.
• [13] ASTM B137-95 (2014), Standard test method for measurement of coating mass per unit area on anodically coated aluminum.
• [14] P. KWOLEK, A. KAMIŃSKI, K. DYCHTOŃ, M. Drajewicz, J. Sieniawski: The corrosion rate of aluminium in the orthophosphoric acid solutions in the presence of sodium molybdate. Corrosion Science, 106(2016), 208–216.
• [15] P. KWOLEK, K. DYCHTOŃ, J. SZYDEŁKO, A. GRADZIK, M. DRAJEWICZ, J. SIENIAWSKI: The influence of sodium molybdate on the rate of corrosion of aluminum in phosphoric (V) acid. Materials Science Forum, 844(2016), 31-37.
• [16] ASTM B117-07a (2007), Standard practice for operating salt spray (Fog), Apparatus.
• [17] L.E. FRATILA-APACHITEI, F.D. TICHELAAR, G.E. THOMPSON, H. TERRYN, P. SKELDON, J. DUSZCZYK, L. KATGERMAN: A transmission electron microscopy study of hard anodic oxide layers on AlSi(Cu) alloys. Electrochimica Acta, 49(2004), 3169-3177.
• [18] Poradnik galwanotechnika. WNT, Warszawa 2002.
• [19] M. JOZEFOWICZ: Hard coat aluminum anodizing. Metal Finishing, 103(2005), 39-41.
• [20] J. RUNGE, L. CHESTERFIELD: The science of successfully anodizing die cast substrates. Aluminium International Today, 22(2010), 30-36.
• [21] L.M. LERNER: Hard anodising of aerospace aluminium alloys, Metal Finishing, 88(2010), 21-24.
• [22] R. SADELER: Effect of a commercial hard anodizing on the fatigue property of a 2014-T6 aluminium alloy. Journal of Materials Science, 41 (2006), 5803–5809.
• [23] A. KUHN: PTFE coating vs. impregnation. Metal Finishing, 102 (2004), 12-17.
• [24] D. ZHANG, G. DONG, Y. CHEN, Q. ZENG: Electrophoretic deposition of PTFE particles on porous anodic aluminum oxide film and its tribological properties. Applied Surface Science, 290 (2014), 466-474.
• [25] T. HATTORI, K. INOGUTT, Y. OHYAMA, Y. NAKAGISHI, M. SAKAGUCHI: Method of making a composite aluminium article. US Patent 5439712, 1995.
• [26] T.R. ROBINSON, L.Y. NELSON: Ultrasonic assisted deposition of anti-stick films on metal oxides. US Patent 6852266B2, 2005.
• [27] W. ZHANG, D. ZHANG, Y. LE, L. LI, B. OU: Fabrication of surface selflubricating composites of aluminum alloy. Applied Surface Science, 255 (2008), 2671-2674.

Uwagi

EN

1. Project no. UOD-DEM-1-557/001, co-financed by the European Union under the European Regional Development Fund within the Innovative Economy Operational Program and Foundation for Polish Science (FNP) are gratefully acknowledged.

PL

2. Opracowanie rekordu w ramach umowy 509/P-DUN/2018 ze środków MNiSW przeznaczonych na działalność upowszechniającą naukę (2018).