Investigation into Biological, Composite Surgical Meshes

• Autorzy: Niekraszewicz A. , Kucharska M. , Struszczyk M. H. , Rogaczewska A. , Struszczyk K.

Warianty tytułu

PL

Badania biologiczne kompozytowych siatek chirurgicznych

• Języki publikacji: EN

Abstrakty

EN

A method is proposed to prepare composite surgical meshes modified by chitosan. The polypropylene mesh OPTOMESHTM Macropore is used as the half product onto which a coating of microcrystalline chitosan with a lowered pH is deposited. The thus modified surgical mesh is sterilized by means of ethylene oxide and assessed in respect to physical–mechanical and biological properties. Cytotoxicity, irritating and allergenic testing was carried out in specialized medical institutions. All examinations made of the microcrystalline chitosancoated meshes confirmed their biocompatibility as acceptable for potential uses in surgery. Hydrolytic and enzymatic degradation of the meshes was estimated, too. It was found that after 180 days the chitosan coating had lost 50% of its original weight when immersed in a bath at 37 °C containing 10 μg/cm3 of lysozyme.

PL

Opracowano metodę wytwarzania kompozytowych siatek chirurgicznych modyfikowanych chitozanem. Wykorzystano półprodukt w postaci polipropylenowych siatek typ OPTOMESHTM Macropore, na które techniką apreterską nanoszono powłokę chitozanową w postaci mikrokrystalicznego chitozanu o obniżonym pH. Modyfikowane siatki chirurgiczne sterylizowano tlenkiem etylenu oraz poddano ocenie parametrów fizyk -mechanicznych i badaniom biologicznym. W wyspecjalizowanych jednostkach medycznych przeprowadzono ocenę cytotoksyczności, działania drażniącego i uczulającego. Przeprowadzone testy wykazały wystarczającą do potencjalnych zastosowań biozgodność kompozytowych siatek chirurgicznych pokrytych mikrokrystalicznym chitozanem. Zbadano podatność na degradację hydrolityczną i enzymatyczną modyfikowanych siatek. Stwierdzono, że w kąpieli zawierającej 10 μg/cm3 lizozymu w temperaturze 37 °C po 180 dobach powłoka chitozanowa wykazuje ponad 50% wag. ubytek masy.

Słowa kluczowe

EN

surgical mesh; chitosan; composite; biodegradation; biocompatibility

PL

siatka chirurgiczna; chitozan; kompozyt; biodegradacja; biokompatybilność

• Wydawca: Sieć Badawcza Łukasiewicz - Łódzki Instytut Technologiczny
• Czasopismo: Fibres & Textiles in Eastern Europe
• Rocznik: 2008
• Tom: Vol. 16, no. 6 (71)
• Strony: 117--121
• Opis fizyczny: Bibliogr. 9 poz., rys., tab.

Twórcy

autor

Niekraszewicz A.

• Institute of Biopolymers and Chemical Fibres, Member of EPNOE, www.epnoe.eu ul. M. Skłodowskiej-Curie 19/27, 90-570 Łódź

autor

Kucharska M.

• Institute of Biopolymers and Chemical Fibres, Member of EPNOE, www.epnoe.eu ul. M. Skłodowskiej-Curie 19/27, 90-570 Łódź

autor

Struszczyk M. H.

• TRICOMED Co., ul. Piotrkowska 270, 90-361 Łódź (at present employed at MORATEX – The Institute of Security Technology, Łódź, Poland)

autor

Rogaczewska A.

• TRICOMED Co., ul. Piotrkowska 270, 90-361 Łódź

autor

Struszczyk K.

• Institut of Technical Biochemistry, Technical University of Łódź ul. B. Stefanowskiego 4/10, 90-924 Łódź

Bibliografia

• 1. www.hernia.org
• 2. Georg E. Wantz, Current Surgical Therapy 1998.
• 3. Trojanowski P., Witczak W., Najdecki M., Stanowski E., Experience in the Treatment of Giant Post-Operation Hernia with the Use of Intraperitoneal Surgical Meshes (in Polish). Pol. Merk. Lek. 2007, Vol. XXII, No. 131, 376
• 4. Coob W.S., Burns J.M., Peindl R.D., Carbonell A.M., Textile Analysis of Heavy Weight, Mid-Weight, and Light Weight Polypropylene Mesh in a Porcine Ventral Hernia Model,Journal Surgical Research 2006, Vol. 136, No. 1, November, pp. 1-7.
• 5. Niekraszewicz A., Kucharska M., Wawro D., Struszczyk M., Kopias K., Rogaczewska A., Development of a Manufacturing Method for Surgical Meshes Modified by Chitosan, Fibres and Textiles in Eastern Europe 2007, Vol. 15, No. 3 (62), pp. 105-108.
• 6. Polish Patent Appl. P 3800861 (2006) Composite surgical meshes and method of their production (in Polish).
• 7. Polish Patent PL-281975 (1989).
• 8. Finish Patent 984989 (1989).
• 9. Polish Patent Appl. P-385031 and P-385032.