2 Archives of Metallurgy and Materials

Znaleziono wyników: 3

Liczba wyników na stronie

Wyniki wyszukiwania

Sortuj według:

Ogranicz wyniki do:

Microstructure of V3Ga superconducting wire using high Ga content Ti-Ga/V precursor composite material

100%

Murakami S. , Matsuda K. , Kawabata T. , Hishinuma Y. , Ikeno S.

tom Vol. 58, iss. 2

325--326

Our co-workers, Hishinuma et. al. have fabricated the V3Ga compound wire by a new process using a high Ga content Ti-Ga compound in order to improve the superconducting property of the wire. In this study, we investigated microstructures of this wire to clarify the existence of V3Ga phase. The different contrasts of the matrix, two V-Ga phases and Ti-Ga core were observed by SEM observation. Two V-Ga phases were also confirmed. The ratio of V to Ga for two V-Ga phases was respectively 3:1 and 6:5 according to the EDS result. And these two phases were confirmed as V3Ga and V6Ga5.

Hishinuma i współpracownicy wytworzyli drut związku międzymetalicznego V3Ga przy użyciu nowej metody wykorzystującej związek międzymetaliczny Ti-Ga o wysokiej zawartości Ga celem poprawy właściwości nadprzewodzących drutu. Zbadaliśmy mikrostrukturę drutu, aby zweryfikować obecność fazy V3Ga. W trakcie badań SEM zaobserwowano zróżnicowany kontrast w osnowie oraz istnienie dwóch faz V-Ga i rdzenia T-Ga. Analiza EDS potwierdziła istnienie dwóch faz z układu V-Ga, w których stosunek V do Ga wynosi odpowiednio 3:1 i 6:5. Potwierdzono, ze te dwie fazy to V3Ga i V6Ga5.

Tem Observation Of Precipitate Structures In Al-Zn-Mg Alloys With Additions Of Cu/Ag

100%

Watanabe K. , Matsuda K. , Ikeno S. , Yoshida T. , Murakami S.

2015

tom Vol. 60, iss. 2A

977--979

Al-Zn-Mg alloy has been known as one of the aluminum alloys with the good age-hardening ability and the high strength among commercial aluminum alloys. The mechanical property of the limited ductility, however, is required to further improvement. In this work, three alloys, which were added Cu or Ag into the Al-Zn-Mg alloy, were prepared to compare the effect of the additional elements on the aging behavior. The content of Ag and Cu were 0.2at.% and the same as, respectively. Ag or Cu added alloy showed higher maximum hardness than base alloy. The particle shape and rod shape precipitates were observed in all alloys peak-aged at 423K. According to addition of Ag or Cu, the number density of the precipitates increased higher than that of base alloy.

Al-Zn-Mg jest stopem, który można efektywnie poddawać procesowi utwardzania wydzieleniowego. Spośród różnorodnych stopów aluminium charakteryzuje się bardzo wysoką wytrzymałością mechaniczną, jednak jego ograniczona plastyczność jest cechą wymagającą poprawy. W toku prac przygotowano trzy stopy: stop bazowy Al-Zn-Mg oraz stopy zawierające dodatki Cu lub Ag, dla porównania wpływu tych dodatków na starzenie się materiału. Zawartość Ag i Cu wynosiła odpowiednio 0,2% at. Stopy z dodatkiem Ag lub Cu wykazywały większą twardość maksymalną w porównaniu ze stopem bazowym. We wszystkich stopach starzonych w temperaturze 423K obserwowano charakterystyczne wydzielenia, a ich koncentracja była odpowiednio większa dla stopów z dodatkiem Ag lub Cu.

Tem Observation Of Precipitate Structures In Al-Zn-Mg Alloys With Additions Of Cu/Ag

58%

Watanabe K. , Matsuda K. , Ikeno S. , Yoshida T. , Murakami S.

nr 2