Yttrium aluminium perovskite with the formula YAlO3 (YAP) is one of the three oxides that occur in the Al2O3-Y2O3 system; YAM and YAG are stable coexisting phases of this system. YAP single crystals are known to be used as optical materials due to their favourable properties, especially when they are doped with rare earth or transition metal ions. The preparation of a monophase yttrium aluminium perovskite is a difficult task as the solid phase synthe- sis method leads to the formation of coexisting phases. High-energy milling is the most effective way to obtain a homogeneous mixture of yttrium and aluminium oxide powders (YAP precursors). In this work, different types of homogenization were compared and then the optimal parameters (rotational speed, milling ball size, milling time) influencing the phase composition and morphology of the product after synthesis were established. The X-ray diffraction (XRD) technique was used to study the phase composition and the morphology was characterized using a scanning electron microscope. The obtained results proved that the method of energy supply to the milled system has a significant impact on the course of synthesis and the morphology of the sintered product.
PL
Perowskit itrowo-glinowy o wzorze YAlO3 (YAP) jest jednym z trzech tlenków występujących w układzie Al2O3-Y2O3; YAM i YAG to współistniejące stabilne fazy tego układu. Wiadomo, że monokryształy YAP są stosowane jako materiały optyczne ze względu na ich korzystne właściwości, zwłaszcza gdy są domieszkowane jonami pierwiastków ziem rzadkich lub metali przejściowych. Przygotowanie jednofazowego perowskitu itrowo-glinowego jest trudnym zadaniem, ponieważ metoda syntezy w fazie stałej prowadzi do powstania faz współistniejących. Najbardziej efektywnym sposobem otrzymywania homogenicznej mieszaniny proszków tlenków itru i glinu (prekursorów YAP) jest mielenie wysokoenergetyczne. W pracy porównano różne rodzaje homogenizacji, a następnie ustalono optymalne parametry (prędkość obrotowa, wielkość mielników, czas mielenia) wpływające na skład fazowy i morfologię produktu po syntezie. Do badania składu fazowego wykorzystano technikę dyfrakcji rentgenowskiej (XRD), a morfologię scharakteryzowano za pomocą skaningowego mikroskopu elektronowego. Uzyskane wyniki dowiodły, że sposób dostarczania energii do mielonego układu ma istotny wpływ na przebieg syntezy i morfologię spiekanego produktu.
EN
The subject of the research is the preparation of yttrium aluminium perovskite YAlO3 (YAP) precursor powder and its free sintering ability. In the conducted research, the influence of the application of chemical methods of precursor powder preparation on its properties, phase composition after thermal treatment and the ability to obtain dense ceramics was checked. The precursor samples were prepared by the Pechini sol-gel and co-precipitation methods and by the combustion method using fuels in the form of citric acid or tris (hydroxymethyl) aminomethane (HOCH2)3CNH2. After calcination of the precursors and thermal treatment at 1600 °C, it was shown that the highest sinter density and the highest phase purity were obtained for ceramics obtained from the powder obtained from combustion with TRIS fuel. The sinterability studies and the development of phase composition depending on the temperature indicate that the most favourable properties of YAP ceramics (99% YAP) are obtained by free sintering of the selected precursor powder at 1400 °C.
PL
Przedmiotem badań jest otrzymywanie proszku prekursora perowskitu itrowo-glinowego YAlO3 (YAP) i jego zdolność do spiekania swobodnego. W przeprowadzonych badaniach sprawdzono wpływ zastosowania chemicznych metod przygotowania proszku prekursora na jego właściwości, skład fazowy po obróbce termicznej i zdolność do uzyskania gęstej ceramiki. Próbki prekursorów przygotowano metodą zol-żel Pechiniego, współstrącania oraz metodą spalania z użyciem paliwa w postaci kwasu cytrynowego lub tris (hydroksymetylo) aminometanu (HOCH2)3CNH2. Po kalcynacji prekursorów oraz obróbce termicznej w 1600 °C wykazano, że najwyższą gęstość spieków i najwyższą czystość fazową uzyskano dla ceramiki otrzymanej z proszku pochodzącego ze spalania z udziałem paliwa TRIS. Badania podatności na spiekanie i rozwój składu fazowego w zależności od temperatury wskazują, że najkorzystniejsze własności ceramiki YAP-u (99% YAP) otrzymuje się przez spiekanie swobodne wybranego proszku prekursora w 1400 °C.