Characterization of Nanocrystalline AlTiSiN Coatings Deposited by a LARCCAE Process

100%

Gołombek K. , Tomiczek A. E. , Pakuła D. , Matus K.

Archives of Metallurgy and Materials

2018

tom Vol. 63, iss. 2

899--906

The paper presents the results of research studies involving the ceramic-metal tool materials with the deposited nitride coatings on the basis of aluminium, titanium and silicon. The cathodic arc evaporation with lateral rotating cathodes method was used for deposition of nanocrystalline, wear resistant nitride coatings – AlTiSiN type. Structural examinations are presented of the applied coatings and their support material made on the scanning electron microscope (SEM) and the scanning/transmission electron microscope (STEM). Chemical composition analysis as a function of the distance from the specimen surface, the so-called profile analysis, were carried out also. The structural analysis confirms that deposited multilayer coatings have dense microstructure without any visible porosity and delamination. It was found that the investigated coatings have nanocrystalline structure and consisting of fine crystallites even less than 6nm. Lattice deformations and numerous structural defects were also observed in the nanolayers. Depositing the AlTiSiN coatings results in the significant hardness increase within the range of 2252 ±256 to 2908 ±295 HV0.01.

Analysis of Crystallisation Process of Cast Magnesium Alloys Based on Thermal Derivative Analysis

88%

Król M. , Tański T. , Matula G. , Snopiński P. , Tomiczek A. E.

tom Vol. 60, iss. 4

2993--3000

The paper presents the results of the crystallisation process of cast magnesium alloys based on the thermal-derivation analysis. The effects of aluminium content and cooling rate on the characteristic parameters of the evaluation of magnesium dendrites during solidification at different cooling rates were investigated by thermal-derivative analysis (TDA). Dendrite coherency point (DCP) is defined with a new approach based on the second derivative cooling curve. Solidification behaviour was evaluated via one thermocouple thermal analysis method. Microstructural evaluations were characterised by light microscope, X-ray diffraction, scanning electron microscopy, and energy dispersive X-ray spectroscopy. This research revealed that utilisation of d2T/dt2 versus the time curve methodology allows for analysis of the dendrite coherency point.

W pracy przedstawiono wyniki badań opisu procesu krystalizacji odlewniczych stopów magnezu w oparciu o analizę termiczno-derywacyjną. Przedstawiono wpływ szybkości chłodzenia oraz stężenia aluminium na charakterystyczne temperatury podczas krystalizacji, jak również wyniki obliczeń udziału frakcji stałej w punkcie koherencji fazy α w oparciu o analizę krzywej d2T/dt2, bazując na pomiarze temperatury jedną termoparą. Przedstawiono i omówiono wyniki wpływu szybkości chłodzenia na charakterystyczne temperatury procesu krystalizacji odlewniczych stopów magnezu. Wpływu założonych szybkości chłodzenia na mikrostrukturę dokonano w oparciu o wyniki badań z wykorzystaniem mikroskopii świetlnej oraz mikroanalizy rentgenowskiej jakościowej i ilościowej z wykorzystaniem elektronowej mikroskopii skaningowej. Przedstawiono wyniki badań składu fazowego w oparciu o rentgenowską jakościową analizę fazową.