Preliminary studies of Pt/Rh-MgO/Al2O3 and Pt/Rh-MgO/CeO2/Al2O3 catalysts for storage and reduction of NOx in exhaust gases at rich and lean fuel mixture were performed. NOx conversion and time of reaching steady state for lean mixture was used for comparison of catalytic and sorption activity. Catalysts were prepared: first on the alumina pellets by impregnation process and second on steel honeycomb monolith with washcoat layer. The conversion of nitrogen oxides as a function of temperature and different time of lean period to rich was determined. Thanks to the results of these studies both catalysts were compared. The prepared bed reactor containing magnesia as NOxtrap oxidizes CO and HC and reduces NOx during cyclic changes of air to fuel mixtures. Oxidation and reduction properties of the reactor are strongly dependent on the cycle of mixture changes and temperature. Generally there is an average NOx conversion ratio decrease with the increase of lean period time. For monolith type of reactor Pt/Rh-MgO/CeO2/Al2O3 conversion didn not obtain acceptable results above 200oC for both SV values. The relation of the surface area to the volume of the reactor was higher for the monolith reactor than for the bed type.
Na podstawie przeprowadzonych badań określono wpływ stosunku przepływu mieszanki bogatej do przepływu mieszanki ubogiej, na zdolności katalityczne układu zawierającego związki potasu i palladu. Testy aktywności wykonano w zakresie temperatury 200-400 stop. C przy przepływie mieszanka bogata/ mieszanka uboga: 1 min/1 min; 1 min/2 min; 1 min/3 min oraz 1 min/4 min. Biorąc pod uwagę czas spalania danej mieszanki oraz odpowiadający jej współczynnik nadmiaru powietrza λ wyznaczono dodatkowy parametr Lambda średnie - λ. Na podstawie jego wartośsci można określić stopień zmniejszenia zużycia paliwa w określonych warunkach. Najwyższe stopnie konwersji tlenków azotu osiągnięto w temperaturze 200 stop. C. Nawet dla λ = 1,15 stopień konwersji nie spadał poniżej 84%.
EN
Studies of Pd/K2CO3/AL2O3 catalyst for nitrogen oxides storage and reduction at different periods of lean and rich mixtures were performed. The highest NOx conversion was obtained at 200°C. Average λ was calculated using times of lean and rich periods. Even for λ, =1,15 conversion was higher than 84%.
The preliminary studies of each component of Pd-K-Al2O3 catalyst for storage and reduction of NOx in exhaust gases at rich and lean fuel mixture were performed. The conversions of nitrogen oxides as function of air to fuel mixture composition were determined.
PL
Przedstawiono wyniki wstępnych badań wpływu poszczególnych składników katalizatora Pd-K-AhO3 na jego aktywność magazynująco-redukującą NO. z gazów spalinowych w czasie działania bogatej i ubogiej mieszanki paliwowej. Określono stopień konwersji tlenków azotu w zależności od stosunku powietrza do paliwa w mieszance.