1

The influence of prolonged ageing on the structure and properties of precipitation hardened austenitic alloy.

100%

Ducki K. , Hetmańczyk M.

Inżynieria Materiałowa

|

2001

|

tom R. XXII, nr 4

290-293

EN

In this work are presented the results of inspections of the structure and mechanical properties of Fe-Ni austenitic alloy with precipitation hardening by gamma' type intermetallic phase. Using the scanning microscopy technique, as well as X-ray microanalysis and analysis were inspected the course of precipitation of intermetallic phases and carbides during prolonged ageing at the temperature of 715 degrees centigrade. There was found a significant increase of hardness and mechanical properties of alloy at the stage of creation of coherent zones and metastable gamma' particles, and decrease of hardness at the stage of overageing and coagulation of precipitates.

PL

W pracy przedstawiono wyniki badań struktury i właściwości mechanicznych austenitycznego stopu Fe-Ni umacnianego wydzieleniowo fazą międzymetaliczną typu gamma'. Metodami mikroskopii skaningowej oraz analizy i mikroanalizy rentgenowskiej badano przebieg wydzielania faz międzymetalicznych i węglików podczas długotrwałego starzenia przy temperaturze 715 stopni Celsjusza. Stwierdzono istotny wzrost twardości i własności wytrzymałościowych stopu na etapie powstawania koherentnych stref i metastabilnych cząstek gamma' oraz spadek umocnienia w stadium przestarzenia i koagulacji wydzieleń.

2

The investigations of hot-deformability and structure of high-temperature Fe-Ni alloy

100%

Ducki K. , Kuc D.

|

2009

|

tom Vol. 35, nr 2

83-90

EN

Purpose: This study describes the influence of initial austenite grain size and parameters of hot plastic deformation on the deformability and structure of high-temperature Fe-Ni austenitic alloy of A-286 type. Design/methodology/approach: The hot deformation characteristics of the alloy were investigated by hot torsion tests using torsion plastometer. The tests were executed at constant strain rates of 0.1 and 1.0 s-1, at a testing temperature in the range from 900 to 1150 °C. The structural inspections were performed on microsections taken from plastometric samples after so called "freezing". Findings: Plastic properties of the alloy were characterized by the worked out flow curves and the temperature relationships of flow stress and the strain limit. The relationship between the peak stress (σpp) and the Zoner-Hollomon parameter (Z) were described by power function. Activation energy for hot working (Q) was assessed for the alloy after two variants of previous heating. The examinations performed, focusing on the influence of hot working parameters on the structure of austenitic alloy, revealed subsequently occurring processes of dynamic recovery, recrystallization and repolygonization. Practical implications: Characteristics of the alloy plastic properties during hot deformation depend considerably on the initial soaking temperature and hot deformation parameters. Optimum values of yield stress and strain limit were obtained for the alloy after its initial soaking at 1100 °C/2h and strain rate of 0.1 s-¹ in the temperature range of 1050-950 °C. Originality/value: An increase of the alloy deformation temperature led to a growth of the size of subgrains with a simultaneous decrease of their internal dislocation density. The influence of the strain rate of the alloy on the size of subgrains and dislocation density is complex by nature and depends on the initial size of the austenite grains and on the mechanism of the dynamic recrystallization process.

3

Influence of initial heat treatment on the fatigue life of austenitic Fe-Ni alloy

100%

Ducki K. , Cieśla M.

|

2008

|

tom Vol. 29, nr 2

89-92

EN

Purpose: The paper addresses the problem of determining the dependence between initial heat treatment of an austenitic Fe–Ni alloy and its mechanical properties and fatigue life at room temperature. Design/methodology/approach: For the investigated Fe–Ni alloy after solution heat treatment, two variants of specimen ageing were applied for comparison, i.e. typical single-stage ageing and novel two-stage ageing. Specimens that underwent heat treatment were subjected to a static tensile test and low-cycle fatigue tests (LCF), carried out at room temperature. Findings: It has been found that, the specimens of Fe–Ni alloy after two-stage ageing are distinguished by higher strength properties with a little lower plastic properties. In a case of low-cycle fatigue tests, specimens after singlestage ageing were characterized by higher fatigue life. Lower fatigue life of the alloy after two-stage ageing can be explained by increased brittleness of material in boundary areas. Practical implications: The fatigue life results obtained in LCF conditions can be used in predicting the duration of operation of products made out of Fe–Ni alloy at room temperature. Originality/value: The significance of the applied ageing variants’ effect on the mechanical properties and fatigue life of the tested austenitic Fe–Ni alloy is shown in the paper.

4

Analiza profilu linii dyfrakcyjnych litych próbek stopu Fe-13,7Cr-24,3Ni-1,9Ti-1,3Mo

100%

Pająk L. , Ducki K.

Archiwum Nauki o Materiałach

|

2002

|

tom T. 23, nr 1

51-66

PL

W pracy dokonano analizy profilu linii dyfrakcyjnych, wykorzystując procedurę Toranyi dla litych próbek polikrystalicznego austenitycznego stopu Fe-13,7Cr-24,3Ni-1,9Ti-1,3Mo po obróbce cieplnej. Procedura Toranyi umożliwia doapsowanie profili zarówno pojedynczych linii dyfrakcyjnych, jak i całego rentgenogramu polikrystalicznego. W odróżnieniu od rezultatów uzyskanych przez Torayę dla modelowego materiału proszkowego alfa-SiO2, w niniejszej pracy stwierdzono złożoną zależność wartości poszczególnych parametrów opisujących profile linii dyfrakcyjnych od kąta dyfrakcji 2 teta dla badanych próbek. Jest to związane ze specyfiką badanego materiału, jakim jest stop austenityczny. Porównano wartości stałych sieciowych wyznaczonych za pomocą funkcji ekstrapolacyjnej cos kwadrat teta na podstawie położeń linii dyfrakcyjnych uzyskanych w wyniku dopasowania profili pojedynczych linii dyfrakcyjnych z wartościami otrzymanymi w wyniku dopasowania profili linii dyfrakcyjnych całego rentgenogramu Rietvelda. Stwierdzono dobrą zgodność wartości stałych sieciowych z użyciem funkcji ekstrapolacyjnej i metodą Rietvelda.

EN

Profiles of diffraction lines using Toraya procedure for heat-treated, solid samples of polycrystalline, austhenitic Fe-13.7Cr-24.3Ni-1.9Ti-1.3Mo alloy were analysed. Toraya procedure enables the fitting of both individual diffraction lines and the whole powder pattern. Contrary to the results obtained by Toraya for alpha-SiO2 powder material a complex dependence of the values of particular profile parameters of diffraction lines on the diffraction angle 2 theta was found. This is connected with the specific nature of the solid, austhenitic alloy. The values of lattice constants estimated with the use of the 2 theta extrapolation function basing on the diffraction line on the positions determined by individual diffraction line fitting were compared with the ones determined by the whole powder pattern fitting procedure and by the Rietveld method. Good agreement between the values of lattice constants determined using the extrapolation function and the Rietveld method was found.

5

Własności i mikrostruktury stopu CuNi2Si1

80%

Rdzawski Z. , Ducki K. , Jabłońska M. , Śmiglewicz A.

|

2010

|

tom R. 55, nr 2

78-83

PL

Stosowane dotychczas elementy osprzętu w urządzeniach elektrycznych są wytwarzane z zimnowalcowanych taśm z brązów cynowych i mosiądzów. Materiały te charakteryzują się wysoką wytrzymałością i dobrą skrawalnością, jednakże obniżoną konduktywnością elektryczną. Jedną z perspektywicznych grup materiałów przeznaczonych do tego typu zastosowań stanowią umacniane wydzieleniowo stopy CuNiSi. W pracy przedstawiono wyniki badań własności mechanicznych, konduktywności elektrycznej, struktury oraz termicznej analizy różnicowej (DTA) stopu CuNi2Si1 po wybranych wariantach procesu technologicznego. Badania prowadzono na próbkach pobranych z taśm stopu CuNi2Si1 w stanie po walcowaniu na gorąco, po przesycaniu w warunkach 950 stopni Celsjusza/1h/woda oraz po starzeniu przy temperaturze 450-600 stopni Celsjusza w czasie od 1 do 420 min. Uzyskane wyniki wykazały, że optymalną kombinację twardości (HV = 150) i konduktywności elektrycznej (gama = 22 MS/m) uzyskano dla taśmy ze stopu CuNi2Si1 po przesycaniu i starzeniu przy temperaturze 550 stopni Celsjusza w czasie 120 min. W substrukturze stopu ujawniono w trakcie starzenia intensywny proces wydzieleniowy koherentnych, manometrycznych cząstek fazy Ni2Si, który przebiegał homogenicznie w osnowie w zakresie temperatury 267-381 stopni Celsjusza.

EN

Modern electrical equipment is made from cold rolled tin bronze and brass strips. These materials have high mechanical strength and good machinability but decreased electrical conductivity. One of perspective group of materials destined to such applications are precipitation hardened CuNiSi alloys. In the present work the results of research of mechanical properties, electrical conductivity, structure and differential thermal analysis (DTA) have been presented. The investigations have been conducted on CuNi2Si1 alloy strips after hot rolling and after solution treatment at 950 degrees of Celsius/1h/water and ageing at temperature 450-600 degrees of Celsius with holding time from 1 to 420 min. The results indicated, that optimum combination of hardness (HV = 150) and electrical conductivity (gamma = 22 MS/m) have been obtained for CuNi2Si1 alloy strips after solution treatment and ageing at 550 degrees of Celsius temperature in time 120 min. An intensive precipitation process of nanometric, coherent particles of Ni2Si phase have been revealed during ageing. This process proceeded homogeneously in the matrix at temperature range 267-381 degrees of Celsius.

6

The Microstructure and Mechanical Properties of Cylindrical Elements from Steel 38Mn6 after Continuous Induction Heating

70%

Smalcerz A. , Barglik J. , Kuc D. , Ducki K. , Wasiński S.

Archives of Metallurgy and Materials

|

2016

|

tom Vol. 61, iss. 4

1969--1974

EN

The paper deals with the influence of induction surface hardening on the microstructure and mechanical properties of cylindrical elements made of steel 38Mn6. The first stage was based on computer simulation of the induction hardening process. The second stage - experiments were provided on laboratory stand for induction surface hardening located at the Silesian University of Technology. Microstructure tests were conducted on light and scanning microscopes. The hardness penetration pattern and thickness of hardened layer were marked. It was found that due to properly chosen parameters of the process, the appropriate properties and thickness of hardened layer were achieved.

7

Podstawowe charakterystyki stali narzedziowych z podwyższoną zawartością azotu

51%

Wiedermann J. , Zalecki W. , Malec M. , Grosman F. , Hetmańczyk M. , Okrajni J. , Hadasik E. , Ducki K. , Pogoda K. , Smyczek H.

|

tom T. 51, z. 1

22-40

PL

Przedstawiono wyniki badań oddziaływania podwyższonej zawartości azotu na podstawowe charakterystyki stali NC11LV, WCLV i SW7M. Badania obejmowały: analizę wpływu azotu na punkty krytyczne i przemianę austenitu podczas chłodzenia ciągłego (wykonano wykresy CTPc stali NC11LV i WCLV), jak też wpływu azotu i temperatury austenityzowania na wielkość ziarna byłego austenitu oraz twardość po hartowaniu. Wykonano pomiary wybranych parametrów stereologicznych wydzieleń po różnych etapach obróbki cieplnej (stan zmiękczony, hartowany, ulepszony cieplnie), analizę wpływu azotu na twardość, ścieralność, odporność na pękanie i zmęczenie niskocykliczne w stanie ulepszonym cieplnie. Stwierdzono korzystny wpływ celowych dodatków azotu na strukturę, twardość i właściwości użytkowe (odporność na ścieranie i kruche pękanie, trwałość pod obciążeniem niskocyklicznym i trwałość w warunkach zmęczenia przy temperaturze 550 stopni Celsjusza) badanych stali.

EN

Effects of alloying with nitrogen were examined in NC11LV, WCLV and SW7M tool steels (cold work, hot work and high speed, respectively). The experiments included examination of: effects of nitrogen on the critical points and continuous cooling transformations of austenite (TTTC diagrams were determined for NC11LV and WCLV grade steels) and also the effects of nitrogen and austenitising temperature on former austenite grain size and hardness after heat treatment. Selected stereological parameters were determined for phases precipitated after various heat treatments (soft annealing, quenching, tempering). Alloying with nitrogen improves structure, hardness, wear resistance, toughness, low-cycle fatigue life and high-temperature (550 degrees centigrade) fatigue strenght of the materials.