Some specifics in deformation and fracture behaviour of austempered ductile cast iron

100%

Kohout J. , Vechet S. , Dorazil E.

Zeszyty Naukowe. Mechanika / Akademia Techniczno-Rolnicza w Bydgoszczy

1998

tom Z. 43 (216)

235-242

With respect to ist low cost the austempered ductile cast iron (ADI) has excellent mechanical and technological properties. Its matrix is created with the mixture of very stiff bainitic and very pliable retained austenite whose content is dependent on the transformation conditions (temperature and time) nad ist certain part can transform under loading. It causes some specifics in ADI behaviour worrying the designers and therefore ADI is used much less than it could be used. The aim of contibution is to explain the substance of these specyfics and to demonstrate that they mostly can increase the utility properties of final products.

Żeliwo sferoidalne hartowane z przemianą izotermiczną (ADI) cechuje się niskimi cechami wytwarzania i bardzo dobrymi własnościami mechnicznymi i technologicznymi.Struktura żeliwa składa się z ferrytu bainitycznego i austenitu szczątkowego, którego udział zależy od temperatury i czasu przemiany izotermicznej. Austenit ten pod wpływem zgniotu może ulec przemianie. Zjawisko to jest zaliczane do szczególnych zachowań żeliwa ADI, będących przyczyną braku zaufania konstruktorów i dlatego jest rzadziej stosowane, niż powinno to wynikać z jego dobrych własności i niskich kosztów wytwarzania. Celem artykułu jest wyjaśnienie tego zjawiska i pokazanie, że w większości przypadków, zjawisko to można wykorzystać dla podwyższenia własności użytkowych wytworu.

ADI - a prospective structural material

100%

Dorazil E. , Věchet S. , Kohout J. , Klakurková L.

Zeszyty Naukowe. Mechanika / Politechnika Opolska

1999

tom z. 59

103-106

Austempered ductile iron (ADI) presents relatively new high strength structural material with very good mechanical and technological properties along with relatively low price (see Fig. 1). This type of nodular cast iron is produced in wide measure not only in large and developed countries (U.S.A. - full half of world-wide production, Japan, China, Germany, Great Britain, France, Italy, Sweden etc.) but also in countries comparable with our country (Finland, Netherlands, Belgium etc.). Word-wide production per year exceeded 60,000 tons in 1995 [1], in 2005 already the production of 230,000 tons is expected (Fig. 2).

Influence of matrix structure on fatigue properties of nodular cast iron

100%

Vechet S. , Dorazil E. , Kohout J.

Zeszyty Naukowe. Mechanika / Akademia Techniczno-Rolnicza w Bydgoszczy

1998

tom Z. 43 (216)

242-250

Sixteen heats of unalloyed and alloyed nodular cast iron were thermally treated in different ways and 34 materials were obtained with ferritic, ferritic-pearlitic and pearlitic structures and with structures of upper, transition and lower bainite. For all those materials static and fatigue tests were made - the latter mostly in symmertical tension-compression loading but some of them also in repeated tension and pulsating bending. From results of fatigue tests the fatigue limits for 10'7 cycles were determined and some Haigh diagrams were drawn. Special care was given to the study of the dependence between tensile strength and fatigue limit.

Z szesnastu wytopów niestopowego i stopowego żeliwa sferoidalnego, przy pomocy różnych rodzajów obróbki cieplnej uzyskano 34 gatunki żeliwa ze strukturą: ferrytyczną, ferrytyczno-perlityczną i perlityczną oraz ze strukturą górnego, przejściowego i dolnego banitu. Dla wszystkich otryzemanych gatunków zostały wykonane badania statyczne i zmęczeniowe. Większość badań zmęczeniowych przeprowadzono przy symetrycznym obciążeniu rozciągającym i ściskającym, a także niektóre z nich przy rozciąganiu tętniącym i zginaniu pulsującym. Wyniki badań zmęczeniowych przedstwiono na wykresach Haigha. W analizie wyników badań szczególną uwagę zwrócono na zalaeżność między wytrzymałością na rozciąganie a granicą zmęczeniową żeliwa sferoidalnego.