Wyniki wyszukiwania - Biblioteka Nauki

1

Pochodne imidazolu jako przyspieszacze procesu sieciowania kompozycji izocyjanianowo-epoksydowych

100%

Pilawka R.

|

tom T. 90, nr 9

1771-1773

2

Teraherz frequencies electromagnetic waves - a new tool for investigating composite defects

63%

Gorący K. , Pilawka R.

|

tom R. 11, nr 1

75-79

EN

In this paper the possibility of using a modern NDT technique - THz electromagnetic waves for composite materials defects detection and identification was investigated. Two technological defects were investigated - voids and internal delaminating. The composite materials were hand lay up made. Several kinds of reinforcing fibers (glass, basalt, jute) and polyester resin were used. Glass micro spheres and mica plates were placed at different depths in order to simulate technological defects. The specimens were tested using terahertz frequencies electromagnetic waves. The goal was to verify if the NDT method is appropriate to identify technological defects, misuse damage as well as determine parameters such as depth or size.

PL

Celem pracy było sprawdzenie możliwości wykorzystania nowoczesnej techniki badań nieniszczących, jaką jest zastosowanie promieniowania elektromagnetycznego w zakresie terahercowym do wykrywania i oceny defektów struktur materiałow kompozytowych polimerowo-włoknistych. Badania przeprowadzono dla wybranych wad technologicznych - pęcherzy powietrza. Badania przeprowadzone zostały dla kompozytow wykonanych metodą laminowania ręcznego. Wytworzono laminaty poliestrowe z różnymi rodzajami wzmocnienia (włókna szklane, bazaltowe, jutowe). W laminatach umieszczono na rożnych głębokościach mikrosfery szklane, płytki miki i inne materiały, aby zasymulować obecności wad. Próbki poddano badaniom metodą terahercową w celu zbadania jej skuteczności w wykrywaniu wad technologicznych oraz eksploatacyjnych oraz określaniu takich ich parametrow, jak położenie oraz wielkość.

3

Wpływ wprowadzenia eterów allilowych na odporność termiczną materiałów epoksydowo-eterowych

63%

Pilawka R. , Urbala M.

|

tom [R.] 18, nr 6

619-621

PL

Badano kompozyty epoksydowo-eterowe, których głównymi składnikami były: żywica epoksydowa Epidian 6 (produkt Zakładów Chemicznych Organika-Sarzyna w Nowej Sarzynie) i zsyntetyzowane etery diallilowe: butan-1,4-diolu (DIBAN) oraz buten-1,4-diolu (DIBEN) użyte jako rozcieńczalniki i modyfikatory. Żywicę epoksydową utwardzano za pomocą 1-butyloimidazolu (1BI, Aldrich), stosowanego w ilości 1 cz.wag. na 100 cz.wag. żywicy; natomiast jako środka sieciującego etery użyto nadtlenku benzoilu (DBPO, Aldrich) w ilości 1 cz.wag na 100 cz.wag. żywicy. Etery stosowano w zakresie wagowym od 1 do 10% wag. w stosunku do żywicy. Kompozycje epoksydowe były utwardzane termicznie w temp. 120°C przez 2 godziny. Temperatura zeszklenia kompozytów została oszacowana przy użyciu aparatu Q-800 (TA Instruments). Wytrzymałość termiczną określono przy użyciu termowagi TGA Q-5000 (TA Instruments). Wprowadzenie eterów allilowych nieznacznie zmniejsza wytrzymałość termiczną materiałów epoksydowo-eterowych przy zawartości do 2,5 %wag.

EN

The epoxy compositions containing epoxy resin Epidian 6 (product of Chemical Works "Organika Sarzyna" in Nowa Sarzyna) and the synthesized diallyl ether of butane-1,4-diol (DIBAN) or diallyl ether of but-2-ene-1,4-diol (DIBEN) as diluents and modifiers have been investigated. The epoxy resin were hardened by 1-butylimidazole (1BI, Aldrich) in amount 1 phr for epoxy resin. For the materials with diallyl ethers, dibenzoyl peroxide (DBPO, Aldrich) in amount 1 phr for ether was used. Content of ethers in the epoxy compositions was changed in the wide range of 1 to 10 wt%. The epoxy composites were hardened thermally at temperature of 120°C during 2 hour. The glass transition values of epoxy materials were characterized by DMA Q-800 (TA Instruments). The thermal strengths of composites were measured with TGA Q-5000. The introducing of allyl ethers insignificantly degreases the thermal strength of epoxy-ethers composites with ether content to 2.5 wt%.

4

Wpływ rodzaju kationu metalu i pochodnych imidazolowych na czas życia kompozycji epoksydowych oraz wytrzymałość połączeń klejowych na ścinanie

63%

Pilawka R. , Mąka H.

|

tom T. 91, nr 1

100-105

PL

Przedstawiono wyniki prac związanych z możliwością zastosowania kompleksów kationów metali i pochodnych imidazolu jako środków sieciujących o charakterze utajonym, służących do utwardzania żywic epoksydowych. Otrzymano utwardzacze utajone na bazie kompleksów imidazolu i kationów metali przy stosunku molowym 4:1. Badano czas życia kompozycji, proces sieciowania metodą mikrokalorymetrii skaningowej DSC, spektrofotometrii w podczerwieni FTIR oraz reometrii przy użyciu aparatu ARES. Dodatkowo wyznaczono wytrzymałość na ścinanie łączeń klejowych uzyskanych po wymieszaniu składników oraz po 1 i 3 miesiącach przechowywania samej kompozycji klejowej. Użycie badanych kompleksów jako środków sieciujących spowodowało wydłużenie czasu życia kompozycji do 2 tygodni w przypadku kompleksów 1-butyloimidazolu oraz do trzech miesięcy w przypadku zastosowania kompleksów 2-etyloimidazolu.

EN

Six latent curing agents were prepd. by complexing Cu(II), Ni(II) and Co(II) ions with imidazole (I) derivatives (1:4 mole ratio) in aq. soln. for 30 min. Pot life times were measured by viscosity changes (ARES rheometer) and FTIR spectra during storage. The agents were then used for curing a com. epoxy resin in adhesive joints (Al plates) at 140°C for 4 h. The joints were studied for shear strength during storage. Use of the complexes resulted in extension of the pot life time of the epoxy compn. up to 1 month for 1-Bu-I complexes or up to 3 months for 2-Et-I complexes.

5

Wpływ kompatybilizatora i warunków przetwórczych na właściwości mieszanin PC/PP

51%

Janik J. , Krala G. , Pilawka R. , Gorący K.

|

tom [R.] 18, nr 6

578-581

PL

Przedstawiony materiał dotyczy mieszanin poliwęglanu z polipropylenem PC/PP, w aspekcie zagospodarowania odpadów z tych tworzyw. Wytworzono mieszaniny PC/PP bez udziału jak i z udziałem kompatybilizatora o 10, 20 i 30% wag. udziale PC (podobnie jak w przypadku płyty CD i DVD z poliwęglanu w pudełku z polipropylenu). Określono wpływ dodatku 5% wag. kompatybilizatora PP-g-MA (Polybond X5104) oraz zamiany układu segmentów ślimaków w procesie wytłaczania na właściwości mechaniczne tych mieszanin (wytrzymałość na rozciąganie σm i zginanie σfm, moduł sprężystości przy rozciąganiu Et, i zginaniu Ef oraz wydłużenie przy zerwaniu εB). Dodatek PP-g-MA do PC/PP poprawia wszystkie badane właściwości tych układów, zmiana układu uplastyczniającego natomiast nie wpłynęła znacząco na ich różnicę.

EN

Presented work is about blends polycarbonate/polypropylene (PC/PP). The aspect of this research is the recycling of PC (from CD) and PP (from CD boxes) wastes without segregation necessity. We have studied the relationship between mechanical properties and contents of PC/PP blends. The content of those polymer blends was 10, 20 and 30 wt % PC in a PP without and with 5 wt % of compatybilizer PP-g-MA (Polybond X5104). This Polybond is effective compatibilizer for PC/PP blends; it improved all of mechanical properties of PC/PP blends: tensile strength σm and flexural strength σfm, elasticity modulus Et and flexural modulus Ef, elongation at break εB. We have tested effect of processing condition on properties of PC/PP and results showed that change of mixing system does not influence on them.

6

Badanie procesu sieciowania jednoskładnikowych żywic epoksydowych ASSET®

51%

Pilawka R. , Mąka H. , Czulak A.

|

tom [R.] 20, nr 6 (162)

517--521

PL

Przedstawiono wyniki badań procesu sieciowania dwóch komercyjnych jednoskładnikowych żywic epoksydowych oferowanych przez firmę „New Era Materials" o różnej reaktywności. Zmiany zachodzące podczas tego procesu obserwowano śledząc zmiany ciepła właściwego za pomocą różnicowej kalorymetrii skaningowej (DSC) oraz lepkości (reometr naprężeniowy ARES) co pozwoliło określić parametry kinetyczne i dopasować modele kinetyczne autokatalitycznego procesu sieciowania zgodnie z równaniami Sesták-Berggrena i Kamala. Dane uzyskane metodą DSC jak i z krzywych reologicznych umożliwiają wyznaczenie parametrów charakterystycznych oraz kinetycznych procesu sieciowania: stałych szybkości reakcji oraz globalnych rzędów reakcji. Ponadto pozwalają na optymalizację procesu sieciowania poprzez dobór temperatury tego procesu, odpowiednio: dla ASSET®01 temperatury 120°C oraz ASSET®02 170°C.

EN

The results of curing process of two commercial one-component epoxy resin exhibiting various reactivity (product by "New Era Materials", Poland), has been presented. Using differential scanning calorimetry and stress rheometry ARES (viscosity changes) allowed to determine kinetic parameters of curing process, such as: rate constant and global reaction orders. Subsequently, kinetic models of autocatalytic curing process were fitted (Sesták-Berggren and Kamal). Moreover, optimal temperature values crosslinking process, i.e. 120°C and 170°C for ASSET®01 and ASSET®02, respectively has been determined.

7

Wpływ dodatku mielonej kory sosnowej na wytrzymałość termiczną skrobi termoplastycznej

51%

Oniszczuk T. , Pilawka R. , Oniszczuk A.

|

2013

|

tom T. 92, nr 8

1554-1558

8

Synthesis and characterization of new poly(ethylene terephthalate)/poly(phenylene oxide) blends

32%

Paszkiewicz S. , Irska I. , Piesowicz E. , Pilawka R. , Pawelec I. , Szymczyk A. , Gorący K. , Wielgosz Z. , Rosłaniec Z.

|

tom T. 62, nr 2

93--100

EN

Several compositions of poly(ethylene terephthalate) (PET) and poly(phenylene oxide) (PPO) were prepared by two different methods: in situ polymerization (IS-P) and direct mixing in the melt (DM). The existence of phase separation in the obtained PET/PPO systems has been confirmed by calculating the solubility parameter of compounds using Hoy's method. The combination of results obtained with DSC and DMTA points toward a complex morphology of PET/PPO systems.

PL

Z zastosowaniem polimeryzacji in situ (IS-P) i mieszania w stanie stopionym (DM) wytworzono dwie serie mieszanin na bazie poli(tereftalanu etylenu) (PET) oraz poli(tlenku fenylenu) (PPO). Na podstawie obliczonych metodą Hoya współczynników rozpuszczalności poszczególnych składników potwierdzono występowanie separacji fazowej w otrzymanych układach PET/PPO. Technikami różnicowej kalorymetrii skaningowej (DSC) i dynamicznej analizy mechaniczno-termicznej (DMTA) potwierdzono złożoność struktury fazowej uzyskanych układów PET/PPO.