Effects of the Microstructure and Strengthening Mechanisms of Mo2C Powders Being Added to Ti-8Nb-4Co Alloy Via the Vacuum Sintering Process

100%

Chang S.-H. , Liao K. J. , Huang K.-T. , Liang C.

Archives of Metallurgy and Materials

2023

tom Vol. 68, iss. 4

1255--1265

This study utilizes Ti-8Nb-4Co alloys added to different proportions of Mo2C powders (1, 3, and 5 mass%) by the vacuum sintering process of powder metallurgy and simultaneously vacuum sinters the alloys at 1240, 1270, 1300, and 1330°C for 1 h, respectively. The experimental results indicate that when 3 mass% Mo2C powders were added to the Ti-8Nb-4Co alloys, the specimens possessed the optimal mechanical properties after sintering at 1300°C for 1 h. The relative density was 98.02%, and the hardness and TRS were enhanced to 69.6 HRA and 1816.7 MPa, respectively. In addition, the microstructure of vacuum sintered Ti-8Nb-4Co-3Mo2C alloys has both α and β-phase structures, as well as TiC precipitates. EBSD results confirm that the Mo2C in situ produced TiC during the sintering process and was uniformly dispersed in the grain boundary. Moreover, the reduced molybdenum atom acted as a β-phase stabilizing element and solid-solution in the titanium matrix.

Investigation of the Microstructure and Strengthening Mechanisms of Ti-6Cu-8Nb-xCr3C2 Alloy through Vacuum Sintering Process

100%

Chang S.-H. , Weng C.-Y. , Huang K.-T. , Liang C.

Archives of Metallurgy and Materials

2022

tom Vol. 67, iss. 3

815--825

This study mixes four different powders to produce Ti-6Cu-8Nb-xCr3C2 (x = 1, 3, and 5 mass%) alloys in three different proportions. The experimental results reveal that when 5 mass% Cr3C2 was added to the Ti-6Cu-8Nb alloys, the specimen possessed optimal mechanical properties after sintering at 1275°C for 1 h. The relative density reached 98.23%, hardness was enhanced to 67.8 HRA, and the transverse rupture strength (TRS) increased to 1821.2 MPa, respectively. The EBSD results show that the added Cr3C2 in situ decomposed into TiC and NbC during the sintering process, and the generated intermetallic compounds (Ti2Cu) were evenly dispersed in the Ti matrix. Furthermore, the reduced Cr atom acts as a β-phase stabilizing element and solid-solution in the Ti matrix. Consequently, the main strengthening mechanisms of the Ti-6Cu-8Nb-xCr3C2 alloys include dispersion strengthening, solid-solution strengthening, and precipitation hardening.