Dispersion strenghened low-alloy steel

100%

Bolanowski K.

|

2008

|

tom Vol. 53, iss. 1

113-16

EN

Low-carbon steel with small additions of vanadium and niobium is dispersion strengthenable. After the treatment, yield strength in such steel plates up to 12 mm in thickness can reach 600 MPa, simultaneously retaining impact strength of approx. 100 J/cm2 . After controlled rolling, the steel structure is composed of ferrite and small amounts of pearlite, whereas the grain size in plates up to 12 mm in thickness does not exceed approx. 40 µm. Following normalisation at approx. 950°C, the size of grains decreases and they do not exceed approx. 20 µm. The technological process of thick plate manufacturing was described in details in technical specifications for steel plates production and also in [5]. On the basis of the data available in the literature [2], rheological investigations into plate material were carried out. The results were used to determine the temperature range in which creep maintains logarithmic character. The results also proved helpful in establishing the dependence (equation) to forecast the material behaviour at elevated temperatures.

PL

Stal niskowęglowa z niewielkimi dodatkami wanadu i niobu jest materialem podatnym na umocnienie wydzieleniowe, po którym granica plastyczności osiąga w blachach o grubości do 12 mm min. 600 MPa, zachowując jednocześnie wysoką udarność rzędu 100 J/cm2 . Po kontrolowanym walcowaniu struktura stali złożona jest z ferrytu i niewielkiej ilości perlitu, a wielkość ziarna w blachach o grubości nie przekraczającej 12 mm nie przewyisza ok. 40 µm. Po normalizowaniu z temperatury ok. 950°C wielkości ziarna maleje i nie przekracza ok. 20 µm. Proces technologiczny wytwarzania blach grubych zostal szczegółowo opisany w warunkach technicznych wytwarzania stali w postaci blach, a także w poz. Lit. 5. Opierając się na danych literaturowych [2] podjęto na materiale blach badania reologiczne, których wyniki posłużyły do określenia zakresu temperatur, w którym pełzanie zachowuje charakter logarytmiczny. Uzyskane wyniki byly także pomocne w opracowaniu zależnośi (równania), pozwalącej na prognozowanie zachowania się materiału w podwyższonych temperaturach.

2

Analysis of the structure and precipitation strengthening in a creep resisting Fe-Ni alloy

84%

Ducki K. J.

|

2007

|

tom Vol. 21, nr 2

25-28

EN

Purpose: This study describes relationships between the kinetics of precipitation and growth of the intermetallic phase gamma' [Ni3(Al, Ti)] and the strengthening magnitude obtained in a high-temperature Fe-Ni alloy of the A-286 type. In order to accomplish the goal of the study, the author used the LSW coagulation theory and Brown and Ham's conventional analysis of strengthening by ordered particles. Design/methodology/approach: The samples were subjected to a solution heat treatment at 980 degrees centigrade/2h/water and then aged at 715, 750, and 780 degrees centigrade, with holding times 0.5-500h. The heat-treated samples were subjected to structural analyses (TEM, X-ray diffraction) and analyses of mechanical properties (hardness test, static tensile test, and impact test). Findings: Based on direct measurements on the TEM pictures converted into binary images, the basic parameters of the gamma' phase, i.e. average diameter, volume fraction, and the average distance between particles, were determined. Linear regressions between the average particle diameter of the gamma' phase and the aging time (t to the 1/3) were conducted for the analyzed aging temperatures on the basis of the LSW theory. The author carried out analyses of strengthening and flow stress (Delta tau) increases as a function of the particle size of the gamma' phase and determined the value of the antiphase boundary energy (gamma APB) for analyzed Fe-Ni alloy. Practical implications: The obtained relationships of the growth of the gamma' phase particles as a function of temperature and aging time can be used to determine the magnitude of strengthening and flow stress in high-temperature Fe-Ni alloys during extended aging or usage. Originality/value: This study exploits LSW coagulation theory and Brown and Ham's conventional analysis to describe precipitation strengthening by ordered particles of the intermetallic phase gamma' in a high temperature Fe-Ni alloy.

3

Influence of precipitation strengthening process on the mechanical properties of 6082 wrought aluminium alloy

84%

Mrówka-Nowotnik G. , Sieniawski J. , Nowotnik A.

|

2006

|

tom Vol. 51, iss. 1

33-36

EN

Aluminium alloys containing Mg and Si as the major solutes are strengthened by precipitation of the metastable precursors of the equilibrium Β(Mg2Si) phase in one or more sequences. There are several particles that can form during aging: GP zones and intermediate metastable phases -Β”, Β’ and stable Β phase [1-10]. Although the precipitation process in Al-Mg-Si alloys has been extensively studied, the understanding of the hardening process is still incomplete, since any change in composition, processing and aging practices could affect the precipitation hardening behaviour [3-6, 10]. In this paper differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and hardness measurements have been utilized to study the effect of the precipitation hardening on the mechanical properties in aluminium alloy 6082. The mechanical (Rm and Rp0.2) and plastic (A) properties of the alloy were evaluated by uniaxial tensile tests at room temperature. The results show that the microstructure and mechanical properties change during artificial aging due to the precipitation strengthening process. Therefore, the parameters (time and aging temperature) of precipitation strengthening process that may lead to the most favourable mechanical properties of 6082 alloy were determined.

PL

Umacnianie stopów AlMgSi następuje wskutek wydzielania się metastabilnych faz przejściowych prowadzących do utworzenia się stabilnej równowagowej fazy Β(Mg2Si). Wydzielanie metastabilnych faz przejściowych jest dość złożone i nie do końca poznane. Najczęściej spotykany w literaturze schemat procesu rozpadu przesyconego roztworu stałego w umacnianych wydzieleniowo stopach AlMgSi ma postac: Α→ GP→ Β”→ Β’→ (Mg2Si) ( Α– przesycony roztwór stały, GP – strefy Guinier’a-Prestona, Β” i Β’ – metastabilne fazy przejsciowe, Β – faza stabilna, równowagowa). Mimo, że procesy wydzielania w stopach AlMgSi były przedmiotem wielu badań, temat ten jest wciąż aktualny. Zmiana np.: składu chemicznego stopów, czy warunków procesu starzenia, wpływa na procesy umocnienia. W artykule zastosowano badania kalorymetryczne, mikroskopię elektronową oraz badania twardości w celu zbadania wpływu czasu i temperatury starzenia na mikrostrukture oraz właściwości mechaniczne stopu aluminium 6082.

4

Single crystals deformed along the basal slip system

84%

Mikułowski B. , Boczkal G.

|

2009

|

tom Vol. 54, iss. 1

197-203

EN

Zn-Ti single crystals of three different chemical compositions grown by the Brigman method were investigated. The microstructure of the materials was determined by scanning electron microscopy. The chemical composition of the matrix and of the second phase was also investigated. The second phase was identified as an intermetallic phase Zn16Ti exhibiting a strongly anisotropic distribution in the matrix. Transmission electron microscopy and electron back scattering diffraction showed that the [1120] direction in the matrix is parallel to the [100] direction in Zn16Ti phase. Sample orientation allowed on the deformation to ϒ=0.2 only in one slip system (0001)<112>. Mechanical properties (critical resolved shear stress and hardening coefficient in the range where easy slip operates) were obtained on the basis of compression test. Investigations were made in the temperature range of 77 K to 513 K and at two strain rates of 10-3 s-1 and 10-4 s-1.

PL

Badano monokryształy Zn-Ti o trzech składach chemicznych, wyhodowane metodą Brigmana. Mikrostruktura materiałów była obserwowana przy użyciu skaningowego mikroskopu elektronowego (SEM). Badano także skład chemiczny osnowy oraz określono wydzielenia drugiej fazy. Faza ta została zidentyfikowana jako faza międzymetaliczna Zn16Ti, która wykazuje stałą zależność krystalograficzną względem osnowy. Badania wykonane na transmisyjnym mikroskopie elektronowym (TEM) oraz przy użyciu techniki EBSD pokazały, że kierunek [1120] w osnowie jest równoległy do kierunku [100] w fazie Zn16Ti. Orientacja badanych próbek pozwalała na zadanie deformacji postaciowej do wielkości ϒ=0.2 przy aktywności tylko jednego systemu poslizgu (0001)<120>. Własności mechaniczne (krytyczne naprężenie ścinające KNS oraz współczynnik umocnienia w zakresie działania łatwego systemu poślizgu ΘA) wyznaczano na podstawie próby ściskania. Badania prowadzono przy temperaturach w zakresie od 77K do 513K, przy dwóch prędkościach odkształcenia; 10-3 s-1 oraz 10-4 s-1.

5

Structure and properties of precipitation strengthened silver alloys

67%

Gryziecki J. , Sobota J.

|

2007

|

tom Vol. 52, iss. 4

665-671

EN

The paper presents the results of investigations of designed and manufactured silver alloys with additions, enabling by way of precipitation strengthening to obtain high strength properties and such additions which have high negative oxidation energy. In the manufactured alloys a high strengthening effect has been obtained as a result of the precipitation of Al4Cu9 phase during the decomposition of supersaturated solid solutions. On the other hand, the alloy additions with high negative oxidation energy formed a self-restoring oxide layer, protecting effectively against atmospheric corrosion. The composition of the obtained properties of the examined alloys guarantees good functional properties of the products made from these alloys as well as high aesthetic assets.

PL

Praca przedstawia wyniki badań nad zaprojektowanymi i wytworzonymi stopami srebra z dodatkami umożliwiającymi drogę umocnienia wydzieleniowego uzyskać wysokie właściwości wytrzymałościowe oraz takimi, które mają dużą ujemną energię utleniania. Osiągnięto w wytworzonych stopach silny efekt umocnieniowy w wyniku wydzielania się fazy Al4Cu9 podczas rozpadu przesyconych roztworów stałych. Natomiast dodatki stopowe o dużej ujemnej energii utleniania utworzyły warstwę tlenkową, samoodnawialną, chroniącą skutecznie przed korozją atmosferyczną. Zespół uzyskanych właściwości badanych stopów zapewnia wytworzonym z nich wyrobom dobre właściwości użytkowe oraz wysokie walory estetyczne.