Rheological characterization of water-based drilling muds

100%

Kherfellah N. , Bekkour K. , Benhadid S.

|

1999

|

tom Vol. 4, no spec.

339-344

EN

The thixotropic properties of the bentonite dispersions were analysed by the use of an approach derived from a Moore-Cheng model in which a single structure parameter 'lambda' varies within the range 0=<'lambda'<1. 'lambda'=0 corresponds to the complete break-down of structure at high shear rates, and 'lambda'=1 to the equilibrium gel structure at rest. In our method the Casson model (which was found to fit adequately the flow curves) was modified to incorporate the effect of changes in the structure parameter 'lambda'. This model was able to describe adequately the time-dependent behaviour of clay dispersions. Creep flow tests give indications about the elastic properties of the material. It was found that the viscoelastic behaviour of the bentonite dispersions could be represented by the generalised Kelvin-Voigt mechanical.

2

Wpływ zawartości zagęszczacza na zjawisko tiksotropii smarów plastycznych

84%

Paszkowski M.

|

2007

|

tom nr 3-4

85-96

PL

Praca dotyczy wpływu udziału procentowego zagęszczacza na zjawisko tiksotropii smarów plastycznych. Badaniom poddano czyste (bez dodatków) smary litowe zagęszczane 12-hydroksystearynianem litu na bazie oleju mineralnego. Wyniki eksperymentu pokazały, że zarówno udział procentowy zagęszczacza, jak i gradient prędkości ścinania mają istotny wpływ na odbudowę mikrostruktury zagęszczacza litowego po procesie ścinania. Badania zostały przeprowadzone z wykorzystaniem reometru rotacyjnego - Rheotest 2.1 ze zmodyfikowaną głowicą pomiarową.

EN

The paper deals with influence of thickener fraction on thixotropy of lubricating greases. The research was done on pure (without any additives) lithium greases thickened by lithium 12-hydroxystearate witl mineral base oil. The results of the experiment showed that both the thickener fraction and shear rate have a significant influence on reconstruction of lithium thickener microstructure after the shearing process. The research was carried out by means of a rotary rheometer - Rheotest 2.1 with modified measuring head.

3

Pseudotiksotropowe właściwości zawiesin iłowo-cementowych

84%

Wójcik Ł. , Izak P. , Stempkowska A.

|

2011

|

tom T. 63, nr 2

278-282

PL

Przedstawiono nową koncepcję reologicznej kwalifikacji zawiesin iłowo-cementowych zawierających składniki strukturotwórcze. Szczególną uwagę zwrócono na odwracalne i nieodwracalne właściwości tiksotropowe. Wykazano, że w zawiesinach iłowo-cementowych w czasie ścinania zachodzą skomplikowane zjawiska mechaniczne powiązane z synerezą i przepływem kanałowym. Odwracalna, słaba struktura tiksotropowa związana z minerałami ilastymi jest przeplatana z nieodwracalną, mocną strukturą wewnętrzną powstałą w wyniku hydratacji cementu. W czasie kształtowania się takiej struktury pseudotiksotropowej, zawiesina iłowo-cementowa w stanie spoczynku przybiera postać żelu, który sukcesywnie wzmacnia się w wyniku reakcji hydratacji. Ostatecznie z takiej zawiesiny tworzy się wysokiej jakości spoiwo hydroizolacyjne.

EN

A new concept of rheological qualification of clay-cement suspensions containing structure agents has been shown. Special attention has been paid on reversible and irreversible thixotropic properties. This paper display, that some complicated phenomena connected with syneresis and channel flow occur inside clay-cement suspensions during shearing. The reversible week thixotropic structure connected with clay minerals is interlaced with the irreversible strong internal structure, creating as a result of the cement hydratation process. During developing this quasi-thixotropic structure, the clay-cement suspension at a rest state gains a gel structure, which successively becomes stronger as a result of the hydratation process, and finally arises a high-quality hydro-isolation binder.

4

Characterization of thixotropic compositions of unsaturated polyester resins. The absolute thixotropy index

84%

Oleksy M. , Galina H.

|

1999

|

tom T. 44, nr 6

430-432

EN

Thixotropic compositions (for details see [16]) of unsaturated polyester resins (POLIMAL 103) and low-M compound-modified smectite clays (bentonites) were Theologically characterized in terms of the absolute thixotropy index (TI). The index defined as the ratio of apparent viscosities at zero shear rate and at infinite shear rate was evaluated from apparent viscosity vs. shear rate curves established with the aid of Haake's RheoStress RS 100 plate-plate oscillatory (50 Hz) rheometer and a Rheotest 2 cylinder-cylinder rheometer at 25C. Results were correlated (eqn. 2); viscosities were evaluated at zero and infinite shear rates and hence TI was calculated (Table 1). The area under the flow curves was interpreted as the energy required to destroy the thixotropic structure of the composition.

PL

Scharakteryzowano 13 kompozycji (skład i preparatyka [16]) typu nienasycona żywica poliestrowa (Polimal 103) - modyfikowany bentonit pod względem właściwości reologicznych, wprowadzając przy tym pojęcie absolutnego indeksu tiksotropii (TI). Absolutny TI zdefiniowano jako stosunek lepkości pozornych określonych w warunkach szybkości ścinania równej zero i nieskończenie wielkiej. TI wyznaczano na podstawie zmierzonych krzywych lepkości pozornej w zależności od szybkości ścinania (rys. 2). Do pomiarów zastosowano reometr oscylacyjny (RheoStress RS 100 firmy "Haake") oraz reometr Rheotest 2 z układem cylindrów S2. Wyniki przybliżano analitycznie [równanie (2) z dobieralnymi parametrami], następnie wyznaczano lepkości graniczne w warunkach zerowej i nieskończenie dużej prędkości ścinania i stąd obliczano absolutny TI (tabela 1). Pole poci krzywą (rys. 2) zinterpretowano jako wartość energii wydatkowanej na zniszczenie tiksotropowej struktury kompozycji.

5

Tiksotropia struktury osadów w wybranych metodach ich kondycjonowania

84%

Bień B. , Bień J. D.

|

2008

|

tom T. 11, nr 1

31-43

PL

Przedstawiono wyniki badań wpływu metod kondycjonowania osadów ściekowych na wartości wskaźnika tiksotropii, charakterystyki reologiczne oraz strukturę. Do badań eksperymentalnych użyto osadów mineralnych pochodzących z galwanizerni. Osady kondycjonowano w następujący sposób: osad z galwanizerni + polielektrolit Praestol 2515 (słabo anionowy), osad z galwanizerni nadźwiękawiany w czasie 5 s, przy amplitudzie 8 µm + polielektrolit Praestol 2515, osad z galwanizerni nadźwiękawiany w czasie 5 s, przy amplitudzie 12 µ m + polielektrolit Praestol 2515, osad z galwanizerni nadźwiękawiany w czasie 5 s, przy amplitudzie 16 µm + polielektrolit Praestol 2515. Dawki polielektrolitów dobrano na podstawie przeprowadzonego testu CSK. Badania reologiczne wykonano za pomocą reometru RC 20. Oceny badanych układów dokonano w przedziale zmian prędkości deformacji: 0 ÷ 100 s-1 w czasie 228 s oraz 100 ÷ 1 s-1 w czasie 114 s. Do obserwacji struktury badanych osadów wykorzystano system analizy obrazu (Quick Photo Camera) i aparat cyfrowy Olympus WZ 7070 zintegrowany z mikroskopem optycznym Olympus BX51. Zdjęcia struktury wykonano w powiększeniu 10:1. Otrzymane dla osadów z galwanizerni krzywe płynięcia nie pokrywały się, dając pętlę histerezy, przy czym wyższe wartości naprężeń ścinających uzyskiwano dla rosnących gradientów prędkości (zakres 0 ÷ 100 s-1). Na podstawie uzyskanych pętli histerezy wyliczono wskaźniki tiksotropii badanych osadów. Stwierdzono, że w przypadku osadów kondycjonowanych zarówno polielektrolitem, jak i metodą łączoną wykorzystującą pole ultradźwiękowe i polielektrolit wartości wskaźnika tiksotropii rosną wraz ze wzrostem dawki. Najwyższe wartości wskaźnika tiksotropii uzyskano dla osadów kondycjonowanych samym polielektrolitem. Analiza struktury osadów kondycjonowanych polielektrolitem Praestol 2515, a także wstępnie polem ultradźwiękowym, a następnie polielektrolitem pokazuje, że wzrost dawki polielektrolitu powodował tworzenie się większych i bardziej zbitych kłaczków. Osady preparowane tylko polielektrolitami mają mniej stabilną strukturę niż osady wstępnie nadźwiękawiane, a następnie preparowane polielektrolitem. Badania tiksotropii osadów pochodzących z galwanizerni charakteryzują zachowanie się ich struktury. W przypadku gdy wskaźnik tiksotropii ma najwyższą wartość, zaobserwowano, że struktura jest najmniej stabilna i jej zachowanie nie może być opisane pojedynczą krzywą płynięcia.

EN

The paper presents the experimental results of the impact of different sludge conditioning methods on the value of thixotropic indicator, rheological behaviour and sludge structure. As sludge samples the mineral sludge from electroplating plant was used. The following methods for sludge conditioning were applied: sludge sample + polyelectrolyte Praestol 2515, sludge sample + sonication: t = 5 s, A = 8 µm + polyelectrolyte Praestol 2515, sludge sample + sonication: t = 5 s, A = 12 µm + polyelectrolyte Praestol 2515, sludge sample + sonication: t = 5 s, A = 16 µm + polyelectrolyte Praestol 2515. The dose of polyelectrolyte was selected based on CST test. The rheological tests were performed by the RC20 rheometer. The rheological properties of sludge were determined by comparison of direct dependences between shear rates and shear stresses. Tests were carried out at the controlled shear rates from 0 to 100 s-1 during 228 s and from 100 to 1 s-1 during 114 s. The sludge structure was observed using an electronic system consisted of digital camera Olympus WZ 7070, optical microscope Olympus BX51 and Quick Photo Camera software. For analysed sludge samples the flowing curves did not cover giving hysteresis noose where the higher value of shear stress was observed at growing shear rate (0 ÷ 100 s-1). On the base of hysteresis noose the thixotropic indicators were calculated. It was shown that the higher dose of polyelectrolyte the value of thixotropic indicator was also higher both when sludge was conditioned only by polyelectrolyte and when polyelectrolyte and ultrasounds were used. However the highest value of thixotropic indicator was obtained when only polyelectrolyte was used. The analysis of sludge structure shows that the higher dose of polyelectrolyte the larger and the more compact particles. Sludge samples prepared only by using polyelectrolytes have less stable structure than these which were first sonicated and than conditioned with polyelectrolytes. When the thixotropic coefficient is the highest, the sludge structure is the least stable and its behaviour cannot be described by a single flowing curve.

6

Monitoring the thixotropic effect in water-clay slurry systems used as a binder for moulding sands

84%

Zych J.

|

2007

|

tom Vol. 52, iss. 3

435-440

EN

The work presents results of studies concerning the reological stability of water-clay pastes. The dynamic viscosity of bentonite pastes was assesed by an ultrasonic method. The studies were focused on kinetics changes at so called restoring period. Changes occuring in that period are the result of thixotropy phenomenon, which is common in dispersed system. It is shown that the degree of the viscosity change is distinctive enough to play an important role in the green moulding sand technology (it amounts to over 240 kPa·s with paste concentration of 75%). The studies were original both in a methodology and obtained results. The dynamic viscosity of bentonite pastes was assessed in the function of their concentration (η = f (% of clay)). The empirical relationship between bentonite paste stretching durability and dynamic viscosity was assessed (Rm = f (η)). The unmonotonous nature of the dependence of dynamic viscosity on temperature was found (η = f (T)). The viscosity of concentrated water-clay systems reaches it�fs minimum in the temperature of about 30°C. The research of dynamic viscosity was conducted using an ultrasound method devised by the author.

PL

Przedstawiono wyniki badań stabilności reologicznej stężonych roztworow wodno-glinowych. Lepkość dynamiczną past bentonitowych wyznaczano metodą ultradźwiękową. Badania dotyczyły wyznaczania kinetyki zmian lepkości w tzw. okresie odstawania, czyli po zakończeniu ścinania. Zmiany w tym okresie są skutkiem zjawiska tiksotropii, które jest typowe dla roztworów dyspersyjnych. Wykazano, że skala zmian lepkości jest na tyle duża (wynosi ponad 240 kPa·s przy stężeniu pasty 75%), iż może mieć istotne znaczenie w całym procesie technologicznym przygotowania i wykorzystania wilgotnych mas formierskich. Wyznaczono lepkość dynamiczną past bentonitowych w funkcji ich stężenia (η = f (% gliny). Wyznaczono empiryczny związek pomiędzy wytrzymałością na rozciąganie i lepkością dynamiczną pasty (Rm = f (η). Stwierdzono niemonotoniczny charakter zależności lepkości dynamicznej od temperatury (η = f (T)). Lepkość stężonych układow wodno-glinowych osiąga minimum w temperaturze około 30°C. Badania lepkości dynamicznej past wykonano metodą ultradźwiękową opracowaną przez autora.

7

Tiksotropia osadów powstających w galwanizerni

84%

Soboniak E. , Bień B.

|

2006

|

tom T. 9, nr 3

287-299

PL

Przeprowadzono ocenę właściwości tiksotropowych osadów na podstawie wyznaczonej doświadczalnie pętli histerezy. Do badań zastosowano przemysłowe osady ściekowe pochodzące z galwanizerni, zlokalizowanej na terenie zakładu zajmującego się nakładaniem powłok galwanicznych. Osady kondycjonowano wstępnie polem ultradźwiękowym przez 5 sekund, stosując amplitudy 8, 12, 16 μm, a następnie dodawano polielektrolitu Praestol 2515. Dawki polielektrolitu dobrano na podstawie testu CSK. Oceny badanych układów dokonano w przedziale zmian prędkości deformacji 0 ÷ 100 s-1 w czasie 228 s oraz w zakresie 100 ÷ 0 s-1 w czasie 114 s i temperaturach: 15, 20, 25°C. Na podstawie przeprowadzonych pomiarów otrzymano zbiory punktów wyznaczających krzywe płynięcia, które nie pokrywały się, dając pętle histerezy. Przeprowadzono również obliczenia powierzchni pętli histerezy oraz wskaźnika tiksotropii. Na podstawie uzyskanych wyników stwierdzono, że istnieje wpływ temperatury oraz amplitudy drgań na wartość wskaźnika tiksotropii. Przedstawione wyniki badań właściwości tiksotropowych przemysłowych osadów ściekowych są dowodem na niestabilność struktury badanych osadów.

EN

The paper presents the results of research concerning the impact of industrial sewage sludge conditioning on changes of rheological parameters. The sludge was choosen from a galvanizing plant. Preliminary, the samples were sonicated for 5 seconds using three different amplitudes 8, 12, 16 μm (the field of 22 kHz was used) and next, polyelectrolytes were used for sludge conditioning anionic polyelectrolyte Praestol 2515. Based on the CST test the optimum doses of polyelectrolyte were determined and added to sludge prior to rheological measurements. The experiment was performed at three temperatures 15, 20, 25°C. The rheological tests were carried out at the shear rate from 0 to 100 s-1 during 228 s and from 100 to 0 s-1 during 114 s. Basing on the histeresis loop the thixotropic coefficients were calculated, and the relationships between them and the temperature. The change of temperature influences on the thixotropic properties of the sludge structure. Thixotropic coefficients show that the structure of industrial sludge is not stabile. Therefore rheological properties are a useful tool in sludge characterization as it allows to determine the stability of structure and the resistance to shearing stresses during sludge conditioning.

8

Charakterystyka płynięcia wybranych handlowych jogurtów naturalnych

84%

Dajnowiec F. , Zander L. , Wołkowiak J.

|

2007

|

tom Nr 1

40-41

PL

Analizowano zmienność parametrów modeli - potęgowego i Cas-sona oraz pola powierzchni pętli histerezy, reprezentujących charakterystyki płynięcia rynkowego jogurtu „naturalnego", pochodzącego od trzech producentów. Próbki od tych samych producentów wykazywały powtarzalne właściwości reologiczne, ale różnice od innych producentów były statystycznie istotne.

EN

The variability of rheological parameters in the power-law and Casson models, and the hysteresis loop area of commercial "natural" brand yoghurt originated from three manufacturers were analyzed. Samples taken from the same manufacturer displayed reproducible rheological properties, however statistically significant differences for various producers were observed.