Wyniki wyszukiwania - Biblioteka Nauki

1

Badanie mechanizmu inicjowania procesu erozji kawitacyjnej stopu odlewniczego na bazie fazy międzymetalicznej Ni₃Al

100%

Zasada D. , Bojar Z. , Jasionowski R.

|

tom Vol. 55, nr 3

235-242

PL

W referacie zaprezentowano wyniki badań erozji kawitacyjnej w okresie inkubacji stopu odlewniczego na bazie fazy międzymetalicznej Ni₃Al z dodatkami stopowymi boru, cyrkonu, chromu, molibdenu i żelaza. Badania prowadzono na materiale w stanie po odlewaniu oraz po procesie homogenizacji w temperaturze 1200°C, w czasie do 100 godzin, w atmosferze powietrza. Stwierdzono podobny charakter inicjowania zużycia kawitacyjnego w postaci mmikropęknięć i lokalnych ubytków zarówno w stanie po odlewaniu, jak i po homogenizacji.

EN

The result of research on initial state-incubation period of a cavitation wear in the intermetallic Ni₃Al alloy with boron, zirconium, chromium molybdenum, and iron are presented in this paper. Investigations were carried out both for as-cast and material after homogenization treatment. Experiments show that first micro-cracks are formed in the matrix-diphase regions (ɣ' + β) regions occur during further interaction of a liquid with alloy surface. After complete pulling out of surface layer fragments, a separation surface shows clear tracks of both brittle cleavable and fatigue crackings

2

Analiza procesu pękania wybranych stopów odlewniczych w próbie udarowego zginania

100%

Sadowski J.

|

tom R. 4, nr 12

167--178

PL

W pracy przedstawiono możliwości wykorzystania oprzyrządowanej próby udarowego zginania, dla dokładnej analizy procesu pękania stopów odlewniczych poprzez analizę rozdziału globalnej pracy łamania K na poszczególne składowe prac: Kz-zapoczątkowania, Kr- rozwoju, Kh- hamowania pęknięcia. Głębsza analiza tych wielkości pozwoliła na ocenę żywotności resztkowej wybranych stopów odlewniczych dla różnych rodzajów karbów karbu, w różnych stadiach obróbki technologicznej.

EN

This paper presents possibilities an application of the instrumentation of the impact bend test for accuracy analysis of cracking process of materials through an assessment of separation the global breaking K in particular components work: Kz –initiation, Kr-evolution, Kh-inhibition of cracking. In the detail analysis above mentioned quantities enable on assessment a remainder life of the choice casting alloys for various notch type and in different stages of the technological treatment.

3

Development of environmentally friendly cast alloys. High-zinc Al alloys

100%

Krajewski W. , Buras J. , Żurakowski M. , Greer A. , Mancheva M. , Haberl K. , Schumacher P.

|

2010

|

tom Vol. 45, nr 2

120-124

EN

Purpose: The main purpose of this paper is presenting the results obtained in years 2007 – 2010 in frame of the project Marie Curie Transfer of Knowledge – CastModel. The project was focused, among others, at elaborating new, environmentally friendly cast alloys based on the Al-Zn system. Particularly, efforts were aimed at improving ductility of the sand cast high-zinc aluminium alloys (HZnAl) by using the newly elaborated master alloys, based on the Al-Zn-Ti system. Design/methodology/approach: The presented work is focused on the nucleation of the high-zinc Al-20 wt% Zn (HZnAl AlZn20) alloy, known as the high damping one, aiming at improving plastic properties of the sand castings. The melted alloy was nucleated with AlTi5B1 (TiBAl) and AlTi3C0.15 (TiCAl) refiners as well as with the newly introduced ZnAl-Ti3 one. During the research the following experimental techniques were used: LM, SEM-EBSD, EDS, TA, DSC, Quantitative Metallography, UTS, Elongation and Attenuation coefficient measurements. Findings: During the performed examinations it was found out that significant increasing of the grain population of the inoculated alloy increases plasticity represented by elongation. The attenuation coefficient of the nucleated alloy, measured using an Olympus Epoch XT device, preserves its high value. The results obtained allow to characterize the examined AlZn20 alloy as promissive, having good strength and damping properties as well as the environmentally friendly alloy because of its comparatively low melting temperatures. Practical implications: The grain-refined high-zinc aluminium alloys can be used as the high damping substitutes of the traditional, more energy consumable Fe-based foundry alloys. Originality/value: The newly elaborated ZnAl-Ti based master alloys show high refining potency and quick dissolution in low melting temperatures of about 500°C, and are the promissive alternatives of the traditional AlTi-based ones.

4

Badania nad procesem plastycznego odkształcania stopów aluminium o strukturze odlewniczej na przykładzie stopu EN AC-42100

84%

Knych T. , Mamala A. , Uliasz P. , Popek B.

|

2008

|

tom R. 53, nr 4

235-240

PL

W artykule zamieszczono wyniki badań nad procesem odkształcenia plastycznego próbek ze stopu EN AC-42100 zaliczanego do grupy stopów odlewniczych. Materiały takie w stanie po odlaniu charakteryzują się dwufazową budową strukturalną oraz możliwością występowania nieciągłości materiałowych w postaci porowatości, co przekładać się może na ograniczenia podczas dalszych procesów technologicznych. Zaprezentowane wyniki obejmują próby spęczania próbek walcowych oraz próbek z symulowaną nieciągłością. Badania prowadzono w zmiennych warunkach temperatur, prędkości odkształcenia oraz wielkości gniotu. W artykule poddano analizie charakterystyki spęczania próbek oraz mikrostruktury z obszarów spajanych nieciągłości. Uzyskane wyniki badań wskazują na możliwość uzyskiwania trwałych odkształceń materiału bez naruszenia jego spójności oraz pozwalają na otrzymanie zespolenia materiału w obszarze występujących porowatości.

EN

This paper presents results of investigation in plastic deformation of typical aluminium casting alloys EN AC-42100. These alloys after cast process characterize diphase structure and porosity which are causes limitation of formability. Presented results shows upsetting tests of cylindrical samples and samples with discontinuity simulation. Tests were performed at different temperature, strain rate and level of deformation condition. Stress-strain curves and microstructure at area of discontinuity were registered. Results shows on possibility of permanent deformation of casting material without decohesion and help in good bonding in discontinuity area.