Stopy intermetaliczne i spieki ciężkie jako nowe materiały

100%

Bojar Z. , Jackowski A. , Michałowski J. , Piętaszewski J. , Przetakiewicz W. , Włodarczyk E.

|

tom Z. 72

83-96

PL

W referacie posumowano wyniki prac w zakresie technologii wytwarzania i przetwarzania stopów na osnowie faz międzymetalicznych, w szczególności z układów Ni-Al i Fe-Al oraz omówiono efekty związane z uplastycznieniem wybranych stopów. Zbadano wpływ rodzaju proszku żelaza, stopnia utlenienia proszku wolframu oraz rodzaju atmosfery spiekania na jakość spieków W-7%Ni-3%Fe. Oceniono wpływ obciążenia wybuchowego spieku na jego właściwości.

EN

The results of investigations of Ni-Al and Fe-Al intermetallic alloys were summarised in this paper. Many different methods utilising plastic forming, heat treatment and thermomechanical tretment of castings as well hot pressing and sintering of powder materials and consolidation of layered structures or protective coatings were used to obtain new alloys on a base or with significant contents of intermetallic phases in the structure. The influence of sintering atmosphere, sort of iron powder and level of tungsten powder oxidation on selected properties of W-Ni-Fe sinters was investigated. The effect of explosive loading of sinters on their properties was described too.

2

Badania wybranych właściwości spieku 80W-20Re

86%

Majewski T. , Durejko T. , Rosiński M. , Michalski A.

|

2012

|

tom Vol. 61, nr 2

391-403

PL

W artykule przedstawiono wyniki wstępnych badań spieków 80W-20Re. Próbki do badań wytworzono, wykorzystując trzy warianty procesu technologicznego: spiekanie rezystancyjne (RS), metodę PPS oraz spiekanie w piecu próżniowym. Dwie pierwsze metody pozwoliły otrzymać spiek o zbliżonych właściwościach (porowatość, twardość), natomiast w wyniku spiekania wysokotemperaturowego w piecu próżniowym uzyskano materiał o bardzo dużej porowatości. Jednocześnie stwierdzono, że spiekanie metodami RS i PPS powoduje powstanie mikrostruktury anizotropowej, o wydłużonym kształcie cząstek.

EN

The results of preliminary investigation of 80W-20Re sinters were presented in the paper. The samples were prepared using 3 variants of technological process: resistance sintering (RS), Pulse Plasma Sintering and sintering in the vacuum furnace. First and second methods allowed us to obtain the sinters possessing similar properties (porosity and hardness), however as a result of final sintering at high temperature in the vacuum furnace, very porous materials were obtained. Moreover it was observed, that sintering by RS and PPS methods caused development of anisotropy microstructure with characteristic elongated shape of particles.

3

Badania spieku 77W-20Re-3Ni przeznaczonego na rdzenie pocisków przeciwpancernych

72%

Majewski T. , Dębski A. , Leszczyńska-Sejda K.

|

2015

|

tom Vol. 6, Nr 4 (22)

69-81

PL

W artykule przedstawiono wyniki badań procesu wytwarzania i właściwości wolframowego spieku ciężkiego, przeznaczonego na rdzenie podkalibrowych pocisków przeciwpancernych. Badany materiał zawierał 77% wolframu, 20% renu oraz 3% niklu. Próbki do badań wykonywano technologią metalurgii proszków. Zastosowano izostatyczne prasowanie mieszanki proszków i dwustopniowe spiekanie: wstępne - w atmosferze zdysocjowanego amoniaku i ostateczne - w próżni. W artykule zamieszczono schemat wytwarzania tego spieku i pokazano przykładowe obrazy jego mikrostruktury. W dalszej części zamieszczono wyniki analizy składu chemicznego w wybranych mikroobszarach badanego materiału oraz wybrane właściwości mechaniczne, takie jak wytrzymałość na ściskanie i twardość. Z otrzymanych spieków wykonano rdzenie do pocisków i umieszczano je w stalowym sabocie. Pokazano wyniki eksperymentów balistycznych dotyczących badania właściwości penetracyjnych w zakresie zastosowania tego spieku na rdzenie pocisków przeciwpancernych. Określono współczynnik penetracji, a także przedstawiono obrazy przekrojów rdzeni po strzelaniu. W oparciu o zdjęcia wykonane przy zastosowaniu skaningowego mikroskopu elektronowego opisano mikrostrukturę wybranych próbek. Ustalono, że procesowi penetracji towarzyszyło zjawisko samoostrzenia rdzenia.

EN

The results of investigation of production process and properties of W-Re-Ni sinters intended for cores of anti-tank missiles were presented in the paper. The tested material contained 77% of tungsten, 20% of rhenium and 3% of nickel. The test specimens were made by powder metallurgy. The production process consisted of powder mixture pressing by CIP method and two-stage sintering: initial - in an atmosphere of dissociated ammonia and final - in vacuum. The diagram of the production process of this sinter and exemplary picture of its microstructure were shown in the paper. The results of the analysis of the chemical composition of selected microregions examined materials, and selected mechanical properties such as compressive strength and hardness were presented in the next part of the paper. The cores of the projectiles, which were made from the examined materials, were put in a steel sabot. The results of experiments connected with investigation of the penetration properties in the field of using this sinter as the cores of anti-tank shells were shown. The penetration coefficient was determined, and moreover cross-sectional images of the cores after shooting were presented. Based on the photographs taken using a scanning electron microscope the microstructure of selected samples was described. It was settled that the cores selfsharpening phenomenon was appeared during penetration.

4

Badanie możliwości wykorzystania renianu(VII) tetraaminaniklu(II) wysokiej czystości do wytwarzania proszku stopowego Re-Ni

72%

Majewski T. , Leszczyńska-Sejda K. , Michałowski J. , Piętaszewski J.

|

2016

|

tom Vol. 65, nr 2

81--92

PL

W artykule przedstawiono metodę otrzymywania wysokiej czystości renianu(VII) tetraaminaniklu(II). Metoda ta polega na reakcji stężonego roztworu wody amoniakalnej z wysokiej czystości bezwodnym renianem(VII) niklu(II). Uzyskany w ten sposób renian(VII) tetraaminaniklu(II) redukowano w atmosferze zdysocjowanego amoniaku w celu otrzymania proszku stopowego Re Ni. W artykule umieszczono również informacje dotyczące wybranych właściwości fizykochemicznych uzyskanego proszku. Stopowy proszek Re-Ni może znaleźć zastosowanie m.in. w wytwarzaniu wolframowych spieków ciężkich.

EN

In this paper, a method for preparation of high purity tetraaminenickel(II) perrhenate is presented. This method comprises reacting of a concentrated solution of ammonia water with high purity anhydrous nickel(II) perrhenate(VII). The resulting tetraaminenickel(II) perrhenate is reduced under dissociated ammonia conditions, to obtain Re-Ni alloy powder. The article also provides information on selected physicochemical properties of the produced powder. Such Re-Ni alloy powder can be applied for tungsten heavy alloys production.

5

Badania i analiza właściwości cieplno-fizycznych spieku 90W-7Ni-3Fe

58%

Panas A. J. , Terpiłowski J. , Majewski T.

|

2010

|

tom Vol. 59, nr 3

307-328

PL

W artykule przedstawiono wyniki badań doświadczalnych oraz kompleksowej analizy właściwości cieplno-fizycznych (termofizycznych) spieku o składzie 90% W, 7% Ni i 3% Fe. Badany materiał, wytwarzany metodą spiekania z udziałem fazy ciekłej, ma niejednorodną strukturę kompozytu dyspersyjnego z fazą wiążącą w postaci stopu o składzie 53% Ni, 23% Fe i 24% W wypełnioną quasi-sferycznymi cząstkami wolframu. W badaniach doświadczalnych określono charakterystyki termiczne ciepła właściwego w zakresie temperatury od -15°C do 600°C, liniowej rozszerzalności cieplnej i wydłużenia względnego w zakresie od 20°C do 1120°C oraz dyfuzyjności cieplnej w zakresie od 20°C do 670°C. Doświadczenia wykonano za pomocą mikrokalorymetru skaningowego (DSC), dylatometru interferencyjnego oraz stanowiska do badań dyfuzyjności cieplnej metodą impulsowego powierzchniowego wymuszenia laserowego. W pracy przedstawiono reprezentatywne charakterystyki poszczególnych właściwości termofizycznych dla zakresu temperatury od 20°C do 600°C, który odpowiada obszarowi wspólnemu dla wszystkich wykonanych doświadczeń. Analizę uzupełniono wynikami predykcji przewodności elektrycznej, a także dodatkowymi badaniami gęstości wykonanymi metodą wypornościową.

EN

Results of experimental investigation followed by complex thermophysical property analysis of 90W-7Ni-3Fe tungsten heavy alloy (WHA) have been discussed. The alloy was manufactured by sintering in a vacuum. It shows the structure of a dispersed composite with 53Ni-23Fe-24W matrix and tungsten quasi-spherical particle filling. The experimental studies included differential scanning calorimetry (DSC), laser interferometry, and laser flash (LF) measurements of a specific heat, thermal expansivity and thermal diffusivity, respectively. The DSC measurements have been performed within the temperature range from -15°C to 600°C, the dilatometric from 20°C to 1120°C, and the LF from 20°C do 670°C. These results have been supplied by a density measurement. The experiments revealed two reversible phase transitions at about 250°C and about 700°C. The raw experimental data of all investigated thermophysical parameters have been fitted applying B-spline approximation. As a result, C1 class thermal characteristics have been obtained for the specific heat (SH), the coefficient of a linear thermal expansion (CLTE) and the thermal diffusivity (TD). Next, the thermal conductivity (TC) within the temperature interval from 20°C to 600°C has been calculated. Finally, the electrical conductivity has been predicted using the Widemann-Franz-Lorentz equation from the TC results.