Nickel and Copper-Free Sintered Structural Steels Containing Mn, Cr, Si, and Mo Developed for High Performance Applications

100%

Cias A. , Stoytchev M.

|

tom Vol. 62, iss. 1

11--17

EN

In an attempt to study the sinterability of potential high-strength nickel-free sintered structural steels containing Mn, Cr, Si and Mo compacts were prepared based on sponge and water atomised iron powders and on Astaloy prealloyed powders. To these were admixed ferromanganese, ferroslicon, and graphite. The samples were sintered at temperatures 1120 and 1250°C in laboratory tube furnaces in hydrogen, hydrogen-nitrogen atmospheres with dew points better than –60°C or in nitrogen in a semiclosed container in a local microatmosphere. After sintering the samples were slowly cooled or sinterhardened. Generally resultant microstructures were inhomogeneous, consisted of pearlite/ bainite/martensite, but were characterised by an absence of oxide networks. Sintering studies performed over a range of compositions have shown that superior strength, ranging beyond 900 MPa, along with reasonable tensile elongation, can be achieved with these new steels.

2

Sintered Steels Coated with a Chromium Layer Doped with Diamond Nanoparticles

100%

Petkov V. , Valov R. , Witkowska M. , Madej M. , Cempura G. , Sułowski M.

|

tom Vol. 64, iss. 4

1633--1638

EN

Electrochemical Cr coatings doped with diamond nanoparticles were deposited on sintered steels with different carbon contents (0.2-0.8 wt.-%). The mechanical properties of surfaces as hardness and wear resistance increase as compared to the steel substrate. Microcutting and microgridding mechanisms were observed after tribological tests, but also adhesive wear in some areas was observed. X-ray examination indicated that the layer was textured, with the exception of the sample with the highest concentration of diamond nanoparticles in the electrolyte (42 g/l). The intensity ratio ICr110/ICr200 was calculated and compared with the indices for a standard sample. The greatest differences in the intensity ratio occurred for the samples with low carbon content (0.2% C). On the other hand, more the material is textured the greater the difference.

3

Własności cykliczne stopowej stali spiekanej po nawęglaniu próżniowym

75%

Kaleta J. , Kotowski P. , Widanka K.

|

tom Z. 68, t. 1

213--220

PL

W pracy porównano własności cykliczne stopowej stali spiekanej z Cr, Mn i Mo o trzech różnych gęstościach w stanie spiekanym i po obróbce cieplno-chemicznej (nawęglaniu próżniowym). Próbki badano w jednoosiowym stanie naprężenia przy zastosowaniu symetrycznego sinusoidalnego widma obciążenia (R=-1) o częstotliwości f=25 Hz. Widmo obejmowało szeroki zakres obciążeń poczynając od obszaru sprężystego aż do zakresu znacznych odkształceń plastycznych. Wielkością sterującą była amplituda odkształcenia σa. Przeprowadzono badania zarówno przy ustalonym jak i narastającym widmie obciążenia. Do wyznaczania energii ΔW i odkształcenia plastycznego obciążenia εpl zastosowano specjalną metodę dynamicznej pętli histerezy. Metoda pozwoliła na pomiar bardzo małych kątów przesunięcia fazowego ϕ, co jest charakterystyczne dla stali spiekanych. Wykazano, iż zastosowana obróbka cieplno-chemiczna spowodowała wzrost własności wytrzymałościowych oraz spadek własności plastycznych. Zmiany własności były uzależnione silnie od gęstości.

EN

Cyclic properties of the alloyed P/M steel with Cr, Mn and Mo with three different densities, in sintered state and after vacuum carburizing are compared. Specimens were tested in one-directional sinusoidal tension-compression (R=-1, f=25 Hz) over a range of load (step-by-step method). The tests were carried out under stress amplitude control conditions. Special method of measurements of hysteresis loop area ΔW and plastic strain εpl was used. The method remains valid in the range of extremely small angles ϕ up to 1 x 10-4 rad. It was shown that proposed case hardening treatment method results in higher cyclic properties.

4

Zastosowanie języka VBA do analizy krzywych rozciągania materiałów spiekanych

51%

Jurczak-Kaczor P. , Sułowski M.

|

tom R. 59, nr 11

545--553

PL

Głównym celem pracy było opracowanie algorytmu i programu komputerowego w języku VBA, który na podstawie danych zapisanych w pliku tekstowym *.dat, otrzymanych ze statycznej próby rozciągania, wyznaczy krzywą rozciągania dla materiałów spiekanych oraz pozwoli na obliczenie wyraźnej lub umownej granicy plastyczności oraz wytrzymałości na rozciąganie, a także wydłużenia materiałów spiekanych. W tym celu wykorzystano rozszerzone możliwości arkusza kalkulacyjnego MS Excel. Zastosowanie języka VBA (poprzez użycie odpowiednich procedur, metod, właściwości, konstrukcji oraz funkcji) pozwoliło na automatyzację obliczeń poprzez utworzenie algorytmu, który w szybki sposób na podstawie danych zarejestrowanych w postaci pliku *.dat, otrzymanego podczas próby rozciągania wyznaczy parametry próby rozciągania. Oprócz opisu działania programu, wraz z wybranymi funkcjami użytymi w trakcie tworzenia kodu, w artykule zamieszczono przykład zastosowania programu do analizy krzywych rozciągania spiekanych stali wykonanych na bazie stopowych proszków żelaza Astaloy CrA, Astaloy CrL oraz Astaloy CrM, o średniej wytrzymałości na rozciąganie mieszczącej się w zakresie od 513 do 753 MPa.

EN

The main aim of the paper was to develop algorithm and computer program in VBA programming language, which would be used to process data text files (*.dat) in order to draw a tensile curve and calculate the yield strength, or offset yield strength, tensile strength and elongation of sintered materials. For this purpose, the extended possibilities of MS Excel worksheet were used. Applying of VBA programming language (by using appropriate procedures, methods, properties, structures and functions) allowed to automate of computing by creation an algorithm, which based on data gathered in *.dat file obtained from tensile test allow to calculate parameters of tensile test of sintered materials. Except the description of the algorithm, together with selected functions used during writing code, in the paper the output of program in the form of strain-stress curves of sintered steels, with mean tensile strength in the range of 513-753 MPa, based on pre-alloyed iron powders Astaloy CrA, Astaloy CrL and Astaloy CrM was shown.