Comparative Study of the Quality Parameters of Knitted Fabrics Produced from Sirospun, Single and Two-ply Yarns twist multiplier on the properties

100%

Kireçci A. , Kaynak H. K. , Ince M. E.

tom Vol. 19, no. 5 (88)

82--86

This study aimed to examine the quality parameters of knitted fabrics produced from sirospun, single and two-ply yarns. To achieve this, knitted fabrics were produced from these yarns with yarn numbers of 29.5 tex, 33 tex and 37 tex. Then sirospun yarn fabrics with 6 mm, 8 mm and 11 mm strand spacings were produced to observe the effect of strand spacing on fabric quality parameters. The experimental results show that the unevenness, hairiness, strength and elongation values of sirospun yarns are similar to or better than those of single and conventional plied yarns for all samples. However, enlarging the strand spacing causes small reductions in hairiness, strength and elongation values. The results of the fabric performance test show that the bursting strength, abrasion resistance and pilling resistance of sirospun yarn fabrics are as good as those of single and conventional plied yarn fabrics. However, the spirality values of plied yarn fabrics are slightly lower than those of sirospun yarn fabrics at finer yarn count values. These results indicate that sirospun yarn may be a good alternative for plied yarn due to its extremely low production cost and high quality values.

Dla przeprowadzenia analizy wyprodukowano dzianiny z przędz o masie liniowej 29.5 tex, 33 tex, 37 tex. Dla oceny wpływu odstępu między tasiemkami stosowano odstępy 6 mm, 8 mm i 11 mm. Wyniki badań wskazują, że nierównomierność, włochatość, wytrzymałość i wydłużenie są podobne dla wszystkich próbek otrzymanych przędz lub korzystniejsze niż dla konwencjonalnie plecionych. Jednakże stwierdzono również, że ze wzrostem odległości między tasiemkami pogarszają się w małym stopniu wyniki w zakresie włochatości, wytrzymałości i wydłużenia . Badanie dzianin wykonanych z przędz sirospun wykazały ,że wytrzymałość na zrywanie, na ścieranie i piling są nie gorsze niż dla przędz pojedynczych i plecionych konwencjonalnie. Jednakże spiralność dzianin wykonanych z przędz pojedynczych lub skręcanych konwencjonalnie jest nieco mniejsza niż spiralność dzianin wykonanych z przędz sirospun o mniejszych masach liniowych. Ogólnie można stwierdzić ,ze przędze typu sirospun są dobra alternatywą do produkcji dzianin biorąc pod uwagę bardzo niskie koszty produkcji i dobrą jakość przędz.

Properties of plain knits from siro-spun viscose/spandex yarns

80%

Beceren Y. , Candan C. , Duru Cimilli S. , Ülger K.

2010

tom Vol. 18, no. 1 (78)

41--46

This paper focuses on the dimensional and selected physical properties of a series of plain jersey fabrics made from viscose siro-spun and carded ring yarns of 2/10 tex and 20 tex, respectively. Elastane yarn was incorporated into the fabric using the plaiting technique. In general, for both greige and dyed knitted fabrics, the stitch density decreased, whereas the weight increased as the stitch length increased. Moreover, for greige and dyed dry-relaxed fabrics from siro yarn, the twist had an influence on fabric properties, the effect being relatively more prominent for slack samples. Moreover, both slack and tight dry relaxed dyed samples from high twist siro yarns featured lower resistance to abrasion. As far, as dyed and laundered samples from siro yarns are concerned, the results revealed that irrespective of the loop length, the samples from average twist siro yarns tended to give a higher stitch density and weight values. When abrasion resistance values of samples from both average and high twist siro yarns were studied, it could be suggested that in addition to yarn properties, the effect of fabric properties on the abrasion behavior of the samples became more prominent after laundering. As far as the abrasion resistance and pilling properties of the samples are concerned, the fabrics from siro-spun yarns tended to perform better. Finally, the pilling test method employed affected not only the size and shape of the pill entanglements on the surface of the samples but also the degree of fibre damage within the fuzz entanglements.

W pracy omówiono właściwości geometryczne i wybrane parametry fizyczne serii dzianin lewo-prawych wykonanych z przędz wiskozowych typu siro-spun i zgrzeblonych przędz obrączkowych o masie liniowej 2/10 tex i 20 tex. Przędze elastomerowe zostały wprowadzone w dzianinę metodą wplecenia. Ogólnie można powiedzieć, że zarówno dla dzianin surowych jak i barwionych gęstość splotów maleje podczas gdy ciężar powierzchniowy wzrasta wraz ze wzrostem długość splotu. Ponadto, dla surowych i barwionych dzianin z przędzy „siro” relaksowanych w stanie suchym, skręt przędzy ma wpływ na parametry dzianiny. Efekt ten jest bardziej widoczny w przypadku dzianin luźnych. Ponadto dzianiny luźne jak i ścisłe relaksowane w stanie suchym wykonane z przędz typu „siro” o dużym skręcie wykazują mniejsza odporność na ścieranie. Biorąc pod uwagę próbki barwione i prane z przędz „siro, wyniki wskazują, że niezależnie od długości oczka, próbki wykonane z przędz o średniej wartości skrętu posiadają wyższą gęstość splotów oraz większy ciężar powierzchniowy. Biorąc pod uwagę odporność na ścieranie próbek wykonanych z przędz o średniej i dużej wartości skrętu można zasugerować, że efekt wpływu właściwości dzianin na odporność na ścieranie jest bardziej widoczny po praniu. Uwzględniając odporność na ścieranie i piling dzianin można powiedzieć, że dzianiny z przędz „siro” wykazują lepsze właściwości. Metoda sprawdzania pilingu ma istotne znaczenie nie tylko na wielkość i kształt pil i sposób splątania włókien ale również na stopień zniszczenia włókien.