The impact of deformation on structural changes of the duplex steel

100%

Niewielski G. , Radwański K. , Kuc D.

Journal of Achievements in Materials and Manufacturing Engineering

2007

tom Vol. 23, nr 1

31-34

Purpose: Despite the many years' research on the plasticity of duplex steels, it was impossible to conclusively determine the mechanisms for structure recovery during the plastic deformation. The paper will attempt to provide explanations for the changes taking place in the steel structure during the superplastic flow. Design/methodology/approach: After a solution heat treatment at 1250 degrees centigrade, the steel was subjected to cold deformation through rolling with the total 70% reduction. The specimens were tensioned in the "Instron" strength-testing machine at temperature 850 degrees centigrade at a rate of vr=15x10 to the -3 mm/s in a 0.005Pa vacuum. Structural examination was carried out using light and electron microscopy. The micro-diffraction technique was applied to provide diffraction images with Kikuchi lines. Findings: A joint operation of structure reconstruction mechanisms during the deformation of the analyzed steel with the process of sigma phase precipitation inhibiting further growth of the newly-formed grain has been determined. Practical implications: The capacity for increased deformability through combined thermo-mechanical processes, requiring a precise selection of the deformation parameters, has been indicated. Originality/value: The results obtained are vital for designing an effective thermo-mechanical processing technology for the investigated steel.

Formability of Invar 36 alloy at high temperatures

80%

Kawulok P. , Jurek D. , Schindler I. , Kawulok R. , Opěla P. , Němec J. , Kawuloková M. , Rusz S. , Sauer M.

tom Vol. 74, no. 1

15--20

By using of hot tensile tests, which were performed on simulator HDS-20, the formability of Invar 36 alloy was investigated. By a special type of a tensile test, involving a continuous control heating of the tested specimens and their simultaneous load by a constant tensile force of 80 N, a nil-strength temperature of investigated alloy 1419°C was determined. By continuous uniaxial tensile tests to rupture the strength and plastic properties of the Invar 36 alloy were determined in the wide range of deformation temperatures (from 800°C to 1390°C) and mean strain rates (from 0.09 s-1 to 75 s-1). On the basis of obtained results the 3D maps were constructed, expressing the dependence of the contractual hot ultimate tensile strength, hot ductility and hot reduction of area of the Invar 36 alloy on the deformation temperature and on the mean strain rate. Based on the determined plastic properties, the nil-ductility temperature of the investigated alloy of 1390°C was also determined.

Za pomocą prób rozciągania na gorąco, które przeprowadzono na symulatorze HDS-20, zbadano odkształcalność stopu Invar 36. Przy użyciu specjalnej próby rozciągania, polegającej na ciągłym sterowanym nagrzewaniu badanych próbek i równoczesnym ich obciążeniu stałą siłą rozciągającą 80 N, wyznaczono temperaturę zerowej wytrzymałości badanego stopu, która wyniosła 1419°C. Za pomocą ciągłych jednoosiowych prób rozciągania prowadzonych do zerwania określono właściwości wytrzymałościowe i plastyczne stopu Invar 36 w szerokim zakresie temperatur odkształcenia (od 800°C do 1390°C) i średnich prędkości odkształcenia (od 0,09 s-1 do 75 s-1). Na podstawie uzyskanych wyników skonstruowano mapy 3D, wyrażające zależność wytrzymałości na rozciąganie na gorąco, plastyczności na gorąco i przewężenia stopu Invar 36 od temperatury odkształcenia i średniej szybkości odkształcania. Na podstawie wyznaczonych właściwości plastycznych określono również temperaturę przejścia w stan kruchy badanego stopu wynoszącą 1390°C.