Wyniki wyszukiwania - Biblioteka Nauki

1

Współczesne tendencje w technologii betonów

100%

Prokopski G.

|

2008

|

tom z. 47 [252]

365-370

PL

Przedstawiono współczesne trendy w wykonywaniu betonów cementowych. Scharakteryzowano podstawowe cechy, jakim powinny odpowiadać betony cementowe nowej generacji, o znacznie większej trwałości oraz rolę domieszek polimerowych w uzyskiwaniu tych betonów.

EN

There were introduced present tendency in executing of cement concretes. Characterized the basic properties of new generation cement concretes (with considerably larger durability) as well as the role of polymer admixtures in produce process these concretes.

2

Nowy środek polimerowy do regulacji parametrów technologicznych świeżych zaczynów cementowych

100%

Stryczek S. , Wysocki S. , Złotkowski A. , Formela M. , Gaczoł M.

|

2018

|

tom T. 97, nr 6

906--909

PL

Przedstawiono wyniki badań nad zastosowaniem nowego środka polimerowego zawierającego terpolimer chlorków [(2-(akryloiloksy) etylo)trimetyloamoniowego i (3-akryloamidopropylo) trimetyloamoniowego] oraz akryloamidu. Dodatek tego środka poprawia właściwości reologiczne badanych zaczynów.

EN

A mixt. of crosslinked starch, a XCD biopolimer and a CH2=CHCOO(CH2)2NMe3Cl, CH2=CHCONH(CH2)3NMe3Cl and CH2 = CHCONH2 terpolymer was prepd. and added as a new polymeric agent to std. cement slurries. The addn. resulted in an improvement of rheol. properties of the slurries.

3

Wpływ czynników materiałowych na skurcz tynków renowacyjnych

80%

Brachaczek W.

Prace Instytutu Ceramiki i Materiałów Budowlanych

|

2018

|

tom R. 11, nr 32

7--20

PL

Do odnawiania zawilgoconych i zasolonych murów stosowane są tynki renowacyjne. Jedną z istotnych właściwości odróżniających je od tradycyjnych tynków cementowych i cementowo-wapiennych jest porowatość. Mimo że tynki renowacyjne stosowane są już od kilkudziesięciu lat i w wielu przypadkach korzyści wynikające z ich używania są oczywiste, to pojawiły się również głosy krytyczne. Dotyczyły one przede wszystkim pojawiania się rys przy wysychaniu, odspajania zarówno bezpośrednio po nałożeniu, jak i w trakcie użytkowania. Jedną z przyczyn tego zjawiska może być nadmierny skurcz tynków renowacyjnych przy wysychaniu [1]. W artykule przedstawiono wyniki badań wpływu pochodnych celulozy, polimerów syntetycznych, domieszek napowietrzających i lekkich kruszyw na skurcz tynków renowacyjnych. Najmniejszy skurcz uzyskano przy zastosowaniu pochodnych celulozy na bazie hydroksyetylometylocelulozy (HEMC), hydroksypropylometylocelulozy (HPMC) oraz polimeru syntetycznego na bazie terpolimeru poli(octan winylu-co-wersenian winylu-co-akrylan) (VA/VeoVa/AC). Wpływ na zmniejszeniu skurczu wywierały także domieszki napowietrzające oraz dodatek lekkich kruszyw. Przez odpowiedni dobór tych składników można znacznie poprawić właściwości użytkowe tynków renowacyjnych.

EN

The renovation plasters are used to cure the damped and salted walls. One of crucial properties which differentiates renovation plasters from traditional lime, or cement-lime plasters, is their porosity. Despite the fact that renovation plasters have been used for several dozen years and in many cases, the benefits of their application are obvious, there are also critical opinions. In a lot of cases, they concern the cracks which appear while drying, and loosening right after the application as well as during the use. One of the causes of this phenomenon is the excessive contraction of renovation plasters while drying [1]. The paper presents the test results of the impact of cellulose admixtures, synthetic polymers, aeration admixtures and light aggregates on the contraction of renovation plasters. The lowest contraction was achieved with the use of cellulose derivates based on hydroxyethyl methyl cellulose (HEMC), hydroxy propyl methyl cellulose (HPMC), and synthetic polymer based on terpolymer poly (vinyl acetate-co-vinyl ester of versenic acid-co-acrylate) (VA/VeoVa/AC). The aeration admixtures and the addition of lightweight aggregates also had an influence on the reduction of the contraction. The smallest shrinkage was obtained using cellulose derivatives based on hydroxyethyl methylcellulose (HEMC), hydroxypropylmethylcellulose (HPMC) and a synthetic polymer based on terpolymer poly (vinyl acetate-co-vinyl ester of versenic acid-co-acrylate) (VA/VeoVa/AC). The aeration admixture and the addition of light aggregates also had an effect on shrinkage reduction. The proper selection of renovation plasters allows for significant improvement in the utility properties of renovation plasters.

4

Wpływ różnych dodatków polimeru butadienowo-styrenowego PBS na hydratację krzemianu trójwapniowego

80%

Wang R. , Yue X.

Cement Wapno Beton

|

2016

|

tom R. 21/83, nr 5

336--346

PL

W pracy omówiono badania wpływu dodatku kopolimeru butadien-styren na hydratację krzemianu trójwapniowego. Oznaczono ciepło hydratacji, morfologię fazy C-S-H, zawartość wodorotlenku wapniowego i C3S, który nie uległ hydratacji. Wyniki wykazały, że kopolimer wydłuża okres indukcji oraz opóźnia pojawienie się okresu wzrostu szybkości reakcji, a także zmniejsza maksymalną szybkość wydzielania ciepła w tej fazie hydratacji. Cząsteczki kopolimeru są adsorbowane na powierzchni ziaren C3S we wczesnej fazie hydratacji. Po 3 dniach hydratacji, polimer może tworzyć błonki na powierzchni alitu, co utrudnia wzrost fazy C-S-H. Dodatek kopolimeru opóźnia hydratację C3S, przy czym efekt ten jest tym większy im większa jest jego zawartość.

EN

The addition of styrene-butadiene rubber latex on the hydration of tricalcium silicate was studied in presented research. Hydration heat, morphology of C-S-H, content of calcium hydroxide and unhydrated C3S were determined. The results showed that SBR latex could not only prolong the induction period and retard the appearance of acceleration period, but also decrease the maximum rate of heat evolution and the slope of acceleration period of C3S hydration. SBR particles adsorbed on the surface of C3S crystals in early age and formed film after 3 days, and decrease the C-S-H fibres. In general, the addition of SBR retarded the hydration of C3S and this effect was enhanced with the increasing dosage of SBR latex.