The influence of pH adjusted with different acids on the dyeability of polyester fabric

100%

Miljkovic M. N. , Djordjevic D. M. , Miljkovic V. M. , Stamenkovic M. , Stepanovic J.

Polish Journal of Chemical Technology

|

2014

|

tom 16

|

nr 4

1-5

EN

The influence of using formic, oxalic, citric, tartaric, hydrochloric, nitric, sulphuric and phosphoric acid for dyebath pH adjustment was investigated upon the dyeing of polyester fabric with CI Disperse Yellow 60. The positions of colour in CIELab coordinates of the samples dyed with the addition of tested acids were assessed and compared to those dyed with the addition of acetic acid. It was found that the differences in dyeabilities obtained with the addition of citric, oxalic, hydrochloric, nitric and sulphuric acid are entirely acceptable according to both M&S 83A and CMC (2:1) standards in comparison to the dyeability obtained with the addition of acetic acid.

2

The inflammatory reaction and the expression of pro- and anti-inflammatory cytokines to a novel polyester-polyurethane aortic prosthesis evaluated in dog sat 6 and 12 months post-implantation

86%

Mālniece A. , Auzāns A. , Mālniece A. , Auzāns A.

|

3

Surface modification of polyester reinforcing materials by plasma

86%

Hudec I. , Amir I. , Černák M.

|

2010

|

tom Nr 12

97-100

EN

In this work, plasma treatment technique for modification of polyester cords was studied. As result of plasma treatment new morphology of surface layer with different chemical structure and roughness was investigated. These changes may have substantial contribution into increasing of adhesion strength of such treated polyester cords to rubber compound.

PL

Celem pracy było zbadanie wpływu cieczy jonowych na stabilność termiczną i palność gumy. W badaniach wykorzystano następujące ciecze jonowe: tri(pentafluoroetylo)-trifluorofosforan triheksylo(tetradecylo)fosfonowy, tetrafluoroboran l-butylo-2,3-dimetylo-imidazoliowy oraz tri(pentafluoroetylo)trifluorofosforan tetrametylo-amoniowy (Sigma Aldrich), za pomocą których modyfikowano powierzchnię krzemionki, którą następnie napełniano kauczuk, lub spęczniano powierzchnię gumy. Wbrew oczekiwaniom, modyfikacja powierzchni cząstek napełniacza za pomocą cieczy jonowej nie podnosi w istotny sposób stabilności termicznej (T5, T50) ani też wartości wskaźnika tlenowego (Ol) gumy z jego udziałem. Trochę lepiej przedstawia się sytuacja w przypadku powierzchniowej modyfikacji gumy za pomocą cieczy jonowych. Podjęto próby wyjaśnienia tej nieoczekiwanej sytuacji (w literaturze przedmiotu można znaleźć szereg doniesień o uniepalnianiu materiałów, np. drewna, za pomocą cieczy jonowych), badając stopień modyfikacji powierzchni napełniaczy i warstwy wierzchniej gumy oraz morfologię napełnionych wulkanizatów.

4

Varnishes modified with nanoparticles for use in electrical insulation

86%

Górnicka B. , Czołowska B. , Mazurek B. , Zawadzka J. , Górecki L.

|

2007

|

tom T. 52, nr 5

367-370

EN

This paper presents the results of investigation of impregnating polyester varnish modified by incorporation of various nanoparticles: fumed nanosilica, nanosilica and titanium dioxide obtained via sol-gel process, zinc oxide or montmorillonite at loading 1-3 wt. %. The compositions have been formulated using various recipes and methods of preparation of nanoparticles. The processing, mechanical, electrical, barrier and thermal properties have been examined for both basic pure varnish and varnish with nanofillers. Improving of dielectric properties (electrical strength, resistance to pulse voltage) of insulating varnishes is possible by incorporation of nanoparticles. Nanofilled varnishes exhibit also the increased thermal endurance, bond strength and smaller susceptibility to water absorption.

PL

Przedstawiono wyniki badań nasycającego poliestrowego lakieru modyfikowanego na drodze wprowadzenia (w ilościach 1-3% mas.) nanocząstek różnych nanonapełniaczy: krzemionki płomieniowej, krzemionki oraz ditlenku tytanu otrzymanych metodą zol-żel, tlenku cynku albo montmorylonitu. Kompozycje zawierały ponadto środki ułatwiające zwilżanie i dyspergowanie nanonapełniaczy oraz substancje sprzyjające odpowietrzaniu. Oceniono właściwości przetwórcze, mechaniczne, elektryczne, barierowe i cieplne lakieru standardowego bądź zmodyfikowanego (tabela 1-3, rys. 1-4). Stwierdzono, że obecność już niewielkich ilości użytych nanonapełniaczy umożliwia poprawę właściwości dielektrycznych (wytrzymałość elektryczna i trwałość w warunkach działania napięcia impulsowego) poliestrowych lakierów elektroizolacyjnych. Lakiery z nanocząstkami wykazują również wzrost (w stosunku do odpowiedniej wartości lakierów nienapełnionych) odporności cieplnej oraz siły wiążącej jak również mniejszą chłonność wody.

5

Application of short-path thin-film distillation to remove a cyclic ester from a saturated polyester

86%

Kapłon J.

|

2007

|

tom Vol. 28, z. 3

485-491

EN

The results of experimental research concerning removing cyclic ester - lactone from saturated polyester Poles 50/23 have been presented. Short-path, thin-film distillation process was used for removing of lactone from polyester resin, with and without the addition of diethlylene glycol. Fogging tests, determining the tendency for plastic and elastomeric materials to volatize substances which can condense and collect on glass surfaces were made according to DIN 75201. The tests have been made to evaluate materials to be used in automotive or other vehicle interiors. Optimal process parameters which give high product quality were established.

PL

Przedstawiono wyniki badań eksperymentalnych dotyczących usuwania laktonu, cyklicznego estru z poliestru Poles 50/23. Do usuwania laktonu zastosowano proces krótkodrożnej destylacji cienkowar-stwowej, także z dodatkiem glikolu dietylenowego. Produkty destylacji poddano testom na mgławienie, zgodnie normą DIN 75201, określającymi zdolność do uwalniania lotnych substancji z tworzyw sztucznych. Testy te są używane do oceny materiałów używanych we wnętrzach samochodów. Ustalono optymalne parametry procesu, zapewniające uzyskanie produktu o wymaganych właściwościach.

6

Mechanical behaviour of chicken quills and chicken feather fibres reinforced polymeric composites

72%

Uzun M. , Sancak E. , Patel I. , Usta I. , Akalin M. , Yuksek M.

|

2011

|

tom Vol. 52, nr 2

82-86

EN

Purpose: The objective of this study is to utilise and evaluate the mechanical properties of the chicken feather quill and fibre reinforced vinylester and polyester composites. Design/methodology/approach: Prior to production of the composites, the chicken feather fibres (CFF) were cleaned, tested and analyzed in terms of physical properties; linear density and tensile behaviour. The unidirectional CFF reinforced composites were produced with vinylester and polyester resins with three fibre reinforcement loadings (2.5, 6, 10wt%). Following experiments were conducted to determine physical properties of the control (0%) and CFF reinforced composites; tensile, flexural and Charpy impact testing. Findings: It was found that the impact properties of the CFF reinforced composites are significantly better than the control composites however both the tensile and the flexural properties of the CFF reinforced composites have poorer values compared to the control composites. For the 10% CFF reinforced vinylester composite, Charpy impact value was 4.42 kgj/mm2 which was 25% higher than the control vinylester composites (3.31 kgj/mm2) and also for the 10% CFF reinforced polyester (4.56 kgj/mm2) composite had three times better impact resistance than the control composite (1.85 kgj/mm2). Practical implications: The CFF reinforced composite have potential applications due to its improved impact behaviour. Originality/value: If the poultry waste can be utilised and used any engineering applications they will be preferred due to low-cost and superior characteristics and the most importantly they will not cause ecological and health problems.

7

Poli(oksyetyleno-b-tereftalan trimetylenu) : synteza, struktura, degradacja

58%

Rokicka J. , Kotowski D. , Ukielski R.

Przetwórstwo Tworzyw

|

2012

|

tom [R.] 18, nr 6

632-636

PL

Otrzymano poli(estro-b-etery) składające się z poli(tereftalanu trimetylenu) (PTT) jako bloku sztywnego oraz poli(oksyetyleno)diolu (PEG) jako bloku giętkiego. Metodami 1H NMR oraz FTIR potwierdzono zakładaną strukturę kopolimerów. Metodami DSC i DMTA zdefiniowano właściwości termiczne i rozdział fazowy otrzymanych układów. Materiały poddano testom podatności na degradację hydrolityczną w roztworach o pH=4,9; 7; 8,5 oraz na degradację w glebie. Degradację polimerów po 8 tygodniach oceniono mierząc zmianę lepkości istotnej.

EN

New poly(ester-b-ether) multiblock elastomers containing poly(trimethylene terephthalate) hard segments and polyoxyethylene soft segment were prepared and studied by 1H NMR and FTIR methods to confirme their assumed chemical structures and by DSC and DMTA methods to define the phase separation and thermal properties. Materials were subjected to hydrolytic degradation in solutions of pH: 4,9; 7; 8,5; and degradation in soil. The degradation after a period of 8 weeks was measured by the change of intrinsic viscosity of the polymers.

8

Pogłębione utlenianie ścieków włókienniczych z procesu barwienia bawełny, poliestru i poliuretanu

58%

Kos L. , Perkowski J. , Ledakowicz S.

|

2001

|

tom Nr 12

16-18

EN

Research results for dye sewage treatment considering cotton, polyester and polyurethane dyeing by method of deeper oxidation using ozone, hydrogen peroxide and UV radiation.

9

Synthesis of water-soluble macromolecular ligands, their chąracterisation and interactions with metal ions

58%

Tulu M.

|

2000

|

tom Vol. 7, nr 10

1094-1104

EN

Synthesis, characterisation, and application of water-soluble macromolecular ligands (polycondensates) and their interactions with heavy metas were investigated. In this study, the polycondensation of well-known complexing agents; e.g. ethylenediaminetetracacetic acid and diethylenediaminepentaacetic acid with water-soluble polymers, namely poly(ethyleneglycol), PEG4000-7500, and diaminopoly(oxyethylene), JEF2000, were studied. Using different spectroscopic techniques, the molecular size, stability, complexation, and the solubility of the new polycondensates were studied. Water-soluble polyesters with pendant carboxylic groups for removal of the metal ions from the industrial waste water, were synthesised. The removal of Cr(III), Fe(III), Co(II), Ni(II), Cu(II), Zn(II), Sr(II), Cd(II) and Pb(II) was checked with the LPR (Liquid Phase Retention) method. Diamino-poly(oxyethylene) was purified by precipitation with dry diethylether from dry toluene. After precipitation solution was first filtered and dried under vacuum. Molten pure diamino-poly(oxyethylene) was treated with fine crystalline ethylenediaminetetracetic acid dianhydride. The product was dissolved in water and filtered. Membrane filtration system of 300 kPa pressure and a l0 K filter were subsequently involved. The retantate was lyophilised. The polymeric products were soluble in water, acetone, chloroform and toluene, and were characterised by elemental analysis, IR and NMR spectroscopy. In addition, the number of carboxyl groups was determined by titration and the hydrolytic stability studied as a function of pH.

PL

Opisano syntezę, charakterystyki fizykochemiczne i zastosowanie rozpuszczalnych w wodzie ligandów makromolekularnych i ich interakcje z metalami ciężkimi. Zbadano polikondensację dobrze znanych czynników kompleksujących: kwasu etylenodiaminotetraoctowego i kwasu dietylenodiaminopentaoctowego z roz-puszczalnymi w wodzie polimerami, mianowicie: poli(etylenoglikolem), PEG4000-7500 i diaminopoli(oksyetylenem), JEF2000. Do analizy użyto różne techniki spektralne, badano wielkość molekuł, ich stabilność, kompleksację i rozpuszczalność w nowych polikondensatach. Zsyntezowano poliestry rozpuszczalne w wodzie z przyłączonymi grupami karboksylowymi, służące do usuwania jonów metali ciężkich ze ścieków przemysłowych. Usuwanie Cr(III), Fe(III), Co(II), Ni(II), Cu(II), Zn(Il), Sr(II), Cd(lI) i Pb(II) sprawdzono za pomocą metody LPR (Liquid Phase Retention). Diaminopoli(oksyetylen) oczyszczono przez strącanie bezwodnym eterem etylowym z bezwodnego roztworu toluenowego. Po strąceniu mieszaninę przesączono i osuszono w próżni. Do roztopionego czystego diaminopoli(oksyetylen) dodawano drobnokrystalicznego bezwodnika kwasu etylenodiaminotetraoctowego. Następnie produkt rozpuszczano w wodzie, przesączano i filtrowano pod ciśnieniem 300 kPa, stosując filtr 10 K. Pozostałość była liofilizowana. Otrzymane produkty polimerowe były rozpuszczane w wodzie, acetonie, chloroformie i toluenie; scharakteryzowano je za pomocą analizy elementarnej oraz widm IR i NMR. Liczbę grup karboksylowych oznaczono miareczkowaniem, zaś ich odporność na hydrolizę badano w roztworach o różnych wartościach pR.

10

Biodegradacja starzonej kompozycji polietylenu z syntetycznym poliestrem

58%

Łabużek S. , Nowak B. , Pająk J.

|

2006

|

tom T. 51, nr 1

27-32

PL

Zbadano wpływ wstępnego starzenia w warunkach abiotycznych (foto-, termo- i fototermodegradacja) na przebieg powodowanej przez grzyby mikroskopowe Penicillium funiculosum biodegradacji folii wykonanej z mieszaniny 80 % PE-LD i 20 % poliestru "Bionolle®". W celach porównawczych badano też folie wykonane z czystych składników tej mieszaniny. Stopień każdego z badanych rodzajów degradacji oceniano na podstawie pomiarów ubytku masy folii, ich właściwości mechanicznych oraz morfologii powierzchni. Analiza widm IR posłużyła do zinterpretowania spowodowanej degradacją zmiany budowy chemicznej badanej mieszaniny polietylenu i poliestru. Ustalono, że degradacja abiotyczna polimerów intensyfikuje ich biodegradację następczą oraz że dodatek poliestru "Bionolle®" uwrażliwia PE-LD na degradacyjne procesy rozkładu.

EN

The effect of preliminary aging, in abiotic conditions (photo-, thermal or photo-thermal degradation), of the film made of 80 % of PE-LD and 20 % of polyester "Bionolle®" on the course of biodegradation caused by Penicillium funiculosum (filamentous fungi) was investigated. The films made of single components of this mixture (Table 1) were also investigated to compare the results obtained. The degrees of each kind of degradation have been estimated on the basis of changes of film weight loss (Table 2 and 3), the mechanical properties (Table 4) and morphology of the surface (characterized using scanning electron microscopy, Fig. 1 and 2). Changes in chemical structure of polyethylene/polyester blend caused by degradation were interpreted on the basis of IR spectra analysis (Fig. 3-5). It was found that abiotic degradation of the polymers accelerated their subsequent biodegradation and that addition of "Bionolle®" polyester made PE-LD more sensitive to degradation processes.