Characterization of oxide layers made on aluminum alloy 7075 by different methods

100%

Jędrusik M. , Dębowska A. , Kopia A. , Petrzak P. , Koclęga D. , Kalemba-Rec I.

Metallurgy and Foundry Engineering

|

2016

|

tom Vol. 42, no. 3

187--193

EN

Aluminum and aluminum alloys are now being widely used as materials for structural applications due to a number of valuable properties. Improvement in the functional and decorative properties of aluminum can be obtained by forming an oxide layer on its surface. The aim of the present study was to produce and compare the properties of oxide layers on the surface of aluminum alloy 7075 and compare their properties. The methods that were used during the study were as follows: phosphating, micro-arc oxidation, and a chemical method involving the formation of a passive layer. The layers were subjected to corrosion tests. SEM and EDS methods were used for characterization of the received results. Also, some tests on an optical profilometer were done. It was proven that the micro-arc oxidation method allowed us to obtain a layer with the greatest thickness and highest corrosion resistance.

PL

Glin i jego stopy są obecnie powszechnie wykorzystywanym materiałem do zastosowań konstrukcyjnych ze względu stosunek masy do wytrzymałości. Poprawę własności funkcyjnych i dekoracyjnych aluminium uzyskać można przez wytworzenie warstwy tlenku na jego powierzchni. Celem badań było wytworzenie warstw tlenkowych na podłożu ze stopu aluminium 7075 i porównanie ich właściwości. Zastosowano trzy metody: fosforanowanie, micro-arc oxidation oraz metodę chemiczną polegającą na wytworzeniu warstwy pasywnej. Otrzymane powłoki poddano testom korozyjnym oraz charakteryzowano z zastosowaniem następujących metod: SEM, EDS. Wykonano też badania na profilometrze optycznym. Metoda micro-arc oxidation pozwala na uzyskanie warstwy o największej grubości oraz najlepszej odporności na korozję.

2

Wpływ izolacji cząstek proszku RE-M-B na szybkość korozji materiałów wiązanych w zakwaszonym roztworze siarczanowym

100%

Pawłowska G. , Klimecka-Tatar D. , Mazik A.

Ochrona przed Korozją

|

2012

|

tom nr 11

531-533

PL

Przeprowadzano badania nad wpływem bienkapsulacji cząstek proszku Nd(Fe,Co)B, powłokami typu Ni-P/żywica epoksydowa i powłokami fosforan/żywica epoksydowa, na korozyjne zachowanie uzyskiwanych na ich bazie materiałów wiązanych w zakwaszonym środowisku siarczanowym. Powłoki Ni-P wytwarzano bezprądowo z wodnego roztworu soli Ni(II) i pofosforynu sodu w czasie 5, 15 i 30 min. Powłoki fosforanowe otrzymano przez kondycjonowanie proszku w roztworach fosforanowych o pH = 3 i 7. Stwierdzono, że bienkapsulacja poprawia odporność korozyjną materiałów wiązanych, przy czym najkorzystniejsze efekty uzyskano w przypadku powłoki fosforanowej wytworzonej w zakwaszonym środowisku fosforanowym.

EN

The investigation under encapsulation of the Nd(Fe,Co)B powder particles with Ni-P/epoxy resin coatings and phosphate/epoxy resin on the corrosion behavior of bonded materials obtained on their base in the acidified sulphate environment have been carried out. The Ni-P coatings were prepared in electroless bath containing salt of Ni (II) and sodium diphosphite, by 5, 15 and 30 minutes of exposure. The phosphate/epoxy resin coatings were obtained by powder conditioning in phosphate solutions acidified to pH = 3 or 7. It was found that the powder biencapsulation increased the corrosion resistance of the bonded materials, with the best results in the case of the phosphate coatings formed in the acidified phosphate environment.

3

Profilometry surface analysis of bonded magnets based on biencapsulated Nd-(Fe,Co)-B powder

100%

Radomska K. , Pawłowska G. , Klimecka-Tatar D.

|

tom nr 4

142--146

EN

In this paper the detailed evaluation of the bonded magnetic materials surface has been presented. Bonded magnets based on Nd-(Fe,Co)-B powder after biencapsulation with coating (phosphate/epoxy resin, Ni-P/epoxy resin). As a reference material, the bonded magnets based on powder encapsulated with epoxy resin was applied. The aim of this study was to analyze the surface of bonded magnetic materials based on Nd-(Fe,Co)-B subjected to different biencapsulation methods. In the work the measurements of roughness (2D) evaluated with contact profilometer (Taylor Hobson) as well as the surface analysis with SEM Phenom microscope (Labsoft) were performed. It was found that the used biencapsulation methods (especially phosphate/epoxy resin coating) have a positive impact on the surface of the bonded magnetic materials.

PL

W niniejszej pracy dokonano szczegółowej oceny powierzchni wiązanych materiałów magnetycznych Nd-(Fe,Co)-B wytworzonych z proszków po procesie bienkapsulacji powłokami ochronnymi (fosforan/żywica epoksydowa oraz Ni-P/żywica epoksydowa). Jako odnośnik zastosowano materiał po enkapsulacji żywicą epoksydową. Celem niniejszej pracy było dokonanie analizy warstwy wierzchniej wiązanych materiałów magnetycznych na bazie Nd-(Fe,Co)-B poddanych różnym procesom bienkapsulacji. W pracy dokonano pomiaru chropowatości (2D) z użyciem profilometru stykowego (Taylor Hobson) oraz analizę powierzchni na mikroskopie SEM Phenom firmy Labsoft. Stwierdzono, że zastosowane metody bienkapsulacji (zwłaszcza powłoka fosforan/żywica epoksydowa) mają korzystny wpływ na stan powierzchni wiązanych materiałów magnetycznych.