Effect of directional crystallization rate on microtexture of Al-CuAl2 eutectic alloy

100%

Góral A. , Jura J. , Bouzy E. , Bieda M. , Lityńska-Dobrzyńska L.

tom Vol. 51, iss. 4

565-568

The effect of crystallization rate on the microstructure and the orientation relationship of (Al) and CuAl2 phases in the eutectic alloy was investigated using a step-by-step beam scan on the computer controlled transmission electron microscope. The microstructure of this alloy evolves from the approximately parallel lamellar structure into the eutectic colony structure depending on the rate of the crystallization. On the basis of the measurement of the individual orientations in the sections perpendicular to the crystallization direction the orientation maps were constructed. The resulting data enabled to link the microstructure to the orientation relationships between (Al) and CuAl2 phases and the preferred orientations. The dominant orientation relationship identified in all analysed samples was (111)(Al)//(211 1)CuAl2, [1110](Al)//[120]CuAl2. In the small irregular areas the appearance of other orientation relationships has been found.

W pracy badano wpływ szybkości krystalizacji kierunkowej stopu eutektycznego Al-CuAl2 na mikrostrukturę i relację orientacji faz (Al) i CuAl2 w transmisyjnym mikroskopie elektronowym. Mikrostruktura stopu zmienia się wraz z szybkością krystalizacji stopu od w przybliżeniu regularnej płytkowej do kolonii eutektycznych. Na podstawie pomiarów pojedynczych orientacji w przekrojach prostopadłych do kierunku krystalizacji zostały utworzone mapy orientacji, na podstawie których określono wyróżnione orientacje obu faz. Stwierdzono, ze dominujaca relacja orientacji faz jest (111)(Al)//(211)CuAl2, [110](Al)//[120]CuAl2.

Large strain deformation substructures and local crystallography in {100}<001>/{110}<001> aluminium bicrystals

86%

Paul H. , Driver J. H. , Maurice C. , Bijak M.

tom Vol. 51, iss. 1

43-53

Symmetrically oriented bicrystals of pure Al(99.998%) have been deformed in channel-die compression up to strains of 1.5 to correlate the dislocation substructures and the slip system distributions. The study has focused on structure development in f100g<001>/f110g<001> (cube/Goss) – oriented bicrystals with the grain boundary situated parallel to the compression plane. Both orientations have the same nominal Taylor factor and deform macroscopically by the same amount but have stable (Goss) and unstable (cube) micro-deformation behavior. The character of the deformation substructure was determined by systematic local orientation measurements using high resolution EBSD in a SEM-FEG scanning electron microscope and also by transmission electron microscopy (TEM) and the CBED technique at specific locations. The bicrystal deformation analysis shows that the microtexture evolution within neighboring grains is quite different. Very strong deformation banding is observed within crystallites with the unstable orientation, i.e. cube-oriented grain forms classical deformation bands of slightly and strongly dislocated areas. The Goss-oriented grains within bicrystals are more stable under plane strain conditions and do not show any tendency to strain inhomogeneties except for the zone near the grain boundary.

W pracy analizowano umocnieniowe zachowanie się bikryształów Al(99.998%) o orientacji krystalitów {100}<001>/ {110}<001>, odkształcanych w próbie nieswobodnego ściskania do zakresu odkształceń ∼1.5. Granica rozdziału pomiędzy ziarnami usytuowana była równolegle do płaszczyzny ściskania. Obydwa krystality formujące bikryształ scharakteryzowane są tą samą wartością współczynnika Taylora. Jednakże ich zachowanie umocnieniowe jest odmienne, tj. orientacja {110}<001> pozostaje stabilna podczas gdy {100}<001> jest silnie niestabilna. W oparciu o pomiary orientacji lokalnych w TEM a także z wykorzystaniem techniki EBSD w SEM wyposażonym w działo o emisji polowej dokonano charakterystyki mikrostrukturalnej i tekturowej. W krystalicie o orientacji {100}<001> obserwowano formowanie się pasm odkształcenia złożonych z obszarów o wysokiej i niskiej gęstości dyslokacji. Orientacja G{110}<001> pozostawała stabilna nie przejawiając tendencji do formowania pasmowych niejednorodności odkształcenia za wyjątkiem wąskich obszarów w pobliżu granicy pomiędzy ziarnami.