A study of arc and melting efficiency in GTAW process

100%

Orłowicz A. W. , Trytek A.

tom R. 3, nr 8

131--140

A study was conducted on the arc and melting efficiency of the gas tungsten arc welding process. The application of the flow type calorimeter for the measurement of arc efficiency is described. The experiment compared worpice materials (spheroidal graphite cast iron) and varied arc power and travel speed. Arc and melting efficiency was determined as a function of current and travel speed as a function of energy input per unit fusion lenght and as function the product of net arc power and travel speed. A stepwise regression method was used to develop relationship betwen GTAW process parametrs and those of fusion geometry, arc efficiency and melting efficiency for the obtained set.

Praca dotyczy określenia sprawności cieplnej i sprawności topienia łukiem elektrycznym przy zastosowaniu elektrody nietopliwej. Dla określenia sprawności cieplnej stosowano kalorymetr przepływowy. Badania prowadzono na próbkach z niestopowego żeliwa sferoidalnego. Zmieniano moc łuku i prędkość skanowania. Analizowano wpływ natężenia prądu, energii liniowej oraz energii wprowadzonej do nagrzewanego materiału i wpływ prędkości skanowania łukiem elektrycznym na sprawność cieplną i sprawność topienia. Stosując metodę regresji krokowej opracowano zależności ujmujące wpływ parametrów procesu na geometrię nadtopień i współczynniki termiczne procesu GTAW.

Geometry of remeltings and efficiency of the surface remelting process applied to cobalt alloy castings

100%

Mróz M. , Orłowicz W. , Tupaj M.

Archives of Foundry Engineering

2013

tom Vol. 13, iss. 2

95--98

The paper summarises results of measurements of remelting area geometry, thermal efficiency and melting efficiency characterising the surface remelting process applied to castings of MAR-M-509 cobalt alloy. The remelting process was carried out with the use of GTAW (Gas Tungsten Arc Welding) method in protective atmosphere of helium, at the electric current intensity in the range from 100 A to 300 A, and the electric arc scanning velocity vs in the range from 200 mm/min to 800 mm/min. The effect of current intensity and electric arc scanning velocity on geometrical parameters of remeltings, thermal efficiency, and melting efficiency characterising the remelting process has been determined.

Współczynniki termiczne procesu GTAW

80%

Mróz M. , Orłowicz A. W. , Tupaj M.

tom R. 5, nr 17

217-224

W pracy przedstawiono wyniki badań wpływu parametrów technologicznych na sprawność cieplną i sprawność topienia w procesie kształtowania na powierzchni odlewów ze stopu AK 20 nadtopień z zastosowaniem metody Gas Tungsten Arc Welding (GTAW). Do oceny sprawności cieplnej procesu zastosowano kalorymetr przepływowy. Stosowano prędkość skanowania łukiem elektrycznym 200, 400, 600 i 800 mm/min, a natężenie prądu wynosiło 100, 150, 200, 250 i 300 A. Z zastosowaniem metody regresji krokowej ustalono związki pomiędzy parametrami procesu technologicznego, a sprawnością cieplną i sprawnością topienia.

In this work the effect of the Gas Tungsten Arc Welding (GTAW ) process parameters on the arc efficiency and melting efficient was presented. A through-flow calorimeter was employed for thermal measurements. The surface fusion process was performed in argon atmosphere under varied electric arc travel speed (vs =200, 400, 600 and 800mm/min) and current intensity (I = 100, 150, 200, 250 and 300A). Relationships between GTAW process parameters and total heat content of the weld sample, as well as heat input that leads to melting of the weld volume were defined.