The influence of post-deformation annealing temperature on the mechanical properties of low-carbon ferritic steel deformed by the DRECE method

100%

Kowalczyk K.

Materials Science Poland

|

2021

|

tom Vol. 39, No. 3

430--435

EN

The paper presents observations on the mechanical properties characterizing low-carbon steel subjected to deformation by the dual rolls equal channel extrusion (DRECE) method and annealed for 60 min in different temperature variants in the range of 450–700°C. The DRECE process was carried out up to seven passes at ambient temperature. The investigations carried out revealed that the strength of the steel strips increases corresponding to the rise in the number of DRECE passes applied. The yield strength (YS) after seven passes is >2.5 times higher compared to the material in the initial state (before the deformation process). However, the tensile ductility decreased significantly after the DRECE. In order to obtain favorable mechanical properties, the steel strips were subjected to annealing. Our study demonstrates that after being processed by the DRECE method, low-carbon steel can be subjected to low-temperature annealing to ensure that it is endowed with high strength, while maintaining the characteristic good ductility of the material. The results of the research were analyzed in the context of an investigation into the microstructure change, assessed by scanning transmission electron microscopy (STEM), induced in low-carbon steel subjected to the DRECE process and low-temperature annealing.

2

Influence of growth of scale thickness on rate of oxidation of low-carbon steel

100%

Jurasz Z. , Adamaszek K.

Advances in Materials Science

|

2007

|

tom Vol. 7, nr 2(12)

242-246

EN

Influence of growth of scale thickness of oxidised low-carbon steel on rate of oxidation was analysed. To the analysis experimental data were applied. The experiment was conducted in chamber electrical furnace on 12 cylindrical samples made of Arema steel with dimension [fi]20, l=30 mm at 1000°C in air atmosphere. Time of oxidation varied from 10 till 2280 min. After oxidation thickness of scale layer for each sample was measured with accuracy 0.01 mm. The conducted analysis re-veals, that rate of oxidation of tested steel initially courses with linear dependence up to limiting value of scale thickness him =0.44 mm, then with hyperbolic dependence according to parabolic law.

3

Korozja naprężeniowa w blachach grubych w kierunku "z" w środowisku wody morskiej

88%

Mazur M. , Kadłuczka A.

Archiwum Odlewnictwa

|

2006

|

tom R. 6, nr 21/1

409-416

PL

W pracy przedstawiono wyniki obserwacji przebiegu pękania korozyjnego blachy grubej ze stali S 355J2G3 wg normy PN-EN 10027. Stwierdzono równoczesny wpływ naprężeń i wodoru na ten proces.

EN

The modeling of Stress Corrosion Cracking (SCC) is probably one of the most delicate challenges issued to corrosion engineers and scientists. The difficulty is mainly due to the involvement in the global process of three a prior distinct phenomena: crack initiation, crack slow propagation and crack fast propagation. An overview of SCC results in 18G2A steel are presented. The correlation was established between stress corrosion crack rates and hydrogen degradation in crack fast propagation zone.

4

Uszkodzenia elementów kotłów wysokoprężnych wykonanych ze stali niskowęglowych i niskostopowych przy oddziaływaniu wody

75%

Tubielewicz K. , Melechov R. , Dudek P.

Energetyka

|

2002

|

tom nr 6

354-359

PL

Przedstawiono dane z analizy korozyjno-mechanicznych uszkodzeń elementów kotłów wysokoprężnych elektrowni cieplnych i elektrociepłowni, jak również przyczyny i mechanizmy ich powstawania przy oddziaływaniu wody kotłowych. Szczególną uwagę zwrócono na rolę wodoru w wywoływaniu tych uszkodzeń oraz warunków termodynamicznych układów metal-środowisko.

EN

There are presented data from the analysis of corrosion and mechanical failures of elements of HP boilers in thermal power stations and CHP stations. Reasons and mechanisms of the failure occurrence under water influence are also presented. Special attention is paid to a role of the hydrogen in the failures and thermodynamic conditions of the metal-environment system.

5

Makrostruktura i plastyczność na gorąco wlewków ciągłych ze stali niskowęglowej przeznaczonej na druty spawalnicze

75%

Herian J. , Kudliński Z. , Płachta A.

|

tom Vol. 77, nr 7

319-321

PL

Za pomocą badań metodami głębokiego trawienia i próby Baumana wykazano, że jakość wlewków ciągłych ze stali niskowęglowej stosowanych do walcowania walcówki będącej wsadem do produkcji drutów spawalniczych, jest zależna od warunków odlewania i sposobu krzepnięcia. Badania plastyczności stali o strukturze pierwotnej oceniono w próbie skręcania na gorąco w zakresie temperatury od 800 do 1100 °C i szybkości odkształcenia od 0,1 do 10,0 s-1. Stwierdzono wysoką podatność stali do przeróbki plastycznej w analizowanym zakresie zmienności parametrów dkształcenia.

EN

It was proved by the deep etching and Baumann tests that the quality of continuous cast low-carbon steel billets used for rolling welding wire depends on casting and solidification conditions. Hot torsion tests of the steel in the as-cast state were carried out in the temperature range from 800 °C to 1100 °C and strain rate range from 0.10 to 10.0 s-1. It was found out that the investigated steel exhibits good formability in the analyzed range of deformation conditions.

6

Badania strukturalne mechanizmu odkształcenia na zimno stali specjalnych

75%

Stępień J. , Wojtas J.

|

2006

|

tom T. 58, nr 3

57-60

PL

Zgniatanie obrotowe na zimno stali niskowęglowej chromowo-manganowo-molibdenowo-wanadowej stosuje się w celu uzyskania w wyrobie gotowym struktury ultra drobnoziarnistej. W pracy po zgniataniu obrotowym uzyskano w wyrobie strukturę silnie rozdrobnionego martenzytu listwowego umocnionego wydzieleniami i pasmami odkształcenia ułożonymi przestrzenie w wielu kierunkach. Na podstawie przeprowadzonych badań strukturalnych stwierdzono, że struktura w wyrobach ze stali EŻP jest bardziej jednorodna i bardziej rozdrobniona niż struktura wyrobów ze stali VAD.

EN

The cold roll flowing of low-carbon chromium-manganese-molybdenum-vanadium steel is used to obtain the ultra-fine grained structure in the finished product. As a result of roll flowing, the structure of highly refined strip martensite strengthened with precipitations and deformation bands, arranged spatially in many different directions, was obtained in the product. On the basis of the structural tests it was found that the structure of ESR steel products was more homogeneous and refined than the structure of VAD steel products.

7

Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel

75%

Long X. Y. , Branco R. , Macek W. , Nejad R. M. , Lesiuk G. , Zhu S. P. , Amaro A. M.

|

2023

|

tom Vol. 23, no. 3

art. no. e201, 2023

EN

This paper examined the cyclic deformation behaviour of multiphase low-carbon steel that was subjected to austempering heat treatments at four temperatures (190 °C, 230 °C, 275 °C, and 315 °C) below the martensite start temperature (Ms = 353 °C). The tests were conducted at room temperature, under fully reversed strain-controlled conditions, with strain amplitudes in the range 0.5–1.0%. The microstructure was observed by transmission electron microscopy, and the fracture surfaces were examined by scanning electron microscopy. The steel had a bainite/martensite microstructure, with increasing bainite content for higher austempering temperatures. Irrespective of the tested conditions, it strain-hardened during the first two cycles and then, strain-softened until failure. The austempering temperature did not significantly affect the stress-based, strain-based and energy-based relationships. However, lower austempering temperatures slightly improved the fatigue performance.

8

Opracowanie parametrów technologii walcowania regulowanego blach ze stali niskowęglowej i ze stali typu IFf w warunkach półprzemysłowych oraz wykonanie badań symulacyjnych w LPS

75%

Woźniak D. , Gawor J. , Palus R. , Adamczyk M. , Galisz U.

|

2011

|

tom T. 63, nr 2

69-73

PL

Celem pracy było opracowanie parametrów niskotemperaturowego walcowania w zakresie ferrytycznym stali z grupy IF i regulowanego walcowania z obróbką cieplnoplastyczną niskowęglowych stali konstrukcyjnych i przeprowadzenie prób walcowania eksperymentalnego w LPS. Do walcowania wytypowano stal IF i 3 gatunki stali niskowęglowych z mikrododatkami Nb, Ti, V o zawartości węgla od 0,06 do 0,15 % wytopione w warunkach laboratoryjnych IMŻ i 3 gatunki w postaci odcinków blach o grubości od 40 i 44 mm ze stali S355, S420 i S500MC pobranych z blach walcowanych w warunkach przemysłowych. W wyniku stwierdzono, że blachy ze stali IF walcowane przy obniżonej temperaturze w zakresie ferrytycznym spełniają wymagane właściwości, a badania blach ze stali niskowęglowych należy kontynuować stosując wyższe temperatury końca walcowania i chłodzenie natryskiem wodnym po walcowaniu o parametrach zależnych od gatunku stali i grubości blachy.

EN

The purpose of the work was to develop parameters of low-temperature ferritic rolling of IF steels and controlled rolling with thermoplastic treatment of low-carbon constructional steels as well as to carry out the experimental rolling in LPS. For rolling the IF steel, 3 grades of low-carbon steel with micro-additives of Nb, Ti, V and carbon content ranging from 0.06 to 0.15%, cast under the Institute for Ferrous Metallurgy's laboratory conditions, and 3 grades in the form of S355, S420 and S500MC steel plate sections with thickness from 40 and 44 mm, taken from plates rolled under the industrial conditions, were selected. As a result, it was found that IF steels put to ferritic rolling at a reduced temperature met the required properties, while the investigations on low-carbon steel plates should be continued by using higher temperatures at the end of rolling and water spray cooling after rolling with parameters dependent on steel grade and plate thickness.

9

Local laser marking - new technology in the identification of steel parts

75%

Kalincsák Z. , Takács J. G. , Sólyomvári K. , Göndöcs B. , Nagy G. C.

Eksploatacja i Niezawodność

|

2007

|

tom nr 3

19-22

EN

The importance of identification of machines in the field of maintenance becomes more and more significant. In the field of mechanical maintenance or especially in large-scale production serious difficulties cause to identify various metal parts which have similar form and/or size during technological process. The paper based and printed barcode seemed a safe resolution to this purpose. Unfortunately during the repairing or renewal process the paper based barcodes of steel parts very often were destroyed or damaged, the currently applied paper based and painted codes can cause data losses. This is the fact which indicated the research of steel marking system. In this type of marking the material contains the signs. Other advantage of this system is the readability beneath from painted layer.

10

Nawęglanie laserowe stali niskowęglowych

75%

Buczma D.

Journal of Research and Applications in Agricultural Engineering

|

2005

|

tom Vol. 50, nr 2

49-53

PL

Przedmiotem prezentowanych badań były próbki ze stali 14MnCr5 na sworznie silników tłokowych, nawęglone laserowo. Stosowane w tłokach sworznie są nawęglane dyfuzyjnie, a więc w głąb ich warstwy wierzchniej silnie maleje zawartość węgla i tym samym mikrotwardość. Wprowadzenie węgla w warstwę powierzchniową próbek ze stali niskowęglowej (14MnCr5) poprzez stopowanie laserowe może doprowadzić do równomiernego stężenia węgla w przetopionej warstwie. W pracy przedstawiono wyniki badań potwierdzające to założenie, a także zaprezentowano zależności efektów stopowania laserowego od warunków jego realizacji.

EN

Laser carbonizing of piston engine pins samples made with 14MnCr5 steel has been the subject matter of presented investigation. Diffusive carbonization method is used in piston pins case usually. Thus carbon amount is decreasing with distance from the surface (hardness is decreasing as well). Steady carbon concentration in melted zone could be achieved by carbon implantation on 14MnCr5 low-carbon steel with laser alloying method. Investigation results confirmed statement presented above. Additionally correlation between laser alloying effects and conditions of this process has been showed.

11

Investigation of reasons for damage to a steel pipeline used for the injection of formation waters

75%

Jachym R. , Gotkowski P. , Gazdowicz J.

|

tom Vol. 64, No. 3

29--35

EN

The article presents results of test concerning reasons for the failure of a steel pipeline (DN 80) used for the injection of formation waters. The tests revealed that the perforation and subsequent material losses in the wall of the DN 80 pipeline made of steel L360NB were caused by deposit corrosion.

PL

Przedstawiono wyniki badań przyczyń awarii rurociągu stalowego DN 80 stosowanego do zatłaczania wód złożowych. Na podstawie przeprowadzonych badań stwierdzono, że przyczyną wystąpienia perforacji oraz kolejnych ubytków materiału w ściance rurociągu DN 80 wykonanej ze stali L360NB była korozja podosadowa.

12

Opracowanie technologicznych podstaw wytwarzania blach grubych wysokowytrzymałych do zastosowań w niskich temperaturach

75%

Gawor J. , Woźniak D.

|

2012

|

tom T. 64, nr 3

27-35

PL

Decydujący wpływ na poziom właściwości mechanicznych stali wywierają parametry przeróbki cieplno-plastycznej i szybkości chłodzenia po przeróbce. Właściwości stali mogą się istotnie zmieniać w zależności od wielkości odkształcenia w końcowych przepustach, temperatury końca walcowania oraz szybkości chłodzenia po walcowaniu. Celem badań było opracowanie półprzemysłowej technologii wytwarzania blach grubych wysokowytrzymałych ze stali niskowęglowych konstrukcyjnych przeznaczonych do zastosowań w obniżonych temperaturach. Wytypowano składy chemiczne stali, określono wstępne parametry procesu i przeprowadzono próby walcowania blach z obróbką cieplno-plastyczną i regulowanym chłodzeniem bezpośrednio po walcowaniu w module B Linii do Półprzemysłowej Symulacji Wytwarzania Metali i Stopów (LPS) budowanej w Instytucie Metalurgii Żelaza. Walcowano stale niskowęglowe o zróżnicowanej zawartości C, Mn i mikrododatków Nb, Ti, V o wartości równoważnika węgla w zakresie 0,36 do 0,50. Wykonano badania właściwości mechanicznych, udarności KV w zakresie temperatur od 20 do -60o C i mikrostruktury. Założoną do osiągnięcia wartość udarności KVmin = 27 J w temperaturze badania -60 C uzyskano dla blach o grubości 6÷7,5 mm. Mikrostruktura tych blach jest drobnoziarnista ferrytyczno-perlityczno-bainityczna, a ich właściwości spełniają wymagania dla kategorii S420ML i S460ML.

EN

The decisive effect on mechanical properties of steel is exerted by the parameters of thermo-mechanical treatment and rate of cooling after treatment. Steel properties can significantly vary depending on the volume of strain in final passes, end-of-rolling temperature and rate of cooling after rolling. The purpose of the research was to develop the semi-industrial technology for manufacturing of high-strength metal plates from low-carbon constructional steels for applications at reduced temperatures. Chemical compositions of steels were selected, initial process parameters were determined and testing of plate rolling with thermo-mechanical treatment and controlled cooling immediately after rolling in module B of the semi-industrial line for simulation of manufacturing metal and alloy products (LPS) being built in the Institute for Ferrous Metallurgy was carried out. Low-carbon steels with diverse content of C, Mn and micro-additions of Nb, Ti, V with carbon equivalent varying between 0.36 and 0.50 were rolled. The investigations of mechanical properties, impact resistance KV within the temperature range from 20 to -60° C and microstructure were carried out. The assumed impact resistance KVmin = 27 J at test temperature of -60° C was obtained for metal plates 6÷7.5 mm thick. These plates have fi ne-grained ferritic-pearlitic-bainitic microstructure and their properties meet the requirements for S420ML and S460ML category.

13

Analysis of fillet weld leg length in a low-carbon steel

63%

Ghazvinloo H. R.

|

2024

|

tom Vol. 125, nr 2

58--64

EN

Purpose: The present article analysed the effect of MAG welding parameters (arc voltage-AV, wire feeding speed-WFS, and welding speed-WS) on fillet weld leg length (FWLL) in low-carbon steel S235JR. Design/methodology/approach: In the research, the Taguchi L8 orthogonal array was used to design experiments. The eight experimental experiments were designed based on the Taguchi method, and the average FWLL was measured in each experiment. The analysis of means (ANOM) and analysis of variance (ANOVA) techniques were used to analyse FWLL. Findings: The highest F-value in ANOVA analysis (96.08) confirmed that the welding speed is the most effective parameter on the response (with a per cent contribution of 92.24%), followed by wire feeding speed and arc voltage, with an F-value of 2.82 and 1.25, respectively. Research limitations/implications: The research was focused on MAG welding as a common process used in different industries. Future studies could consider the effect of parameters on fillet weld leg length in other arc welding processes. Due to its many applications in various industries, the low-carbon steel S235JR plate was chosen as the base material, while other steels can be used for future studies. Practical implications: The findings of the present study have significant practical implications for the welding industry. The design of welding joints is a very important part of the design of metal structures. A weld bead with correct and optimal sizes is desirable and accepted in the design of metal structures. The findings of the present study can be used in the optimal design of fillet welds for low-carbon steel. Originality/value: As far as we know, there is relatively little information on the proper balance of fillet weld leg length in low-carbon steels. Therefore, the research results can be used in the appropriate design of welding joints for low-carbon steels.

14

Własności mechaniczne stali niskowęglowych z manganem, krzemem i miedzią po izotermicznym wyżarzaniu w zakresie 400-700 stopni C

63%

Kruk A. , Osuch W. , Michta G. , Ciura F.

Hutnik, Wiadomości Hutnicze

|

2007

|

tom Vol. 74, nr 11

601-607

PL

W pracy przedstawiono wyniki badań własności mechanicznych dla dwu wytopów stali nisko węglowej: zawierającej mangan i krzem (0,2 %C, 1,5 %Mn, 1,5 %Si), oraz mangan, krzem i miedź (0,2 %C, 1,5 %Mn, 1,5 %Si, 1,0% Cu). Badania prowadzono po chłodzeniu z zakresu dwufazowego i przemianie izotermicznej przebiegającej przy temperaturach z zakresu 400-700 °C. Własności mechaniczne po przemianie perlitycznej (500-650 °C) były zbliżone, natomiast próbki, w których strukturze pozostawał jeszcze austenit, charakteryzowały się niższą granicą plastyczności i wyższą wytrzymałością na rozciąganie (wyższy stosunek Rm/Re) Odmiennie zachowywały się również próbki po przemianie izotermicznej przy najwyższej temperaturze (700 °C). Kształt krzywych rozciągania i zmiany chwilowego wykładnika umocnienia wskazywały na obecność w strukturze austenitu (potwierdzono to również badaniami magnetycznymi). Próbki te wykazywały własności podobne do tych po przemianie w dolnym zakresie temperatur (poniżej 450 °C).

EN

In this paper results of mechanical properties measurement for two melting's of low-carbon steel containing manganese and silicon (0.2 %C, 1.5 %Mn, 1.5 %Si), and manganese, silicon and copper (0.2 %C, 1.5 %Mn, 1.5 %Si 1.0 %Cu) are presented. Research were performed after cooling from the two-phase range and the isothermal transformation proceeded in the temperature range from 400 to700 °C. Mechanical properties after the pearlitic (500-650 °C) transformation were similar, however samples, the structure of which stayed still the austenite range were characterized with the lower yield stress and with the higher tensile strength (the higher Rm/Re ratio). In a different manner behaved also samples after the transformation in the highest temperature (700 °C). The shape of curves and changes of the instantaneous strengthening exponent indicated the presence of austenite in the structure (it was confirmed also by magnetic investigations). These samples showed similar properties to those transformed in the low temperature range (below 450 °C).

15

Simulation of fatigue process

63%

Kuffova M.

|

tom Vol. 27, no. 3

110-112

EN

In the paper are shown the results of fatigue crack propagation in the microstructure of material and the dependence da/dN - DKapl by finite - element software ADINA. These results are confronted with the results of fatigue tests. The aim was to elaborate on the crack initiation and growth in the microstructure containing a stress concentrator and redistribution of stress during propagation.

PL

W artykule pokazano wyniki propagacji pęknięć zmęczeniowych w mikrostrukturze materiału oraz zależności da/dN - DKapl uzyskanych metodą elementów skończonych w pakiecie ADINA. Wyniki te porównano z rezultatami laboratoryjnych badań zmęczeniowych. Celem było wypracowanie pęknięcia inicjującego i jego rozwinięcie w mikrostrukturze z koncentratorem naprężeń oraz obserwowanie zmian rozkładu naprężeń w trakcie propagacji pęknięcia.

16

Production of seamless pipes grade X65 according to API 5L

63%

Bar J. , Melecki J.

Hutnik, Wiadomości Hutnicze

|

2008

|

tom Vol. 75, nr 8

460-462

EN

This paper presents the project, which solved development and verification of production of line pipes grade X65 PSL2 according to API 5L. The authors describe basic period of solution: design chemical composition of steel, steel making, continuous casting and line pipes production. The pipes were quenched and tempered according to requirement of specification. Final properties of line pipes (yield strength, tensile strength, ductility, notch toughness) were attested. All mechanical values matched the requirements for grade X65 PSL2. The line pipes may be used for sour service.

PL

W artykule zaprezentowano projekt, którego celem było opracowanie i weryfikacja technologii produkcji rurze stali X65 PSL2 zgodnie z normą API 5L. Autorzy opisują zasadnicze etapy rozwiązania problemu: zaprojektowanie składu chemicznego stali, wytworzenie stali, proces ciągłego odlewania stali oraz produkcję rur Rury były chłodzone oraz hartowane zgodnie z wymaganymi warunkami. Końcowe właściwości rur przewodowych (umowna granica plastyczności, wytrzymałość na rozciąganie, plastyczność, udarność) zostały potwierdzone w badaniach. Właściwości mechaniczne były zgodne z wymaganiami dla stali X65 PSL2. Rury przewodowe mogą być zastosowane w przemyśle chemicznym, naftowym (do transportu cieczy agresywnych).

17

Reduction macrosedregation in concast slabs of deep drawing steel

63%

Gawor J. , Paduch J.

Archives of Metallurgy and Materials

|

2007

|

tom Vol. 52, iss. 1

135-142

EN

Results of laboratory and industrial tests related to development and implementation of the comprehensive technology of production and continuous casting of Bw11 low carbon steel for cold drawing of special products are presented. The aim of material tests was to assess the impact of the applied technological processes on reduction of central macrosegregation in slabs and plates. Segregation of alloying elements and impurities in steel, occurring during the process of concast slab solidification, results in formation of the central segregation zone. In heavy plates rolled from concast slabs, the zone is disclosed during the deep etch test, and constitutes material faults which disqualifies plates from application for cartridge cases. In the segregation band of higher hardness, revealed by means of the Oberhoffer’s reagent, intensified pearlite banding, characteristic strips of fine pearlite and numerous non-metallic inclusions – mostly elongated MnS sulphides, were found. In order to reduce central segregation in concast slabs, the following treatments were performed: – reduction of P and S content in steel, – modification of non-metallic inclusions by means of Ca addition, – using Ti and B microadditives for the purpose of modification of steel solidification structure, – reduction of the degree of steel overheating prior to casting, – increasing intensity of concast slabs cooling, – soft reduction of concast slab in the final phase of solidification. By means of the standard technology modified in the above manner, plates without the central segregation were manufactured in the steel plant (Huta Stali Czestochowa). The produced plates fulfil conditions of the acceptance test specifications, moreover, their usability was verified by means of laboratory press forming tests as well as tests of industrial cartridge casing forming.

PL

W niniejszej publikacji przedstawiono wyniki badań laboratoryjnych i przemysłowych, związanych z opracowaniem i wdrożeniem kompleksowej technologii wytwarzania i odlewania ciągłego stali niskowęglowej Bw11, przeznaczonej do tłoczenia na zimno wyrobów specjalnych. Celem badań materiałowych była ocena wpływu zastosowanych procesów technologicznych na redukcję makrosegregacji środkowej we wlewkach i blachach. Zachodząca podczas krzepnięcia wlewka ciągłego segregacja pierwiastków stopowych i zanieczyszczeń zawartych w stali powoduje utworzenie środkowej strefy pasm segregacyjnych. W blachach grubych walcowanych z wlewków ciągłych strefa ta ujawnia się podczas próby głębokiego trawienia i stanowi wadę dyskwalifikujacą blachy do zastosowań na łuski amunicyjne. W paśmie segregacyjnym, o podwyższonej twardości, ujawnianym za pomocą odczynnika Oberhoffera, stwierdzono zintensyfikowaną pasmowość perlitu, charakterystyczne pasemka drobnopłytkowego perlitu oraz liczne wtrącenia niemetaliczne, w głównej mierze wydłużone siarczki MnS. W celu ograniczenia segregacji środkowej w wlewkach ciągłych zastosowano: – ograniczenie poziomu P i S w stali, – modyfikacje wtrąceń niemetalicznych za pomocą wapnia, – mikrododatki Ti i B w celu modyfikacji struktury krzepnięcia stali, – zmniejszenie stopnia przegrzania stali przed odlewaniem, – zwiększenie intensywności chłodzenia wlewków ciągłych, – zabieg miękkiego dogniatania wlewka ciągłego w ostatniej fazie krzepnięcia. Za pomocą tak zmodyfikowanej technologii wytworzono w Hucie Stali Częstochowa blachy bez segregacji środkowej, które spełniły wymagania odbiorowe, a ich przydatność została zweryfikowana za pomocą laboratoryjnych prób tłoczności oraz prób przemysłowego tłoczenia łusek.

18

Nawęglanie próżniowe stali niskostopowej DC04 w atmosferze węglowodorów alifatycznych

63%

Hermanowicz P. , Smolik J.

Problemy Eksploatacji

|

2008

|

tom nr 1

21-34

PL

W artykule przedstawiono wyniki projektowania parametrów technologicznych procesu nawęglania próżniowego stali niskowęglowej DC4 w celu uzyskania założonych parametrów warstwy nawęglanej, tj. powierzchniowego stężenia węgla IcSurf, efektywnego stężenia węgla IcEfect oraz efektywnej grubości warstwy nawęglanej DcEfect. Proces projektowania parametrów technologicznych nawęglania próżniowego przeprowadzono z wykorzystaniem pakietu symulacyjnego SimVac Plus v.2.7.3(EN). Dla otrzymanych warstw nawęglanych przeprowadzono badania zmian zawartości węgla (GDOES) oraz rozkłady zmian twardości (Vickers) w funkcji odległości od powierzchni. Dokonano porównania rzeczywistych zmian zawartości węgla w wytworzonych warstwach nawęglanych ze zmianami wyznaczonymi w procesie symulacji. Dla wytworzonych warstw nawęglanych przeprowadzono również analizę zmian twardości w funkcji odległości od powierzchni, na podstawie której określono przedziały twardości uzyskiwane w stali DC4 dla danej wartości stężenia węgla i parametrów obróbki cieplnej.

EN

This paper presents the results of the research work concerning the design of the vacuum carburising processes of low carbon steel grade DC4, in order to obtain the required parameters of carburising zone, i.e. surface concentration of carbon IcSurf, efficient concentration of carbon IcEfect and the efficient thickness of carburising zone DcEfect. The special simulation software SimVac Plus v.2.7.3(EN) was used in this research. For all the investigated structures, the authors carried out chemical composition analysis with the use of the GDOS method and hardness patterns in the changes of depth of the carburising zone with the use of the Vickers method. The results of investigations into chemical composition of carbon were compared with the results obtained by the simulation method. The authors carried out the analysis of the range of hardness of low carbon steel grade DC4, which was obtained for different chemical compositions of carbon and for the selected parameters of heat treatment.

19

Odkształcalność graniczna niskowęglowych, ocynkowanych elektrolitycznie stali głębokotłocznych.

63%

Frącz W. , Stachowicz F.

Rudy i Metale Nieżelazne

|

1999

|

tom R. 44, nr 11

617-621

PL

Badaniom poddano elektrolitycznie ocynkowane, stalowe blachy głębokotłoczne. Krzywe odkształcalności granicznej (KOG) dla tych materiałów określono doświadczalnie oraz teoretycznie. Obliczenia przeprowadzono na podstawie modeli Hilla-Swifta, Marciniaka-Kuczyńskiego oraz Singa-Rao. Najlepszą zgodność z wynikami badań doświadczalnych wykazują KOG wyznaczone na podstawie aproksymowanej prostoliniową zależnością krzywej naprężeń granicznych (KNG). Do wyznaczenia krzywej odkształcalności granicznej przy pękaniu powłoki (KOGP) wykorzystano wyniki ilościowej mikroanalizy rentgenowskiej zawartości widma Fe na powierzchni powłoki. Jako kryterium do obliczenia teoretycznej KOGP uwzględniono postępującą wraz z odkształceniem zmianę grubości, zarówno samej powłoki cynkowej, jak i materiału bazowego.

EN

Forming limit curves of deep drawn steel sheets have been determined experimentally and calculated on the base of the material tensile properties following the Hill, Swift, Marciniak-Kuczyński and Sing-Rao methods. Only the FLC modeled from a singly linear forming limit stress curve exhibits good agreement with experimental curve. The quantitative X-ray microanalysis of the Fe contents in the sheet surface layer composition was used to determine cracking limit curve (CLC) of electro-galvanized steel sheet. The change in zinc layer (and base sheet metal) thickness was used as a criterion in calculation of the CLC.

20

Struktura i własności mechaniczne niskowęglowej stali C-Mn-V po obróbce cieplno-plastycznej

63%

Lis A. , Lis J. , Wieczorek P.

Hutnik, Wiadomości Hutnicze

|

2008

|

tom Vol. 75, nr 6

299-304

PL

Za pomocą przedstawionych wzorów oszacowano ewolucję struktury austenitycznej w czasie walcowania blach o grubości 12 mm z kontrolowaną rekrystalizacją ze stali niskowęglowej z mikrododatkiem wanadu i podwyższoną zawartością azotu (16 MnV6). Dokonano oceny rekrystalizacji między przepustami oraz wielkości ziarna po walcowaniu z przyspieszonym chłodzeniem. Otrzymano drobnoziarnistą strukturę ferrytyczno-perlityczną, która rekompensuje niekorzystny wpływ umocnienia wydzieleniowego na temperaturę przejściowej kruchości w badanej stali. Pozwoliło to na uzyskanie wysokiej wytrzymałości - Remm=540 MPa, Rm >675 MPa i dobrej ciągliwości - A =23 %, w blachach ze stali 16 MnV6.

EN

Using equations presented in the paper the evolution of the austenitic structure during recrystallization rolling 12 mm plates made from low-carbon steel with microaddition of Vand increased nitrogen content (16MnV6) was estimated. Recrystallization between passes and grain size after rolling with accelerated cooling was evaluated. Fine grained ferrite-pearlite structure was obtained which compensate detrimental effect of precipitation strengthening on impact transision temperature in the tested steel. This allowed to obtain high strength - Remm=540 MPa, Rm>675 MPa and advantageous elongation - A5=23 %for 16 MnV6 steel plates.