Wyniki wyszukiwania - Biblioteka Nauki

1

The Properties and Microstructure of AlTi6/Al2O3 Joints

100%

Sulima I. , Mikułowski B.

|

tom R. 60, nr 4

151--156

EN

The influence of the titanium addition into aluminium on the bond strength properties and structure of interface of the AlTi6/Al2O3 joints was investigated. The bond strength of the metal/Al2O3 joints was determined by the push-off test. Addition of 5.9 wt.%. Ti to Al caused the reduction of shear strength of the AlTi6/Al2O3 joints. The investigations by mean of electron microscopy equipped with a spectrometric system for microanalysis of the chemical composition revealed TiAl3 phases formed at the AlTi6/Al2O3 interface. Oxygen was detected in some areas of TiAl3 phases. Finally, this structure of the AlTi6/Al2O3 interface was responsible for lower bond strength comparing to properties of the Al/Al2O3 joints.

PL

W pracy przedstawiono badania dotyczące wpływu dodatku tytanu do aluminium na wytrzymałość na ścinanie oraz mikrostrukturę połączenia AlTi6/Al2O3. Wyniki wykazały, że dodanie tytanu do aluminium wpływa na obniżenie wytrzymałość na ścinanie badanego połączenia. Badania mikrostrukturalne (SEM oraz TEM) połączone z analizą składu chemicznego wykazały powstanie wydzieleń fazy TiAl3 na granicy rozdziału połączenia. W obszarach fazy TiAl3 obserwowano obecność tlenu. Tworzenie nowych faz na granicy rozdziału połączenie AlTi6/Al2O3 odpowiada za obniżenie wytrzymałości w porównaniu z połączeniem Al/Al2O3.

2

Zwilżalność i granica rozdziału w układzie Al/AlN

84%

Książek M. , Sobczak N. , Stobierski L. , Lis J. , Morgiel J. , Radziwiłł W.

|

tom R. 45, nr 1

8-13

PL

Przedstawiono rezultaty eksperymentalnej analizy procesu zwilżania podłoża z AIN przez ciekłe Al połączonej ze szczegółową analizą strukturalną granicy rozdziału powstającego połączenia. Metodą kropli leżącej przeprowadzono badania kinetyki zwilżania podłoża z AIN przez Al i jego stop AlTi6 w temperaturze 1173 i 1273 K w warunkach próżni dynamicznej rzędu 1 MPa. Badania struktury i składu chemicznego granicy rozdziału pomiędzy kroplą metalu i podłożem wykonano metodą transmisyjnej mikroskopii elektronowej. Przedstawiono analizę porównawczą otrzymanych wyników z danymi uzyskanymi w innych laboratoriach badawczych, biorąc pod uwagę wpływ na specyfikę oddziaływania w badanym układzie takich czynników jak: temperatura i czas oddziaływania, technologiczne parametry syntezy podłoża AIN, zastosowana procedura do badań zwilżalności oraz wpływ dodatku Ti do aluminium.

EN

Aluminum nitride belongs to the family of advanced engineering ceramics because it offers the attractive combination of physical and mechanical properties. The information concerning the interaction of aluminum nitride with liquid metals and alloys is of great interest in the terms of such practical applications as brazing AlN and production of composite materials. The paper reports the results of the study of wetting behaviour of the Al/AlN system coupled with detailed structural examination of the Al/AlN interfaces. Applying the sessile drop method the wettability of aluminum nitride substrate by Al and its AlTi6 alloy was investigated at a temperature of 1173 and 1273 K under dynamic vacuum of 2 x 10 hPa. The structure and chemistry of interfaces in die drop/substrate couples were characterised by transmission electron microscopy. The experimental data are analysed and compared with those data obtained in different laboratories taking into account such factors as temperature and time of interaction, processing parameters for sintering A1N substrates, applied procedure for wettability tests and Ti addition to aluminum.

3

Polimerowo-węglowy kompozyt dla sterowanej regeneracji tkanek

67%

Pamuła E. , Błażewicz M. , Chomyszyn-Gajewska M.

|

2000

|

tom R. 3, nr 10

3--8

PL

Leczenie chorób przyzębia techniką kontrolowanej regeneracji tkanek wymaga od implantu, aby pełnił rolę membrany odizolowującej komórki tkanki łącznej i nabłonka dziąsła od miejsca gojenia i umożliwiał komórkom ozębnej repopulację i utworzenie cementu korzeniowego z wbudowanymi włóknami kolagenowymi. W stomatologii obserwuje się coraz większe zainteresowanie implantami membranowymi do leczenia chorób przyzębia. Znanych jest wiele materiałów organicznych resorbowalnych i nieresorbowalnych, z których wytwarza się implanty dla sterowanej rekonstrukcji tkanek. W pracy przedstawiono próbę otrzymania trójfazowego implantu będącego połączeniem dwóch biozgodnych składników a mianowicie: włókniny węglowej i poli-L-laktydu. Zewnętrzną część implantu stanowi błona polimerowa będąca barierą dla niepożądanych komórek nabłonka zaś wewnętrzna część zbudowana jest z włókien węglowych stymulujących proces regeneracji tkanki kostnej. Implant polimerowo-węglowy został poddany badaniom przy zastosowaniu metod: FTIR, SEM i DSC co pozwoliło na charakterystykę jego budowy chemicznej i morfologii, natomiast inkubacja próbek w sztucznym płynie ustrojowym dostarczyła danych o trwałości implantu w warunkach in vitro.

EN

In the treatment of parodontopathy by guided tissue regeneration, it is required that the implant should play a role of a membrane that separates the connective tissue and gingival epithelium from the healing site. It should also permit repopulation of the periodontium cells along with formation of tooth root cement with the collagen fibres. In stomatology the interest in membrane implants for the treatment of parodontopathy continually increases: There are many resorbable and non-resorbable organic materials used as implants in guided tissue reconstruction. This work is an attempt to develop a three-phase implant being a combination of two biocompatible components, i.e. carbon felt and poly-L-lactide. The outer part of the implant is built of a polymeric membrane, a barrier for undesirable gingival epithelium cells, while the inner part consists of carbon fibres that stimulate the process of bone tissue regeneration. The polymer-carbon implant was examined using FTIR, SEM; and DSC, to characterise its chemistry and morphology, while incubation of samples in simulated body fluid provided the data on their stability in the in vitro conditions.