Elektrochemiczna aktywacja ekspandowanego grafitu

100%

Krawczyk P. , Skowroński J. M.

Przemysł Chemiczny

|

2006

|

tom T. 85, nr 8-9

1198-1200

PL

Zbadano wpływ elektrochemicznej aktywacji elektrody wykonanej z ekspandowanego grafitu na przebieg procesu elektrochemicznego utleniania fenolu. W wyniku potencjostatycznej aktywacji, prowadzonej w środowisku 0,5 M KOH aktywność elektrochemiczna badanej elektrody znacznie wzrosła, zarówno w pierwszym, jak i w kolejnych cyklach utleniania fenolu w porównaniu z oryginalnym ekspandowanym grafitem.

EN

Intercalating H2SO4.IEG compd. prepd. by anodic oxidn. of natural graphite in 18 M H2SO4, was exfoliated 5 min at 800°C in air. The EG electrode was oxidized 1.5 hr. in 0.5 KOH at 1.2 V. PhOH, 0.1 M in 0.5 M KOH, was oxidized at this electrode by cyclic voltammetry at potentials up to 0.8 V, scan rate 0.1 mV/s. The EG electrode was examd. in 0.5 M KOH at 0.8 to –0.95 V in a three–electrode system. The preoxidized EG was electrochem. more active than the original EG. In the 1st and in successive PhOH oxidn. cycles, current charges were larger. The activity drop occurring with original EG after the 1st cycle was inhibited; it appeared after the 2nd cycle but to a lesser deg. FTIR spectra showed topochem. changes in the activated EG.

2

Przemysłowe zastosowania grafitu

100%

Łuczak J.

Stal, Metale & Nowe Technologie

|

2014

|

tom nr 9-10

98--101

PL

Grafit to alotropowa odmiana węgla o charakterystycznej heksagonalnej budowie kryształów, której konsekwencją są jedna z najwyższych znanych w przyrodzie wytrzymałości i unikalne właściwości fizyczne. Materiały grafitowe stosowane w przemyśle nigdy nie mają w pełni wykształconej struktury, raczej są formą przejściową pomiędzy węglem amorficznym a kryształem grafitu. Ich właściwości, a przez to jakość, są ściśle skorelowane ze stopniem grafityzacji, strukturą wewnętrzną i z zawartością zanieczyszczeń, która nie przekracza 10 ppm w najlepszych grafitach.

3

Określenie kształtu porów w prasowanym graficie ekspandowanym za pomocą pomiarów ultradźwiękowych : badania wstępne

75%

Krzesińska M.

Karbo

|

2001

|

tom Nr 11

386-389

PL

Wykonano ultradźwiękowe badania dla dwóch serii monolitycznych próbek CEP o tych samych matrycach (zależnych od rodzaju kompresowanego grafitu ekspandowego - GE), ale o zróżnicowanej porowatości. Serie próbek wykonano z GE o gęstościach nasypowych 7,5 oraz 4 kg/m3. Stwierdzono, że dynamiczny moduł sprężystości i jego zależność od porowatości wynika z właściwości wyjściowego GE oraz, że parametr geometrycznego upakowania a dla wszystkich badanych próbek jest jednakowy i wynosi l niezależnie od użytego GE. Oznacza to, że pory w GEP są upakowane przypadkowo; nie tworzą regularnego systemu. Wyznaczone parametry n opisujące kształt porów były niższe niż dla idealnych sferycznych lub kubicznych porów. Przypuszcza się, że porowatość GEP może odpowiadać układowi porów cylindrycznych o osiach pod różnymi kątami do kierunku prasowania.

EN

The ultrasonic investigations of two series of monolithic samples of CEG with the same matrixes (dependent on used kind of expanded graphite (EG), but various porosity were made. Monolithic samples of compressed expanded graphite were produced using powders of expanded graphites of apparent densities 7,5 kg/m3 and 4 kg/m3 by means of compression under various pressures. Dynamic elastic modulus was found to be dependent on properties of initial EG. The packing geometry factor ,,a" was found to be equal to about 1 for all studied samples. It means that pores in CEG are randomly packed; they do not create regular system. Parameters ,,n" describing pore shapes were lower than those for ideal spherical or cubic pores. It was suggested that pores in CEG samples are cylinders with axes under various angles to the compression direction.

4

Właściwości prasowanych grafitów ekspandowanych w świetle badań niskotremperaturowej adsorpcji azotu i porozymetrii rtęciowej

75%

Lachowski A. I. , Krzesińska M. , Pająk J.

Chemik

|

2002

|

tom Vol. LV, nr 11

353-356

PL

Przeprowadzono badania właściwości monolitycznych kształtek formowanych poprzez jednoosiowe prasowanie ekspandowanego grafitu (ZEW Racibórz i SGL Carbon), które mogą stanowić matrycę do otrzymywania monolitycznych adsorbentów. Wykonano pomiary izoterm adsorpcji azotu i badania metodą porozymetrii rtęciowej. Otrzymano dane odnośnie dystrybucji porów w kształtkach o różnej gęstości pozornej.

EN

The properties of monolithic samples prepared by uniaxal compression of exfoliated graphite (ZEW Racibórz i SGL Carbon) have been studied. Such samples might be used as matrices for monolithic adsorbents. The isotherm of adsorption of nitrogen and mercury porosimetry have been performed. Pore distributions within samples of various apparent density have been estimated.

5

Właściwości przetwórcze kompozytów polipropylenowych modyfikowanych grafitem ekspandowanym

75%

Tartakowski Z. , Lewandowska-Kosyl J. , Kosyl M.

Przetwórstwo Tworzyw

|

2014

|

tom [R.] 20, nr 4 (160)

344--348

PL

W artykule przedstawiono wyniki badań właściwości przetwórczych kompozytów polipropylenowych modyfikowanych grafitem ekspandowanym (PP/EGexp), do zastosowań na wyroby techniczne. Udział napełniacza grafitowego w kompozytach wynosił 1, 2,5 i 5% wag. Analizowano wpływ wielkości cząstek i ich udział wagowy na właściwości przetwórcze wytworzonych kompozytów. Badano stopień wypełnienia gniazda formującego o kształcie spiralnym i wielostopniowym, skurcz wtryskowy przy różnych parametrach przetwórczych (ciśnienie wtryskiwania, temperatura wtryskiwania) oraz masowy wskaźnik szybkości płynięcia materiałów kompozytowych. Stwierdzono, że ilość i wielkość cząstek grafitowych wpływa na zmniejszenie skurczu wtryskowego. Wzrost temperatury przetwórstwa i ciśnienia wtryskiwania, powoduje zwiększenie wypełnienia gniazda formującego. Wykazano również, że poprzez zmianę parametrów przetwórstwa można regulować stopień wypełnienia gniazda formującego. Przeprowadzone badania potwierdziły, możliwość aplikacji materiałów na specjalne wyroby techniczne o złożonej geometrii kształtu.

EN

This paper presents the results of processing properties of polypropylene composites modified expanded graphite (PP / EGexp), which may be used for technical products for special application. The share of graphite filler in composites were 1, 2.5 and 5 wt%. The influence of particle size and the weight fraction on the processing properties of the composites produced has been studied. Materials were tested degree of filling of the cavity in a spiral shape, shrinkage after injection. Also analyzed the degree of filling the mold with the socket in the stepped shape of the product at different processing parameters (injection pressure, injection temperature) and the melt flow rate of composite materials. It was found that the amount and size of graphite particles reduces shrinkage after injection. The increase in processing temperature and injection pressure, increases the filling cavity. It was also shown that by varying the processing parameters can be adjusted by the degree of filling the cavity. The study confirmed the possibility of the application materials for special technical products with complex geometry shape.

6

Grafit ekspandowany jako napełniacz wzmacniający kompozyty elastomerowe

75%

Pingot T. , Pingot M. , Zaborski M.

Przemysł Chemiczny

|

2011

|

tom T. 90, nr 4

550-554

7

A study of static friction in reciprocating movement of sliding pair steel-expanded graphite

75%

Rewolińska A. , Kowalewski P. , Perz K. , Paczkowska M.

Tribologia

|

2016

|

tom nr 6

131--138

EN

The paper presents the results of coefficient of static and kinetic friction depending on the load. During the study, the sample in the form of a pin with expanded graphite, mounted in a holder, was forcibly pressed the Fn to the steel countersample. The device on which the tests were carried out research allows sliding friction in reciprocating motion. It has been found that there is a noticeable difference between the coefficient of static friction and kinetic for both fixed and different pressures. In the field of applied pressure, there were no significant their impact on the coefficient of friction; applied force was not sufficiently high which may have contributed to this state. The study had a distinctive character.

PL

W pracy przedstawiono wyniki badań wartości współczynnika tarcia statycznego i kinetycznego w zależności od obciążenia. Podczas przeprowadzonych badań próbka w postaci trzpienia z grafitu ekspandowanego, zamocowana w uchwycie, dociskana była siłą Fn do stalowej przeciwpróbki. Urządzenie, na którym wykonano badania umożliwia prowadzenie badań tarcia ślizgowego w ruchu posuwisto-zwrotnym. Stwierdzono, że zauważalna jest różnica między współczynnikiem tarcia statycznego oraz kinetycznego zarówno dla stałych, jak i różnych nacisków. W zakresie stosowanych nacisków nie odnotowano znaczącego ich wpływu na współczynnik tarcia; przyłożona siła nie była wystarczająco duża, co mogło przyczynić się do powyższego stanu. Przeprowadzone badania miały charakter rozpoznawczy.

8

Antistatic polyethylene free-standing films modified with expanded graphite – technological aspects

75%

Imiołek P. , Kasprowicz K. , Laska J.

Polimery

|

2020

|

tom T. 65, nr 4

275--279

EN

The main goal of this research was to develop antistatic polyethylene films with a surface resistance of ≤109 Ω. The research involved testing low density polyethylene/linear low density polyethylene (PE-LD/PELLD) filled with various amounts of expanded graphite EG 096. The samples were made by hot pressing and injection molding. Mechanical and electrical properties were tested. The research results show that samples with a content of 30% by weight of expanded graphite are characterized by good mechanical properties, e.g. Young’s modulus of the filled PE was higher by 195% compared to pure polyethylene.

PL

Głównym celem prezentowanych badań było opracowanie antystatycznych folii polietylenowych o oporności powierzchniowej ≤109 Ω. W pracy zbadano polietylen małej gęstości (PE-LD/PE-LLD) napełniony różną ilością grafitu ekspandowanego EG 096. Próbki wykonano metodą prasowania na gorąco i formowania wtryskowego. Zbadano ich właściwości mechaniczne oraz elektryczne. Na podstawie wyników badań stwierdzono, że próbki o zawartości 30% mas. grafitu ekspandowanego charakteryzują się korzystnymi właściwościami mechanicznymi, np. moduł Younga napełnionego PE był o 195% większy niż polietylenu bez udziału napełniacza.

9

Chemiczno-termiczna obróbka ekspandowanego grafitu jako metoda jego aktywacji i regeneracji

75%

Krawczyk P. , Skowroński J. M.

Przemysł Chemiczny

|

2013

|

tom T. 92, nr 1

86-89

10

Nanokompozyty termoplastycznego poliuretanu wzmacniane napełniaczami węglowymi

63%

Stafin K. , Leszczyńska A. , Pielichowski K.

Chemik

|

2016

|

tom Vol. 70, nr 11-12

685--690

PL

Termoplastyczny poliuretan (TPU) łączy w sobie właściwości usieciowanych chemicznie kauczuków w temperaturze użytkowania oraz tworzyw termoplastycznych w warunkach przetwórstwa w podwyższonej temperaturze. W niniejszej pracy przedstawiono nanokompozyty tego materiału wzmacniane napełniaczami węglowymi, takimi jak nanorurki węglowe, grafen i ekspandowany grafit. Nanododatki węglowe istotnie poprawiają właściwości polimeru, w tym wytrzymałość mechaniczną oraz stabilność termiczną, a także umożliwiają wytwarzanie nanokompozytów przewodzących ładunki elektryczne. Poprawa lub uzyskanie nowych właściwości zależy nie tylko od ilości i sposobu wprowadzania nanonapełniacza do osnowy polimeru, ale również od występowania specyficznych oddziaływań pomiędzy nanonapełniaczem a segmentami sztywnymi i miękkimi TPU. Z tego względu, dobór i modyfikacja budowy chemicznej napełniacza lub TPU są kluczowe dla uzyskania pożądanych cech użytkowych tworzywa.

EN

Thermoplastic polyurethane (TPU) behaves both as a crosslinking rubber and thermoplast at ambient temperature during use and at elevated processing temperature, respectively. In this paper, thermoplastic polyurethane reinforced with carbon nanofillers (e.g. carbon nanotubes, graphene and expanded graphite) was presented. Carbon nanofillers improve mechanical strength, thermal stability and are effective modifiers for manufacturing electrically conductive nanocomposites. Improved or new properties of TPU nanocomposites depend not only on the amount of filler and the method of its incorporation into the polymer matrix, but also on the occurrence of a specific interactions between the filler and rigid or soft TPU segments. Therefore the proper selection and modification of chemical structure of the polymer and filler are crucial for the successful manufacturing of new material with desired properties.

11

Electrochemical properties of exfoliated graphites in alkaline solution

63%

Skowroński J. M. , Krawczyk P.

Karbo

|

2002

|

tom Nr 3

78-81

EN

The study of electrochemical properties of exfoliated graphite was carried out in 0,5 M KOH using cyclic voltammetric method. Four different types of graphite intercalation compounds (H(2)SO(4)-GIC, H(2)SO(4)-GIC, CrO(3)-GIC and FeCl(3)-GIC) were thermally exfoliated in air at 800°C for 4 min to obtain the exfoliated graphites (EG) or exfoliated graphite intercalation compounds (EG-GIC). In the latter case intercalate persists in graphite structure after the process of exfoliation. Some differences in electrochemical behaviour of exfoliated GICs are observed on cyclic voltammograms. The location of current peaks and the peak charges can be related to the differences in specific surface area and the degree of exfoliation of investigated compounds. Generally, the results of voltammetric measurements allow the correlation between the electrochemical features of exfoliated graphite intercalation compounds in alkaline solution and type of precursor used for exfoliation.

PL

Badania elektrochemicznych właściwości eksfoliowanego grafitu prowadzone były w 0,5 M KOH przy użyciu metody cyklicznej woltamperometrii. W celu otrzymania eksfoliowanych grafitów (EG) lub eksfoliowanych interkala-cyjnych związków grafitu (EG-IZG) cztery różne interkalacyjne związki grafitu (HClO(4)-IZG, CrO(3)-IZG, H(2)SO(4)-IZG i FeCl(3)-IZG) były termicznie eksfoliowane w atmosferze powietrza w 800°C przez 4 minuty. W przypadku EG-IZG interkalat pozostaje w strukturze grafitu po procesie eksfoliacji. Na woltamogramach obserwuje się różnice w elektrochemicznym zachowaniu się eksfoliowanych IZG. Położenie oraz prądy pików mogą być powiązane z rozwinięciem powierzchni aktywnej oraz stopniem eksfoliacji badanych związków. Ogólnie wyniki pomiarów woltamperometrycznych pozwalają wnioskować na temat zależności pomiędzy elektrochemicznymi właściwościami eksfoliowanych. interkalacyjnych związków grafitu w środowisku alkalicznym a typem prekursora wykorzystanego do eksfoliacji.

12

Struktura i właściwości termiczne nanokompozytów ekspandowany grafit(EG))/poli(tereftalan etylenu)(PET)

63%

Paszkiewicz S. , Rosłaniec Z. , Szymczyk A. , Spitalsky Z. , Mosnacek J.

Chemik

|

2012

|

tom Vol. 66, nr 1

21-30

PL

Uzyskano nanokompozyty poli(tereftalanu etylenu) z ekspandowanym grafitem (PET/EG) o zawartości nanonapełniacza 0.025 - 0.4 %wag. metodą polimeryzacji kondensacyjnej (polikondensacji) in situ. Określono ich morfologię (SEM i TEM), stabilność termiczną przy wykorzystaniu metody TGA (temperatury odpowiadające: 2% (T-2%),10% (T-10%) i 50% (T-50%) ubytku masy, energię aktywacji metodą Freemana-Carrolla (Ea), temperaturę maksimum szybkości ubytku masy nanokompozytów w atmosferze powietrza i w argonie. Oceniono również wpływ grafenu na przemiany fizyczne zachodzące w PET (DSC). Wyniki badań nanokompozytów PET/EG porównano z wynikami badań niemodyfikowanego PET. Fotografie SEM nanokompozytów wykazują dwufazową strukturę układów PET/EG z wyraźnie widocznymi płytkami grafenu, jak i nielicznymi aglomeratami. Badania nanokompozytów PET/EG z wykorzystaniem techniki TEM potwierdziły obecność płytek grafenowych o wielkości ok. 1-10 ?m. Oznacza to, że zastosowana metoda in situ pozwala na otrzymanie rozsuniętych i stosunkowo równomiernie rozłożonych płytek grafenowych (EG) w osnowie PET. Ponadto wykazano, że dodatek nanonapełniacza nie wpływa znacząco na temperatury przemian fizycznych, jak również na stopień krystaliczności PET. Zaobserwowano natomiast wyższą termostabilność oraz stabilność termo-oksydacyjną nanokompozytów wynikającą z udziału nanocząstek grafenowych.

EN

Nanocomposites based on poly(ethylene terephtalate) and expanded graphite (PET/EG) with 0.025-0.4wt.% nanofiller content were prepared by in situ condensation polymerization (polycondensation). Their morphology was determined (TEM, SEM), thermal stability by TGA (temperatures corresponding to: 2% (T-2%),10% (T-10%) and 50% (T-50%) weight loss, activation energy by Freeman-Carroll method (Ea), temperature of maximum mass loss rate of nanocomposites in air and in argon. Also the influence of graphene was assessed on the physical transition occurring in the PET (DSC). The results of PET/EG nanocomposites were compared with the unmodified PET. SEM images of nanocomposite exhibit a diphasic structure of PET / EG of clearly visible graphene platelets, and few agglomerates. The study of nanocomposites of PET / EG using TEM techniques confirmed the presence of grephene platelets size of about 1÷10 ?m. This means, that in situ polymerization has been used to obtain exfoliated and relatively evenly spaced graphene plates (EG) in the PET matrix. In addition, it was demonstrated that the addition of nanofiller not significantly affect the physical transition temperature, as well as the degree of crystallinity of PET. Higher thermal stability and thermo-oxidative stability of the nanocomposites was observed resulting from participation of graphene nanoparticles.

13

Właściwości kompozytów cementowych z dodatkiem grafitu ekspandowanego

63%

Pichór W. , Słomka J.

Cement Wapno Beton

|

2011

|

tom R. 16/78, nr 4

210-214

PL

Opisano badania właściwości zaczynów i zapraw cementowych przy dodatku grafitu ekspandowanego. Stwierdzono, że dodatek ten zmniejsza wytrzymałość na ściskanie, natomiast materiały te uzyskują interesujące właściwości elektryczne. Oporność próbek spada aż o 7 wielkości. Uzyskane wyniki doświadczeń pokazują, że właściwości zapraw z dodatkiem grafitu ekspandowanego w ilości przekraczającej próg perkolacji [około 30%] mają właściwości elektryczne pozwalające na ich wykorzystanie do pomiarów temperatury i naprężeń mechanicznych tych kompozytów.

EN

The properties of cement pastes and mortars with the addition of expanded graphite were investigated. It was found that this addition caused the decrease of compressive strength, but the composites reach very interesting electric properties. The resistivity of the samples is decreasing as much as of 7 order of magnitude. The results show that the mortars properties, in the case of expanded graphite in the ratio exceeding the percolation threshold [about 30% of volume], have the electric properties allowing their usage for temperature and mechanic stress measurements of this composite.

14

Thermoelectric properties of expanded graphite as filler of multifunctional cement composites

63%

Pichór W. , Frąc M.

Composites Theory and Practice

|

2012

|

tom R. 12, nr 3

205-209

EN

This paper presents the results of investigations on the thermoelectric properties of expanded graphite obtained by different methods. The expanded graphite was subjected to thermal treatment by two different ways: by rapid heating in a furnace and by irradiated microwave. For each of the methods, graphite was expanded in different conditions for the purpose of investigating the influence of thermal treatment on their thermoelectric properties. The bulk density and thermoelectric properties (Seebeck coefficient) of expanded graphite were measured. The results of the investigations show that the method and time of thermal treatment have a major influence on the thermoelectric properties of expanded graphite.

PL

W pracy przedstawiono wyniki badań właściwości termoelektrycznych grafitu ekspandowanego otrzymanego różnymi metodami. Wykorzystano dwie metody ekspandacji: przez gwałtowne podgrzanie w piecu laboratoryjnym oraz przez poddanie działaniu promieniowania mikrofalowego. W przypadku metody bezpośredniego ogrzewania proces prowadzono w różnej temperaturze w zakresie 500÷1000°C i przy różnym czasie ogrzewania, natomiast w metodzie mikrofalowej zmienną poza czasem procesu była moc dostarczona do próbki. Wyniki pomiaru współczynnika Seebecka pokazały, że metoda ekspandacji oraz czas procesu mają duży wpływ na otrzymane właściwości termoelektryczne grafitu ekspandowanego.

15

Wpływ temperatury na zjawiska tribologiczne występujące w skojarzeniu grafit ekspandowany–stal

63%

Rewolińska A. , Paczkowska M. , Perz K. , Orłowski T.

Tribologia

|

2015

|

tom nr 4

159--166

PL

Celem niniejszego opracowania jest ocena wpływu temperatury na właściwości tribologiczne skojarzenia grafit ekspandowany–stalowa tarcza. Badane skojarzenie składa się z próbek wykonanych z grafitu ekspandowanego, które współpracowały z tarczą wykonaną ze stali wysokowęglowej. Próbki wykonano z grafitu ekspandowanego w postaci taśmy, która została sprasowana. Parametry chropowatości tarczy są następujące: Ra = 2,233 μm, Rz = 15,608 μm, Rq = 2,736 μm. Badania wykonywano w różnych temperaturach. Czas trwania testu wynosił odpowiednio 30 i 60 s, a prędkość poślizgu 25 mm/s. Po zakończeniu każdego z etapów próbki ważono. Na podstawie przeprowadzonych testów określano wartości współczynnika tarcia oraz szybkość zużycia masowego próbek. W wyniku współpracy tribologicznej skojarzenia odnotowano spadek współczynnika tarcia wraz ze wzrostem temperatury. Uzyskane wartości współczynnika tarcia dla próbek wykonanych z grafitu ekspandowanego są niższe niż dla grafitu proszkowego. W zakresie stosowanych nacisków wynoszących 50 i 100 N/cm2 nie odnotowano ich wpływu na współczynnik tarcia. Wykonane badania zużycia masowego próbek wskazują na potrzebę wydłużenia czasu badania. Odnotowania wymaga również fakt powstającej na powierzchni stalowej skojarzenia warstewki, która jest charakterystyczna dla współpracy stali z grafitem.

EN

The aim of this article is to evaluate the effect of temperature on the tribological properties of expanded graphite works with a steel shield. The examined association was composed of samples made from expanded graphite, which cooperated with a shield made of high carbon steel. The values of roughness of the disc are as follows: Ra = 2.233 μm, Rz = 15.608 μm, and Rq = 2.736 μm. Tests were performed at different temperatures. The durations of the tests were 30 and 60 seconds, and the sliding velocity was 25 mm/s. After each step, the samples were weighed. Based on the tests, the coefficient of friction and wear rate of the samples were determined. The tribological combination decreased the coefficient of friction with increasing temperature. The resulting coefficients of friction for specimens made of expanded graphite were lower than the graphite powder. In the field of applied pressures of 50 and 100 N/cm2, there was no effect on the coefficient of friction. A layer was formed on the surface of the steel, which is characteristic of graphite cooperation with steel.

16

Graphite expanded as a film-forming material on a steel surface

63%

Rewolińska A. , Perz K. , Kinal G.

Tribologia

|

2017

|

tom nr 5

81--85

EN

The results of observational studies of the emerging graphite film on the steel surface are presented. The association – steel pin and graphite element – reciprocating motion was employed. The results show the possible mechanism of graphite film formation for the various stages of association work under various operating conditions. For a water-impregnated graphite element, the film forming process takes place faster than for a dry element.

PL

Przedstawiono wyniki badań obserwacyjnych powstającej warstewki grafitowej na stalowym podłożu. Skojarzenie pracowało w układzie stalowy trzpień poruszający się ruchem posuwisto-zwrotnym po elemencie wykonanym z grafitu ekspandowanego. Wyniki badań przedstawiają możliwy mechanizm powstawania warstewki grafitowej na poszczególnych etapach pracy skojarzenia, w różnych warunkach pracy. Dla elementu grafitowego nasączonego wodą proces formowania się warstewki zachodzi szybciej niż dla elementu suchego.

17

Zjawisko przenoszenia materiału w skojarzeniu grafit ekspandowany–stal

63%

Rewolińska A. , Stachowiak A. , Kinal G. , Paczkowska M. , Perz K.

Tribologia

|

2015

|

tom nr 4

167--175

PL

Celem artykułu jest identyfikacja zjawiska przenoszenia materiału w skojarzeniu pary tribologicznej grafit ekspandowany–stal w wybranych warunkach. Badanie skojarzenia materiałowego wykonano na stanowisku kulka–pierścień. Stalowa kulka poruszała się ruchem posuwisto-zwrotnym po powierzchni próbki (pierścień) z grafitu ekspandowanego. Próby wykonano na sucho oraz mokro (całkowite zanurzenie skojarzenia w wodzie). Ocenę powierzchni kulki oraz pierścienia prowadzono z wykorzystaniem metalograficznego mikroskopu op-tycznego firmy ZAISS. Stwierdzono, że na powierzchni kulki, zarówno podczas pracy na sucho jak i po zanurzeniu skojarzenia w wodzie powstaje warstwa grafitu. Wygląd tworzonej warstwy zależy od warunków pracy skojarzenia–warstewka utworzona w wodzie jest cieńsza niż warstwa utworzona podczas pracy na sucho. Utworzona warstwa ma wyraźną strefową budowę warstwy. Na powierzchni bocznej kulki powstają zarysowania, których mechanizm powstawania wymaga wyjaśnienia. Należy poznać mechanizm powstawania warstwy oraz warunki kształtowania tej warstewki o optymalnych właściwościach.

EN

A phenomenon closely related to cooperation tribological pair of graphite-metal is the transmission of the material. A large number of physical and chemical factors affecting the transfer of graphite cause the lack of theory describing this phenomenon. It also is difficult to determine which of the elementary frictions dominates under certain conditions. The aim of this article is to identify the relocation of the material in the combination tribological pair of expanded graphite-steel under the selected conditions. Research was carried out on post-ball-ring tester. A steel ball moved with a reciprocating motion over the surface of the sample (ring) of the expanded graphite. Tests were carried out in dry and wet (total immersion association in water) conditions. The evaluation of the surface of the ball and ring were conducted using optical microscopy (metallographic manual Zaiss). The surface of the balls, both in dry and after immersion associations in water, formed a layer of graphite. The exterior layer formed varied with the operating conditions of association; the layer formed in water was thinner than the layer formed in dry working conditions. The formed layer has a clearly layered structure. On the surface of the balls, cracks were found and the mechanism needs to be clarified. Wear products, which are products of reactions and removed from the workplace, had a beneficial role in this case, under appropriate conditions. There is a need to understand the mechanism of the formation of the layer and the layer forming conditions with optimal properties.

18

Production and characterization of polyurethane/expanded graphite composites for industrial food preservation

63%

Güngör Ertuğral T.

Polimery

|

2022

|

tom Vol. 67, nr 11-12

588--594

EN

Thermal insulation materials extend the shelf life of food and reduce energy consumption. Polyurethane (PU) insulation materials are often used to keep food hot and cold. Improving the thermal insulation properties of PU can significantly contribute to energy savings and lower food-related costs in the food and pharmaceutical industries. Polyurethane/expanded graphite (PU/EG) composites were obtained by hot-pressing by adding expanded graphite (EG) to PU foams. Composites with 0.05%, 5%, and 10% EG were characterized by Fourier transform infrared spectroscopy (FTIR), scanning electron microscope (SEM), and thermogravimetric analysis (TGA).

PL

Materiały termoizolacyjne wydłużają okres przydatności do spożycia żywności oraz zmniejszają zużycie energii. Poliuretanowe (PU) materiały izolacyjne są często stosowane do przechowywania żywności na gorąco i na zimno. Poprawa właściwości termoizolacyjnych PU może znacząco przyczynić się do oszczędności energii i obniżenia kosztów związanych z żywnością w przemyśle spożywczym i farmaceutycznym. Kompozyty poliuretan/ekspandowany grafit (PU/EG) wytworzono metodą prasowania na gorąco poprzez dodanie ekspandowanego grafitu (EG) do pianek PU. Kompozyty z udziałem 0,05% mas., 5% mas. i 10% mas. EG scharakteryzowano za pomocą spektroskopii w podczerwieni z transformacją Fouriera (FTIR), skaningowego mikroskopu elektronowego (SEM) i analizy termograwimetrycznej (TGA).

19

Flame retardant and thermal behavior of polylactide/expandable graphite composites

63%

Wei P. , Bocchini S. , Camino G.

Polimery

|

2013

|

tom T. 58, nr 5

361-364

EN

In this article expandable graphite was used to produce fire retardant biobased polylactide. For this purpose, PLA blends with addition of 1, 5 or 10 wt. % of expandable graphite intercalated with sulphuric acid (GR) were obtained using co-rotating twin screw extruder. Thermal stability and flammability of prepared samples were examined by thermogravimetric analysis (TGA), cone calorimeter measurements and UL 94 test. Flammability UL-94 test shows the highest V-0 ranking from 5 % graphite loading, whereas 10 % is required for sensible decrease of rate of combustion in cone calorimeter forced combustion test.

PL

W artykule przedstawiono wyniki badań nad zastosowaniem zdolnego do ekspandowania grafitu do uniepalniania polilaktydu (PLA). W tym celu za pomocą wytłaczarki dwuślimakowej sporządzono mieszanki PLA z dodatkiem 1, 5 lub 10 % mas. ekspandowalnego grafitu interkalowanego kwasem siarkowym (GR). Otrzymane próbki badano metodą termograwimetryczną (TGA), a także wykonano pomiary z zastosowaniem kalorymetru stożkowego. Przeprowadzono również testy palności UL-94. Stwierdzono, że najskuteczniej uniepalnionym materiałem spełniającym kryteria klasy palności V-0 jest kompozyt zawierający 5 % mas. GR. Natomiast zapewnienie odpowiedniego zmniejszenia szybkości wydzielania ciepła (HRR) wymaga dodania 10 % mas. GR.

20

Correlations between Structures of Expanded Graphite - Polymer Composites and Acoustic Emission Phenomena

63%

Berdowska A. , Berdowski J. , Aubry F.

Archives of Metallurgy and Materials

|

2015

|

tom Vol. 60, iss. 4

2479--2484

EN

Compressed expanded graphite was applied as a base matrix to the preparation of microporous composites as products of impregnation, polymerization and carbonization of poly-furfuryl alcohol. During carbonization, the original polymeric structure is transformed into an amorphous turbostratic carbon structure with ultramicropores. The structure, porosity and many chemical and physical properties change after each stage of their technological treatment. The acoustic emission method was used for accurate determination of these changes. It is possible to determine a large number of acoustic emission parameters and therefore to increase the amount of information provided by the studied materials. Acoustic emission pulses, counts rate, events rate, signal peak value and their sums were measured. Also frequency spectrum was received as a result of acoustic emission signal analysis with use of Fourier transformation procedure. The conclusions resulting from the Fourier analysis of the registered spectrum are very interesting and provide information about composite structures as well as bonds between the graphite matrix and the polymer that fills it. Analysis of acoustic emission parameters provides data on physical and chemical processes that would be very difficult to study by means of other techniques. Wide applications of these porous composites make them very interesting subject of the study.

PL

Sprasowany grafit ekspandowany użyto jako bazową matrycę do wytworzenia mikroporowatych kompozytów będących produktami impregnacji, polimeryzacji i karbonizacji alkoholu polifurfurylowego. Podczas procesu karbonizacji oryginalna struktura polimerowa jest przekształcana w strukturę turbostratyczną węgla amorficznego z ultramikroporami. Struktura, porowatość oraz wiele chemicznych i fizycznych własności ulega zmianie na poszczególnych etapach technologicznego procesu. Metodę emisji akustycznej użyto w celu dokładnego przebadania tych zmian. Możliwym jest wyznaczenie w eksperymentach dużej liczby parametrów emisji akustycznej co pozwala uzyskać dużą ilość informacji o badanych materiałach. Zmierzono następujące parametry emisji akustycznej: szybkość zliczeń, szybkość zdarzeń, amplituda impulsu, średnia wartość skuteczna sygnałów oraz sumy tych parametrów. Także analizowano widmo częstotliwościowe sygnałów przy pomocy transformaty Fouriera. Wnioski wynikające z analizy fourierowskiej widm są niezwykle interesujące i dostarczają informacje o strukturze kompozytów oraz o wiązaniach między grafitową matrycą a polimerem wypełniającym ją. Analiza parametrów emisji akustycznej dostarcza wielu danych o fizycznych i chemicznych własnościach, które byłyby bardzo trudne do zbadania przy użyciu innych metod. Szerokie zastosowania omawianej grupy porowatych kompozytów czyni je bardzo interesującym przedmiotem badań.