Wyniki wyszukiwania - Biblioteka Nauki

Nowa wersja platformy, zawierająca wyłącznie zasoby pełnotekstowe, jest już dostępna.
Przejdź na https://bibliotekanauki.pl

Ograniczanie wyników

Znaleziono wyników: 3

Liczba wyników na stronie

Wyniki wyszukiwania

Wyszukiwano:
w słowach kluczowych: glow

Sortuj według:

Ogranicz wyniki do:

Light and Space. On the Phenomenology of Light

100%

Böhme G.

Dialogue and Universalism

2014

nr 4

62-73

As its subtitle suggests, the essay is a phenomenological account of the diverse ways in which light can be experienced by the senses. Gernot Böhme divides these experienc-es into two types depending on whether they concern the relation between light and space (the categories “light-cleared space,” “lightspace,” “lights in space”) or between light and objects (“things in light,” “light upon things”). Böhme sees the synthesis of both these types of experiences in the illumination phenomenon, in which spatial/light effects and the way in which objects are illuminated combine to create a specific atmos-phere during the sensual, bodily experiencing of space. Böhme also discusses the appli-cations of light effects in contemporary architecture and art.

Dyfuzja azotu w warstwie powierzchniowej spieków na bazie kobaltu

100%

Borowiecka-Jamrozek J. , Lachowski J.

Inżynieria Powierzchni

2011

tom nr 1

31-34

W pracy przedstawiono wyniki badań procesu dyfuzji w warstwie powierzchniowej spieku na bazie kobaltu. Warstwę powierzchniową uzyskano podczas azotowania kobaltu oraz wieloskładnikowego stopu na bazie kobaltu, w warunkach wyładowania jarzeniowego. Obróbkę prowadzono przez 4 godziny, w temperaturze 520°C, w atmosferze N2 - 33%-obj. H2 przy ciśnieniu 3 hPa. Próbki do badań wykonano metodą metalurgii proszków, techniką prasowania na gorąco proszku Co Extrafine oraz mieszanki proszków Co Extrafine i stopu niklu HMSP 1660-02 (po 50 %-mas.). Określono: grubość, mikrostrukturę oraz mikrotwardość otrzymanej warstwy. Zaproponowano model dyfuzji atomów azotu w spieku, zakładając międzywęzłowy mechanizm dyfuzji. Oszacowano wartość współczynnika dyfuzji azotu. Otrzymany współczynnik dyfuzji porównano z danymi dla dyfuzji wodoru i węgla w kobalcie.

The reaserch results of the nitriding diffusion into the cobalt sinters and into a complex cobalt-base alloy are presented in the paper. The specimens were nitrided under the glow discharge conditions for 4 hours, at 520°C and 3 hPa, in N2 - 33vol-%H2 atmosphere. The hot pressing powder metallurgy route was chosen for the production ofspecimens from the commercial Co Extrafine powder and Co Extrafine/HMSP 1660-02 powder mix (50/50 by weight). The thickness, the microstructure and the microhardness of the layer have been measured. The model of interstitial diffusion of nitrogen atoms in a sinter has been proposed. The diffusion coefficient of nitrogen has been estimeted. The diffusion coefficient has been compared with the data of diffusion of hydrogen and carbon in cobalt.

Properties of surface layers produced on titanium alloy under glow discharge conditions.

88%

Fleszar A. , Wierzchoń T.

Inżynieria Materiałowa

1998

tom R. XIX, nr 4

1011-1014

The recent rapid progress in surface treatment techniques dictates that titanium alloys should have an improved resistance to frictional wear without any loss of their high corrosion resistance. These requirements can be satisfied by producing surface layers of specified microstructure and phase composition. The paper presents the results of metallographical examinations, corrosion and wear resistance tests and SEM observations of the surface layers produced on the OT4-0 titanium alloy using the nitriding and carbonitriding process under glow discharge conditions. These techniques permit controlling the chemical composition, thickness and microstructure of the surface layers, parameters that essentially affect their performance properties such as the corrosion resistance and frictional wear resistance.