Abrasion resistance of Ni-B/Si3N4 composite layers produced by electroless method

100%

Mazurek A. , Cieślak G. , Bartoszek W. , Trzaska M.

2017

tom Vol. 87, nr 1

21--26

Purpose: The paper presents the results of investigations of Ni-B/Si3N4 composite layers produced on steel substrate by electroless method. Design/methodology/approach: Amorphous silicon nitride powder (Si3N4) with nanometric particle sizes was used as a dispersion phase for the production of composite layers. Ni-B/Si3N4 composite layers were produced in baths of varying Si3N4 powder content. For comparative purposes, the study also includes results related to a Ni-B layer. The Si3N4 powder and the structure of the produced layers were characterized. The topography and morphology of the surface of the produced layers are presented. The adhesion of the layers to the substrate material was determined. Microhardness and tribological properties of test materials were determined. Findings: The results of the studies show that Ni-B/Si3N4 composite layers and Ni-B composite layers are characterized by compact structures and good adhesion to the substrate material. The incorporation of Si3N4 particles into the Ni-B layers increases the degree of surface development of the layers. The Ni-B/Si3N4 composite layer material exhibits less microhardness and less abrasive wear compared to Ni-B layers. However, the extent of wear damage of the Ni-B/Si3N4 is relatively small comparing to Ni-B layers.

Corrosion properties of Ni-B/Al203 composites layers produced by electroless method

100%

Cieślak G. , Mazurek A. , Bartoszek W. , Trzaska M.

tom nr 7

215--217

The paper presents results of studies of alloy composite layers of Ni-B/Al203 produced by electroless method on steel substrate. As the dispersion phase is the powder of aluminum oxide Al203 with nanometric size. Two variants of Ni-B/Al203 layers deposited from a bath containing different amounts of aluminum oxide (5 and 10 g/dm3) were prepared and for comparison purposes the Ni-B layer without built-AI203 particles was also studied. The powder of Al203 and the produced layers were examined by the scanning electron microscopy (SEM), X-Ray diffraction (XRD), optical microscopy and measurements of Vickers microhardness, and of roughness parameters of Ra and Rr Corrosion resistance were studied by the potentiodynamic method in the environment of 0.5 M Nad. The results of identifications of structure of the Al203 powder and produced Ni-B and Ni-B/Al203 layers, their microhardness and results of corrosion testing are presented. The produced layers are compact and have uniform thickness. Incorporation of Al203 powder particles in a matrix of nickel-boron increases the level of surface development and increase of corrosion resistance.

W pracy przedstawiono wyniki badań stopowych warstw kompozytowych Ni-B/ Al2O3 wytwarzanych metodą bezprądową na podłożu stalowym. Jako fazę dyspersyjną stosowano proszek tlenku glinu Al2O3 o nanometrycznych wymiarach cząstek. Wytworzono dwa warianty warstw kompozytowych Ni-B/ Al2O3 osadzanych z kąpieli o różnej zawartości tlenku glinu (5 i 10 g/dm3), oraz w celach porównawczych warstwę Ni-B bez wbudowanych cząstek Al2O3. Proszek Al2O3 oraz wytworzone warstwy Ni-B badano za pomocą skaningowej mikroskopii elektronowej (SEM), dyfrakcji promieniowania rentgenowskiego (XRD), mikroskopii optycznej, pomiarów mikrotwardości metodą Vickersa oraz parametrów chropowatości Ra i Rz. Badania odporności na korozję zrealizowano metodą potencjodynamiczną w środowisku 0,5 M NaCl. Przedstawiono wyniki badań struktury proszku Al2O3 oraz powłok Ni-B oraz Ni-B/ Al2O3, a także mikrotwardość oraz odporność na korozję w badanych warunkach. Wytworzone warstwy charakteryzują się zwartą budową i równomierną grubością. Wbudowanie cząstek proszku Al2O3 w niklowoborową osnowę wpływa na zwiększenie stopnia rozwinięcia powierzchni oraz zwiększenie odporności na korozję.