Wyniki wyszukiwania - Biblioteka Nauki

1

Diffusion of Chloride Ions in the Pastes and Mortars Containing Ground Granulated Blast Furnace Slag

100%

Deja J. , Łój G.

|

2009

|

tom Vol. 83, nr 8

1471-1479

EN

The chloride corrosion is one of the seriously harmful processes leading to the destruction of con crete structure. Aparat from the chemical attack on the concrete cover, the chloride ions show their aggres sive action on the steel reinforcing elements. The high resis tance of slag cementitious materials has been proved in many earlier works. In the presented study the au thors give a confrontation of results on the durability of Portland cement, slag cement with 60% granulated blast furnace slag and alkali acti vated slag cement. The mortars were stored in NaCl, MgCl2 and CaCl2 solutions respectively. Aparat from the strength tests, the phase composition studies using XRD and SEM were carried out. The effective diffusion coefficients of Cl– ions, originating from NaCl, MgCl2 or CaCl2, were measured for the Portland cement and slag mortars. The significantly higher corrosion resistance of slag cementitious mortars has been thus proved. It has been also shown that the rate of corrosion process was closely correlated with the type of accompanying cation in chloride solution. The progress of corrosion was the most evident in the presence of Mg2+ ion, the slow est corrosion was observed in the presence of sodium.

2

Chemiczne i mikrostrukturalne uwarunkowania odporności betonu na działanie środowiska chlorkowego i siarczanowego

72%

Deja J. , Kołodziej Ł.

|

2011

|

tom nr 6

338-340

PL

W artykule zaprezentowano między innymi badania nad dyfuzją jonów chlorkowych przez przegrodę wykonaną z zaprawy cementowej zawierającej cement portlandzki oraz różną zawartość popiołu. Pozorne współczynniki dyfuzji jonów chlorkowych zostały określone przy użyciu metody komór dyfuzyjnych dla próbek po 28, 56, 91, 180, 360 dniach dyfuzji. Dla scharakteryzowania materiałów użyto analizy chemicznej analizy XRD oraz SEM. Główne wnioski z tych badań są takie, że zastąpienie cementu portlandzkiego popiołem fluidalnym powoduje spadek pozornych współczynników dyfuzji jonów chlorkowych. Dodatek popiołu w ilości 15-30% powoduje korzystne zmniejszenie dyfuzji jonów chlorkowych.

EN

This paper presents the results of study on chloride diffusion through barriers made with mortars containing composite cement and ordinary Portland cement. The apparent diffusion coefficient for each mortars with different contents of ashes was determined using cell diffusion method test after 28, 56, 91, 180, 270, 360 days of diffusion. For characterization of materials SEM and XRD analyses were used. The main findings were that substitution of cement by ashes decrease chloride ions diffusion coefficients through the mortars. Increase in the ash amount in the range from 15-30% increase beneficial effect of decreasing chloride ions diffusion.

3

Zmiany mikrostruktury zaczynu poddanego dekalcyfikacji

72%

Słomka-Słupik B. , Zybura A.

|

2010

|

tom R. 15/77, nr 6

333-339

PL

W pracy zamieszczono wyniki makroskopowych, mikroskopowych i fazowych badań próbki zaczynu z CEM I poddanej 25 dobowej agresji w nasyconym wodnym roztworze chlorku amonu. Przedstawiono półilościowe metody wyznaczania porowatości oraz zawartości faz zaczynu. Uzyskany rozkład porowatości skonfrontowano ze zmianami składu fazowego zniszczonej strefy próbki zaczynu cementowego.

EN

Cement paste produced from CEM I, exposed for 25 days to the attack of saturated ammonium chloride solution, was examined using the macroscopic and microscopic methods, as well as subjected to the phase composition determination. The semi-quantitative estimation of porosity and phase contents was presented. The distribution of porosity was discussed in terms of altered phase composition in the destructed area of sample.

4

Numerical analysis of chloride corrosion of reinforced concrete

58%

German M. , Zaborski A.

|

2011

|

tom R. 108, z. 1-B

47-59

EN

The phenomenon of corrosion can be divided in two stages: the initiation and propagation phases. The initiation phase analysis considers a chloride ions flux described by Nernst-Planck equation. Following the results of initiation phase, a numerical analysis of corrosion propagation phase has been performed. The propagation phase is the time, when corrosion cell is formed. As a result of current flowing through reinforcement, the corrosion products are accumulated at the steel-concrete interface, what generates the tensile stresses in concrete, causing cracking. On the surface longitudinal cracks and concrete splitting are observed. This leads to the loss of strength of the element.

PL

Zjawisko korozji może być podzielone na dwa etapy: inicjacji i propagacji. Analiza fazy inicjacji obejmuje dotyczy przepływu jonów chlorkowych, który został opisany równaniem Nernsta-Plancka. Na podstawie uzyskanych rezultatów dokonano analizy fazy propagacji korozji. Podczas fazy propagacji korozji utworzone zostaje ogniwo korozyjne, w wyniku czego przez zbrojenie przepływa prąd. Pręt zbrojeniowy ulega korozji, a jej produkty są gromadzone na styku stal-beton. W betonie generowane są naprężenia rozciągające, powodujące zarysowanie widoczne na powierzchni betonu. Korozja chlorkowa prowadzi do zarysowanie, odprysków betonu, utraty przyczepności między stalą i betonem oraz utratą nośności elementu.