An Influence of Ageing on the Structure, Corrosion Resistance and Hardness of High Aluminum ZnAl40Cu3 Alloy

100%

Michalik R. , Tomaszewska A.

Archives of Metallurgy and Materials

2016

tom Vol. 61, iss. 1

289--294

Zn-Al-Cu alloys are used primarily because of their tribological properties as an alternative material for bronze, cast iron and aluminum alloy bearings and as a construction material. Particularly interesting are high aluminum zinc alloys. Monoeutectic zinc and aluminum alloys are characterized by the highest hardness, tensile strength and wear resistance of all of the zinc alloys. A significant problem with the use of the Zn-Al-Cu alloys is their insufficient resistance to electrochemical corrosion. Properties of Zn-Al-Cu alloys can be improved by heat treatment. The purpose of examination was to determine the effect of heat treatment (aging at various temperatures) on the microstructure and corrosion resistance of the ZnAl40Cu3 alloy. The scope of the examination included: structural examinations, determination of hardness using Brinell’s method and corrosion resistance examinations. Ageing at higher temperatures causes a creation of areas where is an eutectoid mixture. The study showed that ageing causes a decrease in hardness of ZnAl40Cu3 alloy. This decrease is even greater, when the temperature of ageing is lower. The studies have shown a significant influence of ageing on the corrosion resistance of the alloy ZnAl40Cu3. Maximum corrosion resistance were characterized by the sample after ageing at higher temperatures.

Wpływ składu chemicznego na odporność korozyjną stopu ZnAl22Cu3

100%

Michalik R. , Tomaszewska A.

Ochrona przed Korozją

2013

tom nr 12

566--569

Przeprowadzono badania wpływu dodatku krzemu oraz modyfikacji pierwiastkami ziem rzadkich na odporność korozyjną stopu ZnAl22Cu3 w 3% roztworze NaCl. Wykonano badania potencjodynamiczne oraz badania potencjostatyczne. Badania wykazały, że dodatek krzemu oraz dodatek krzemu z jednoczesną modyfikacją pierwiastkami ziem rzadkich stopu ZnAl22Cu3 wpływa na jego odporność na korozję. W przypadku polaryzacji anodowej dla mniejszych wartości potencjału wpływ dodatku krzemu jest korzystny, dla polaryzacji dla większych wartości potencjału – niekorzystny.

The influence of an addition of silicon and rare earth elements on the corrosion resistance of ZnAl22Cu3 alloy in 3% NaCl has been examined. Potentiodynamic and potentiostatic tests were carried out .Studies have shown that the addition of silicon alone and silicon with rare earth elements to ZnAl22Cu3 alloy influences its corrosion resistance. At lower anodic polarization potential, the addition of silicon is beneficial for the alloy’s corrosion resistance, while at higher polarization potential, the addition of silicon has an adverse effect.

Effect of TiB2 on tribological properties of as-cast Zn-Al-Cu/SiC composites using Taguchi and ANOVA techniques

63%

Chebolu R. , Nallu R. , Chanamala R.

Composites Theory and Practice

2022

tom R. 22, nr 2

79--86

The present study presents an evaluation of the tribological properties of the as-cast Zn-Al-Cu alloy-based hybrid metal matrix composite and also the effect of the weight percent of TiB2. The hybrid composites were fabricated using ultrasonic assisted stir casting with 5 wt.% silicon carbide (SiC) and varying X wt.% (0, 5, 10) of titanium diboride (TiB2). A pin-on-disc type tribometer was used to ascertain the tribological properties like the wear rate and coefficient of friction (COF). The influence of various parameters like the weight percentage of TiB2 particles (0, 5 and 10 %), loads (10, 20 and 30 N) and sliding speeds (0.25, 0.5 and 1 m/s) on the tribological behaviour was determined using the L9 orthogonal array for Taguchi and ANOVA.

Wpływ obróbki cieplnej na odporność korozyjną stopu ZnAl22Cu3 w 3% NaCl

63%

Michalik R. , Woźnica H.

Ochrona przed Korozją

2012

tom nr 12

564-567

Celem pracy było określenie wpływu obróbki cieplnej na odporność korozyjną stopu ZnAl22Cu3 w 3% roztworze NaCl. Badaniom poddano niemodyfikowany stop ZnAl33Cu3. Badany stop poddano: wygrzewaniu w temperaturze 185oC w czasie 10 godzin z chłodzeniem w wodzie, wygrzewaniu w temperaturze 385oC w czasie 10 godzin z chłodzeniem w wodzie oraz wygrzewaniu w temperaturze 385oC w czasie 10 godzin z następnym wygrzewaniem w temperaturze 175oC w czasie 10 godzin z chłodzeniem w powietrzu. Przeprowadzono badania potencjodynamiczne oraz potencjostatyczne w 3% roztworze NaCl. Po badaniach korozyjnych przeprowadzono badania stanu powierzchni próbek. Badania wykazały iż najwyższą odpornością na korozję charakteryzowały się próbki wygrzewane w 385oC/10 h natomiast najgorszą w 185oC/10 h.

The purpose of this examination was to determine the influence of heat treatment on ZnAl22Cu3 alloy corrosion resistance in the 3% NaCl solution. The subject of examination was unmodified ZnAl33Cu3 alloy. The tested alloy was: heated at the temperature of 185oC during10 hours with cooling in water, heated at the temperature of 380oC during 10 hours with cooling in water and heated at the temperature of 385oC for 10 hours followed by heating at the temperature of 175oC with cooling in the water. Potentiodynamic and potentiostatic tests were carried out in the 3% NaCl solution. After corrosion tests examination of the surface of the samples were conducted. Examinations have shown that the highest corrosion resistance is characterized by an alloy after heating at the temperature of 385oC/10h and the lowest after heating at 185oC/10 h.