Two poly(L-lactide-co-trimethylene carbanates)s having the carbonate content of 15% and 50%, respectively were prepared by ring-opening copolymerization with the use of zirconium acetylacatonate as an initiator. The copolymers were characterized by NMR,GPC, DSC and AFM. Wettability and surface energy of the copolymers were also evaluated. The copolymers were submitted to degradation in phosphate buffered saline at 37 Celcius degrees for 10 weeks. It was shown that degradation mechanism and kinetics depend on chemical structure of the copolymers.
2
Dostęp do pełnego tekstu na zewnętrznej witrynie WWW
Opisano syntezę liniowych poli(estrouretanów) (PESU) z 4,4`-diizocyjanianu dicykloheksylenometanu, 1,4 - butanodiolu i kopoliestrodioli z L-laktydu (LA) i poli(e-kaprolaktono)diolu (PCL, Mn 560 g/mol). Kopoliestrodiole o Mn 760, 1250 i 3390 g/mol otrzymano przy trzech stosunkach masowych PLA i PCL w obecności oktanianu Sn (II). PESU otrzymane przy różnych stosunkach molowych komponentów scharakteryzowano przez pomiary twardości, wytrzymałości na rozciąganie i badania degradowalności w buforze fosforanowym o pH = 7,4, w temp. 38 0C. Oznaczono kąty zwilżania wodą, chłonność wody i chłonność oleju roślinnego. Właściwości termiczne PESU określono z użyciem dynamiczno-mechanicznej analizy termicznej (DMTA) i analizy termograwimetrycznej (TGA). Podatność otrzymanych PESU na degradację hydrolityczną porównano z degradowalnością opisanych w literaturze usieciowanych poli(estrouretanów) opartych na kopoliestrotriolach z LA i epsilon-kaprolaktonu.
EN
Synthesis of the linear poly(esterurethanes) (PESUs) from the cycloaliphatic diisocyanate, 1,4-butane diol and copolyesterdiols from L-lactide (LA) and poly(e-caprolactone) diol (PCL, Mn 560 g/mol) have been described. The copolyester diols of Mn 760, 1250 and 3390 g/mol were prepared with three mass proportion of LA and PCL in the presence of Sn (II) octoate. PESUs obtained with different molar ratio of the components were characterized by hardness, tensile-stress properties and degradability in the phosphate buffer solution of pH = 7,4 at temp. 38 0C. The contact angles with water, sorption of water and vegetable oil were denoted. Thermal properties of PESUs were investigated by dynamic mechanical thermal analysis (DMTA) and by thermogravimetric analysis (TGA). The fitness of PESUs on hydrolytical degradability has been compared with degradability of known crosslinked poly(esterurethanes) from copolyester triols based on LA and epsilon-caprolactone.
JavaScript jest wyłączony w Twojej przeglądarce internetowej. Włącz go, a następnie odśwież stronę, aby móc w pełni z niej korzystać.