Analysis of wear resistance of metallic-reinforced polyurethane resin composites for sheet metal forming

100%

Wiewióra M. , Żaba K. , Kuczek Ł. , Balcerzak M. , Marcin M.

Advances in Materials Science

2024

tom Vol. 24, nr 3(81)

18--29

The paper presents the results of testing the wear resistance and coefficient of friction (COF) tools made of SikaBeresin® F50 polyurethane resin intended for dies and punches for the cold sheet metal forming process. Seven sets of composite tools (rotating rings) additionally reinforced with waste metallic powders from Al and Cu alloys (5-20% by volume) from the dry cutting process of pipes and rods were tested. Wear resistance tests and determination coefficient of friction were carried out using the T-05 block-on-ring tribotester. The tests were performed for heat and corrosion resistant sheets made of nickel alloy AMS5599 (Inconel 625), iron alloy AMS5510 (321) and aluminum alloy sheets AMS4026 (6061-T4). Composite tools with the addition of 20% aluminum powder (A+B+C+20%Al) tested with a specimen of steel alloy AMS5510 and nickel alloy AMS5599 were characterized by the lowest wear resistance. In each case, the composite rotating ring without reinforcements was characterized by the lowest coefficient of friction. The use of Cu powder reinforcements in each case had a positive effect on increasing wear resistance. The best wear resistance of 0.011% was obtained for composite rotating ring with the addition of 10% copper powder paired with specimen of nickel alloy AMS5599 sheet.

Analysis of tribological performance of new stamping die composite inserts using strip drawing test

86%

Żaba K. , Kuczek Ł. , Puchlerska S. , Wiewióra M. , Góral M. , Trzepieciński T.

Advances in Mechanical and Materials Engineering

2023

tom Vol. 40, nr 1

55--62

This article assesses the tribological performance of new composite tool sets for stamping dies. Four sets of composite countersamples were tested. These consisted of polyurethane resin with mineral filler (base variant) and modified with aluminium powder (10wt%) and roving fabric (5wt%). Strip samples for the strip drawing tests were cut from AMS5599 (Inconel 625) corrosion-resistant nickel alloy, AMS5510 (321) corrosion and heat-resistant steel and AMS6061-T4 heat treatable aluminium alloy sheet metals. The influence of the type of sample material on the coefficient of friction (COF) was observed. The smallest values of the COF over the entire range of clamping force values used on AMS5599 and AMS5510 sheets were observed during tests with countersamples made of the base variant of composite. When testing the AMS6061-T4 aluminium alloy sheet, the countersamples modified with roving fabric provided the lowest value of COF, which stabilised at a value of about 0.197 as pressure was increased.

Celem artykułu jest ocena właściwości tribologicznych nowych kompozytowych wkładek do tłoczników. Badaniom poddano cztery zestawy przeciwpróbek kompozytowych składających się z żywicy poliuretanowej z wypełniaczem mineralnym (wariant bazowy) oraz modyfikowanych proszkiem aluminiowym (10% mas.) i tkaniną rowingową (5% mas.). Próbki do testu przeciągania pasa blachy wycięto z blach AMS5599, AMS5510 i AMS6061-T4. Zaobserwowano wpływ rodzaju materiału przeciwpróbki na współczynnik tarcia. Najmniejsze wartości współczynnika tarcia w całym zakresie zmian siły docisku dla blach AMS5599 i AMS5510 zaobserwowano podczas badań z przeciwpróbkami wykonanymi z bazowego wariantu kompozytu. Podczas badania blachy ze stopu aluminium AMS6061-T4 przeciwpróbki modyfikowane tkaniną rowingową zapewniły najmniejszą wartość współczynnika tarcia, która w zakresie ustabilizowanym osiągnęła wartość około 0,197.