Sclerometric and Tribological Properties of Polytetrafluoroethylene with 40% Bronze Content Formed by Electron Beam Irradiation

100%

Barylski A. , Aniołek K. , Kaptacz S.

Tribologia

|

2019

|

tom nr 3

13--17

EN

The paper focuses on the improvement of sclerometric and tribological properties of polytetrafluoroethylene (PTFE) with 40% bronze content implied by irradiation with an electron beam of 10 MeV and a power of 10 kW, in a dose of 26–156 kGy. The results of the study confirm that radiation modification of the PTFE-bronze composite causes structural changes induced by breaking of bonds in long PTFE chains and the branching of the polymer structure. As a result, an increase in such properties as the wear resistance ratio, Wβ, is observed. In addition, sclerometric tests have shown that, with an increase of the absorbed radiation dose, the groove-to-elevation area ratio changes during scratching, which indicates a change in the micromechanism of wear, i.e. the material undergoes ploughing. From the operating point of view, the most important were tribological tests, which were carried out on a pin-on-disc test stand (T-01). The tests showed a nearly fourfold reduction in wear at a load of 20 N and more than a threefold reduction at 40 N. Controlled radiation modification leads to improved properties of the PTFE-bronze composite, which may result in a wider range of its applications.

PL

W pracy skoncentrowano uwagę na poprawie właściwości sklerometrycznych i tribologicznych politetrafluoroetylenu z 40% zawartością brązu implikowanych przez napromieniowanie strumieniem elektronów o energii wiązki 10 MeV i mocy 10 kW oraz dawce 26–156 kGy. Wyniki badań potwierdzają, że modyfikacja radiacyjna, jakiej poddany został kompozyt PTFE–brąz, powoduje zmiany strukturalne wywołane zrywaniem wiązań w długich łańcuchach PTFE oraz rozgałęzianiem się struktury polimeru. W konsekwencji obserwuje się wzrost takich właściwości jak wskaźnik odporności na zużycie Wβ. Badania sklerometryczne wykazały ponadto, że wraz ze wzrostem pochłoniętej dawki promieniowania zmienia się stosunek powierzchni wyżłobienia i wypiętrzenia podczas zarysowania, co świadczy o zmianie mikromechanizmu zużycia – materiał ulega bruzdowaniu. Z punktu widzenia eksploatacyjnego najważniejsze było przeprowadzenie badań tribologicznych, które wykonano na stanowisku trzpień–tarcza (T-01). Badania wykazały blisko 4-krotne ograniczenie zużycia przy zastosowaniu obciążenia 20 N oraz ponad 3-krotne przy zwiększeniu obciążenia do 40 N. Kontrolowana modyfikacja radiacyjna prowadzi do poprawy właściwości kompozytu PTFE–brąz, co może prowadzić do poszerzenia spektrum jego zastosowań.

2

Inspekcja rozdzielnicy niskiego napięcia za pomocą kamery termowizyjnej na podczerwień

100%

Włóczyk A. , Wawrzyniak S. , Kaptacz S. , Bzowski B.

|

tom nr 9

646--648

PL

Artykuł zawiera wyniki badań z inspekcji dwóch rozdzielnic niskiego napięcia za pomocą kamery termowizyjnej na podczerwień. Dokonano rejestracji obrazów termalnych selektywnie wybranych przedziałów rozdzielnic podczas ich pracy w najwyższym stopniu obciążenia, w trakcie jednej zmiany w dwóch zakładach produkcyjnych.

EN

Given are results of inspections conducted in two LV switchgears with the use of an infrared thermal imaging camera. Made are recordings of thermal images of selectively chosen switchgear compartments during their work in peak-load conditions during one shift at two production plants.

3

Tribological Properties of AAO Coatings Catalytically Modified with Nickel

100%

Bara M. , Korzekwa J. , Niedźwiedź M. , Kaptacz S.

|

tom nr 2

7--20

EN

The purpose of this work is to determine the possibility of modifying oxide coating with nickel in the catalytic process and to verify the tribological properties of the coatings as a result of such modification. The coatings were made on the EN AW-5251 aluminum alloy by electrochemical method. Nickel dispersions were obtained through thermochemical treatment of the coatings. Tribological tests were carried out in a combination of coatings with polymer, cast iron, and steel, in a reciprocating motion on the T-17 tester. The paper presents the results of tribological tests and roughness of AAO coatings modified with nickel, before and after the tribological test. The results of tribological tests were supplemented with SEM tests and statistical analysis. The tests showed the possibility of modifying the AAO coatings with nickel compounds, which, in the case of a sliding combination of the modified coating with steel, causes a significant reduction of friction forces both in the case of technically dry friction and friction with lubrication.

PL

Celem niniejszej pracy było określenie możliwości modyfikacji powłoki tlenkowej niklem w procesie katali tycznym i weryfikacja właściwości tribologicznych powłok w wyniku takiej modyfikacji. Powłoki wytworzo no na stopie aluminium EN AW-5251 metodą elektrochemiczną. Dyspersje niklu uzyskano w wyniku procesu obróbki cieplno-chemicznej powłok. Testy tribologiczne przeprowadzono w skojarzeniu powłok z polime rem, żeliwem i stalą, w ruchu posuwisto-zwrotnym na testerze T-17. W pracy przedstawiono rezultaty badań tribologicznych oraz chropowatości powłok AAO modyfikowanych niklem, przed i po teście tribologicznym. Wyniki badań tribologicznych uzupełniono o badania SEM oraz analizę statystyczną. Badania wykazały moż liwość modyfikacji powłok AAO związkami niklu, które w przypadku skojarzenia ślizgowego modyfikowa nej powłoki ze stalą powodują znaczne obniżenie sił tarcia zarówno w przypadku tarcia technicznie suchego, jak i tarcia ze smarowaniem.