Characterization of IN713C superalloy microstructure after high temperature creep test by LM, SEM and STEM

100%

Szczotok A. , Kościelniak B.

tom Vol. 37, nr 2

50--58

This work focuses on the influence of creep phenomenon on the cast IN713C nickel-based superalloy. The carrot-shape IN713C superalloy castings were produced in an investment casting cluster mould and the creep test samples were then prepared from the castings. The creep tests were carried out in order to investigate processing–microstructure–property relationships. The resultant macro- and microstructures were observed and characterized after the creep tests using light microscopy, scanning electron microscopy and scanning transmission electron microscopy. The aim of the analysis was to reveal the changes in the microstructure that occurred as a result of the creep and to identify the phases that participate in voids formation, and crack generation and propagation during the creep tests. It was confirmed that the creep resistance of the IN713C superalloy is negatively affected by some structural characteristics such as porosity, (γ + γ′) eutectic or carbide precipitates along the grain boundaries. Our work confirms that a combination of thermal conditions with a tensile force affected the microstructure of IN713C nickel-based superalloy causing changes in morphologies of the existing precipitations and phase transformations, as in the case of the carbides. Additionally, carbide sulphides containing primarily Zr and intermetallic phase including mainly Ni and Zr were observed.

Artykuł dotyczy wpływu zjawiska pełzania na strukturę odlewniczego nadstopu na osnowie niklu IN713C. Makro- i mikrostrukturę materiału uzyskaną w efekcie przeprowadzonej próby pełzania obserwowano przy różnych powiększeniach. Celem badań było ujawnienie zmian struktury, jakie pojawiły się w efekcie pełzania i zidentyfikowanie faz, które brały udział w powstawaniu nieciągłości materiału oraz generowaniu i propagacji pęknięć podczas próby pełzania.

Characteristic of cyclic oxidation of chosen austenitic steels in a steam atmosphere

80%

Kościelniak B. , Smoła G. , Grzesik Z.

tom nr 1

2--5

The aim of the study was to evaluate the oxidation resistance of chromium-nickel austenitic steels in an atmosphere, which contains oxygen and steam at a temperature of 750oC. The oxidation test of steel samples X2CrNiMo17-12-2, X6CrNiMoTi17-12-2, Super 304H and HR3C was carried out in a cyclic mode, made up of 100 cycles trials of 2 hours. The results show the mass changes of steels caused by a cyclic oxidation. The morphology and chemical composition of the oxide layer formed on the surface of tested samples were also described. It has been proved that under these conditions HR3C steel shows the best heat resistance and X2CrNiMo17-12-2 steel presents the worst tendency of oxides to defoliation.

Celem badań była ocena odporności na utlenianie austenitycznych stali chromowo-niklowych w atmosferze zawierającej tlen i parę wodną w temperaturze 750oC. Utlenianie próbek ze stali X2CrNiMo17-12-2, X6CrNiMoTi17-12-2, Super 304H i HR3C przeprowadzono w sposób cykliczny, składający się ze 100 cykli trwających 2 godziny. Przedstawiono wyniki zmiany masy materiałów wywołanych cyklicznym utlenianiem. Scharakteryzowano również morfologię i skład chemiczny warstw tlenkowych powstałych na powierzchni badanych stali. Wykazano, że najlepszą żaroodporność w tych warunkach posiada stal HR3C, a najgorszą stal X2CrNiMo17-12-2 wykazująca skłonność do defoliacji tlenków.

Selective Corrosion of Al2Cu Intermetallic Phase in Orthophosphoric Acid Aqueous Solutions

71%

Kwolek P. , Gradzik A. , Szeliga D. , Kościelniak B. , Kwolek P. , Gradzik A. , Szeliga D. , Kościelniak B.

nr 4

Evaluation of Carbides in Turbine Blade Made of IN713C Superalloy After Hot Isostatic Pressing

50%

Kościelniak B. , Roskosz S. , Cwajna J.