Growth and characterization of Cr:SrGdGa₃O₇ and Cr:SrLaGa₃O₇ single crystals

100%

Kaczmarek S. M. , Berkowski M. , Jabłoński R. , Pracka I. , Kwaśny M. , Świrkowicz M.

1998

tom Vol. 47, nr 7-8

141-151

Growth and recharging processes of chromium ions in SrGdGa₃O₇ and SrLaGa₃O₇ single crystals incorporated during growth or doping by diffusion (only for SrLaGa₃O₇ crystal) were analyzed. The annealing at 1000°C in air and ionizing with gamma rays (doses from 10³ to 10⁵ Gy) and protons (10¹⁴ cm⁻² only for SrGdGa₃O₇ crystal) were performed. Different kinds of chromium ions valency, from two to four, were found. Electron spin resonance measurements in the temperature range 5-300 K with the use of Brucker spectrometer were also done.

Analizowano proces wzrostu i procesy zmiany walecyjności jonów chromu w monokryształach SrGdGa₃O₇ i SrLaGa₃O₇. Chrom wprowadzono podczas procsu wzrostu oraz w wyniku procesu dyfuzji (tylko dla kryształu SrLaGa₃O₇). Przeprowadzono wygrzwanie w temperaturze 1000°C w powietrzu oraz naświetlania kwantami gamma (dawki 10³ - 10⁵ Gy) i protonami (10¹⁴ cm⁻² tylko dla kryształu SrGdGa₃O₇). Stwierdzono występowanie jonów chromu o walencyjności od 2 do 4. Przeprowadzono również pomiary elektronowego rezonansu spinowego w zakresie temperatur 5-300 K z wykorzystaniem spektrometru firmy

Influence of γ-radiation on Dy³⁺ doped LiNbO₃ single crystals

100%

Kaczmarek S. M. , Łukasiewicz T. , Pracka I. , Jabłoński R. , Boulon G. , Kaczmarek B. , Warchoł S.

1998

tom Vol. 47, nr 7-8

101-112

Absorption measurements of the "as grown", gamma irradiated and thermal annealed LiNbO₃ crystals doped with Dy³⁺ ions for several activator concentrations were performed. It was stated that positions occupied by Dy³⁺ ions in LiNbO₃ lattice depend on the impurity concentration. May be large ion radius of Dy³⁺ ion makes, that it locates in interstitial position as Dy²⁺. Dy²⁺ ions after the exposure with gamma rays, as well as after the thermal annealing, change their valency and become Dy³⁺. The ESR measurements were performed for trivalent dysprosium. There were no changes in ESR lines before and after gamma exposure performed at room temperature, but after UV irradiation with an mercury lamp changes were very clar.

Zbadano wpływ naświetlania domieszkowanych dysprozem kryształów LiNbO3 kwantami gamma (⁶⁰Co, 1.25 MeV) na ich charakterystyki optyczne. Przeprowadzono badania EPR przed i po naświetleniu kwantami y (dawka 10³-10⁶ Gy) oraz przed i po naświetlaniu UV z lampy rtęciowej. Centra barwne powstające po naswietlaniu kryształu niobianu litu wskazują na obecność w nich jonów Dy²⁺, które lokują się w silnie zdefektowanych obszarach kryształu, nie dając żadnych pasm w widmie absorpcji. Ich obecność staje się zauważalna dopiero po naświtlaniu kryształu kwantami gamma lub UV. Koncentracja jonów Dy²⁺ zależy istotnie od założonej koncentracji jonów Dy³⁺.

Electronic hot bands in Yb³⁺ doped LiNbO₃ single crystals co-doped with rare-earth ions under influence of [gamma]-quanta

84%

Kaczmarek S. M. , Tsuboi T. , Boulon G. , Włodarski M. , Pracka I. , Podgórska D. , Czuba M. , Kaczmarek M. , Warchoł S.

tom Vol. 52, nr 12

5-25

EPR, absorption and emission spectra have been studied for Yb³⁺ - doped LiNbO₃ single crystals and Yb³⁺/Nd³⁺- Yb³⁺/Er³⁺ - and Yb³⁺/Pr³⁺ - codoped LiNbO₃ crystals before and after γ-irradiation with a dose of 10⁵ - 10⁷ Gy. As a reference we also measured the absorption of pure and single LiNbO₃ crystals doped with Er³⁺, Nd³⁺, and Pr³⁺ ions. The absorption measurements were performed versus temperature in the range of 190 nm - 3100 nm from 15 K to 292 K. We observed rare-earth ions substitute for Li⁺ sites in Er³⁺ - and Yb³⁺ - co-doped crystals, while also at Nb⁵⁺ sites in the case of Pr³⁺ - and Nd³⁺ - co-doped crystals. Niobium sites give rise to absorption bands by means of absorption of OH⁻ line. Moreover, after gamma irradiation, due to a large discrepancy between ionic radii of Nd³⁺ or Pr³⁺ dopant and Li⁺ or Nb⁵⁺ sites, intense additional absorption bands in UV-VIS were observed due to the effect of oxygen vacancy recharging (F-centres) and Nb⁴⁺ polaron arising. Hot absorption bands due to the electronic transition from thermally populated levels were observed at the low energy side of the 980 nm sharp Yb³⁺ line. Temperature dependence observed for the hot bands is explained by an energy level calculatipon. It is understood by electronic transition from the thermally populated ²F⁷/². Stark levels to the excited ²F⁵/² level. The position of the Yb³⁺ ²F⁷/² ²F⁵/² first resonant line was observed to be a slightly different among the co-doped crystals. This is due to the perturbation of Yb³⁺ by co-doped rare-earth ion which is located at the neighborhood of the Yb³⁺. Comparative calculations were performed using factor analysis method for the absorption spectrum of Er³⁺, Yb³⁺ : LiNbO₃ single crystal, to confirm the mixed nature (vibrational & electronic) of 1→5 electron transition.

Badano pasma absorpcji i emisji monokryształów Yb³⁺:LiNbO₃ oraz współdomieszkowanych monokryształów Yb³⁺/Nd³⁺, Yb³⁺/Er³⁺, Yb³⁺/Pr³⁺: LiNbO₃ przed i po naświetleniu ich kwantami gamma dawką 10⁵ - 10⁷ Gy. Porównawczo zmierzono również odpowiednie widma monokryształów LiNbO₃ domieszkowanych jonami Er³⁺, Nd³⁺ oraz Pr³⁺. Badania przeprowadzano w funkcji temperatury w obszarze 190 nm-3100 nm od 16 K do 292 K. Obserwowano, że jony ziem rzadkich podstawiają się w położeniu Li⁺ w kryształach współ-domieszkowanych Er³⁺ oraz Yb³⁺, natomiast w położenia Nb⁵⁺ w kryształach domieszkowanych Pr³⁺ oraz Nd³⁺. Położenia Nb⁵⁺ dają wkład do widma absorpcji w postaci linii obsorpcji jonów OH⁻ . Ponadto, z uwagi na duży rozrzut promieni jonowych Nd³⁺ lub Pr³⁺ oraz Li⁺ lub Nb⁵⁺, po naświetleniu kwantami gamma, obserwowano intensywne dodatkowe pasma absorpcji w obszarze UV-VIS, będące efektem przeładowania wakansów anionowych (centra F) oraz powstania polaronu Nb⁴⁺. Obserwowano występowanie elektronowych pasm termicznych pochodzących od termicznie zapełnionych poziomów elektronowych po niskoenergetycznej stronie ostrej linii przejścia elektronowego Yb³⁺ 980 nm. Zależność temperaturową dla tych pasm wyjasniono poprzez obliczenia poziomów energetycznych jonu Yb³⁺. Obserwowano wielo-fotonową relaksację z pierwszego poziomu przejścia termicznego (1004 nm) do stanu podstawowego za sprawą dwóch zlokalizowanych fotonów o energiach: 80 cm⁻¹ oraz 140 cm⁻¹. Więcej zlokalizowanych fotonów obserwowano w kryształach po ich naświetleniu kwantami gamma. Przeprowadzono analizę porównawczą widma absorpcji monokryształu Er³⁺, Yb³⁺:LiNbOO₃ metodą analizy czynnikowej, aby uzyskać potwierdzenie mieszanej natury (wibronowo-elektronowej) przejścia elektronowego 1→5.