Kinetics of static recrystallization in the coarse-grained Fe–40 at.%Al–Zr–B alloy

100%

Schindler I. , Kopeček J. , Kawulok P. , Jabłońska M. , Hadasik E. , Jóźwik P. , Opěla P. , Hanus P. , Polkowski W. , Bojar Z.

2017

tom Vol. 17, no. 4

816--826

The aim of works was to describe mathematically the kinetics of static recrystallization of the alloy type Fe–40 at.%Al–Zr–B (with 24.6 Al–0.01 B–0.18 Zr–0.01 C in wt.%) with the coarse-grained structure. The microstructure of the laboratory castings made of this extremely brittle alloy was homogenized by hot rolling of the material in the protective capsules and by the long-term annealing at 1200 °C. An initial microstructure with average grain size 0.77 ± 0.27 mm was obtained. Based on the isothermal plastic deformation tests and EBSD analysis, the static recrystallization kinetics of the prepared coarse-grained B2 iron aluminide after strain 0.20 was mathematically described. Recrystallized fraction depends on deformation/annealing temperature (900–1100 °C) as well as on annealing time. The activation energy of static recrystallization was calculated as 255 kJ mol−1. Competition between dynamic recovery and static recrystallization was proved after strain 0.35 and annealing temperature 1100 °C. Static recrystallization starts relatively easily in the studied alloy, but a very long-term annealing is quite necessary for the complete course of recrystallization. The mean size of recrystallized grains falls with the decreasing annealing temperature (0.47 ± 0.15 mm for temperature 1100 °C, and 0.22 ± 0.04 mm for 900 °C). Even at a temperature of 1200 °C the annealing after deformation should last approx. 1 min for obtaining the fully recrystallized microstructure. That is why the standard hot forming technologies should be combined by an interpass annealing in order to refine sufficiently the coarse grains.

Optimization of Laboratory Hot Rolling of Brittle Fe-40at.%Al-Zr-B Aluminide

100%

Schindler I. , Hadasik E. , Kopeček J. , Kawulok P. , Fabík R. , Opěla P. , Rusz S. , Kawulok R. , Jabłońska M.

Archives of Metallurgy and Materials

2015

tom Vol. 60, iss. 3A

1693--1701

Use of the protective steel capsules enabled to manage the laboratory hot flat rolling of the extremely brittle as-cast aluminide Fe-40at.%Al-Zr-B with the total height reduction of almost 70 %. The hot rolling parameters were optimized to obtain the best combination of deformation temperature (from 1160°C up to 1240°C) and rolling speed (from 0.14 m·s−1 to 0.53 m·s−1). The resistance against cracking and refinement of the highly heterogeneous cast microstructure were the main criteria. Both experiments and mathematical simulations based on FEM demonstrated that it is not possible to exploit enhanced plasticity of the investigated alloy at low strain rates in the hot rolling process. The heat flux from the sample to the working rolls is so intensive at low rolling speed that even the protective capsule does not prevent massive appearance of the surface transverse cracking. The homogeneity and size of product’s grain was influenced significantly by temperature of deformation, whereas the effect of rolling speed was relatively negligible. The optimal forming parameters were found as rolling temperature 1200°C and the rolling speed 0.35 m·s-1. The effective technology of the iron aluminide Fe-40at.% Al-Zr-B preparation by simple processes of melting, casting and hot rolling was thus established and optimized.

Zastosowanie ochronnych stalowych kapsuł pozwoliło na przeprowadzenie laboratoryjnego walcowania na gorąco pasm z niezwykle kruchego odlewanego aluminidku żelaza (stopu na osnowie fazy międzymetalicznej) Fe-40at.%Al-Zr-B, które umożliwiło redukcję wysokości o prawie 70%. Parametry walcowania na gorąco były dostosowywane celem uzyskania korzystnego zakresu temperatury odkształcenia (od 1160°C do 1240°C) oraz prędkości walcowania (od 0.14 m·s−1 do 0.53 m·s−1) dla otrzymania pasma bez pęknięć i rozdrobnienia silnie niejednorodnej mikrostruktury odlewu. Zarówno eksperymenty jak i matematyczne symulacje oparte na MES wykazały, że niemożliwe jest uzyskanie dobrej plastyczności badanego stopu przy niskich prędkościach odkształcenia podczas walcowania na gorąco. Strumień ciepła płynący z próbki na walce jest tak intensywny przy małej prędkości walcowania, że nawet kapsuła ochronna nie zapobiega pojawieniu się powierzchniowych pęknięć poprzecznych. Jednorodność i rozmiar ziarn w materiale silnie zależy od temperatury odkształcenia, podczas gdy wpływ prędkości walcowania jest relatywnie niewielki. Optymalne parametry kształtowania stopu to: temperatura 1200°C oraz prędkość walcowania 0.35 m·s−1. Skuteczna technologia przygotowania aluminidku żelaza Fe-40at.%Al-Zr-B w prostym procesie topienia, odlewania i walcowania na gorąco została w ten sposób ustalona i zoptymalizowana.