Some properties of chromized stainless steels

100%

Pałka K. , Weroński A.

Inżynieria Materiałowa

|

2004

|

tom R. XXV, nr 3

V-VI

EN

Materials used for constructions in food processing industry should meet mechanical specifications and sanitary requirements. The most often used steels AISI304 and 316L have similar mechanical characteristics, but the corrosion resistance of 316L stainless steel is considerably better. On the other hand the price of 316L steel is twice higher. The advantageous solution with minimal investment cost is chemical modification of stainless steel surface layer. Main directions of chemical modifications of surface layers were characterised in this paper. In this paper there were also presented effects of chromizing of steel type AISI316L in order to increasing erosion - corrosion resistance. There were analysed structures; mechanical characteristics and durability of chromized stainless steel.

PL

Materiały używane w konstrukcjach dla przemysłu spożywczego winny charakteryzować się wysoką wytrzymałością mechaniczną przy spełnieniu wymagań sanitarno - higienicznych. Główne grupy stali austenitycznych: 18/8 oraz 17/14+Mo, stosowane najczęściej w budowie maszyn dla przemysłu spożywczego, posiadają zbliżone właściwości wytrzymałościowe [1÷3], natomiast odporność korozyjna stali 17/14+Mo jest istotnie wyższa ze względu na większą zawartość niklu oraz 2% dodatek molibdenu [2,4]. Jednakże stal ta jest dwukrotnie droższa od stali typu 18/8 Korzystnym rozwiązaniem przy minimalnych kosztach inwestycyjnych jest modyfikacja składu chemicznego warstwy wierzchniej stali austenitycznych. W pracy scharakteryzowano główne kierunki modyfikacji składu chemicznego. Przedstawiono efekty chromowania stali typu AISI316L w aspekcie podwyższania trwałości erozyjno -korozyjnej. Przeanalizowano uzyskane w efekcie chromowania struktury i uzyskaną charakterystykę mechaniczną pod kątem prognozowania trwałości warstw.

2

Enzymatic reductive amination of p-hydroxy- and phenylpyruvic acids as a method of synthesis of L-tyrosine and L-phenylalanine labelled with deuterium and tritium

100%

Pałka K. , Kańska M.

|

tom Vol. 57, No. 3

383-387

EN

We report the synthesis of isotopomers of L-phenylalanine and L-tyrosine selectively labelled with hydrogen isotopes in the 2-position of the side chain. The deuterium or tritium label was introduced using reductive amination activity of enzyme L-phenylalanine dehydrogenase (EC 1.4.1.20). This way p-phenylpyruvic acid was converted into [2-2H]-, [2-3H]-, and doubly labelled [2-2H/3H]-isotopomers of L-phenylalanine, using deuteriated, tritiated, and mixed (DTO) incubation media, respectively. Similarly, p-hydroxyphenylpyruvic acid was converted into [2-2H]-, [2-3H]-, and [2-2H/3H]-L-tyrosine. Deuterium labelled isotopomers of L-phenylalanine and --tyrosine can be used as markers in the investigation of abnormal metabolism of these amino acids observed in patients with inborn genetic diseases such as phenylketonuria and tyrosinemia.

3

Korozja wżerowa stali 18/8 stosowanej w płytowych wymiennikach ciepła

100%

Pałka K. , Weroński A.

|

2001

|

tom nr 8

205-208

PL

Przeprowadzono analizę uszkodzeń spowodowanych korozją wżerową w płytowych wymiennikach ciepła w przemyśle spożywczym. Wykonano badania makroskopowe i mikroskopowe oraz badania korozji wżerowej metodą potencjodynamiczną. Sformuowano wnioski o wpływie poszczególnych środowisk i warunków realizacji na wartości potencjałów charakterystycznych.

EN

The analysis of damages caussed by pitting corrosion in plate heat exchangers for food industry was drown. The macro- and microscopic observations were executed also pitting corrosion researches using potentiodynamic method were performed. The conclustions of influence of environments and researches conditions on values of characteristic potentials were drawn.

4

Stan naprężeń w warstwie wierzchniej stali austenitycznych chromowanych dyfuzyjnie

100%

Pałka K. , Weroński A.

Inżynieria Materiałowa

|

2006

|

tom Vol. 27, nr 3

502-504

PL

Dyfuzyjne wytwarzanie warstw chromowych na stalach austenitycznych prowadzi do zmian struktury stali, głównie poprzez rozpuszczanie chromu w roztworze stałym. Równoważnik chromu ulega podwyższeniu, co w konsekwencji prowadzi do zmiany struktury z austenitycznej na dwufazową austenityczno - ferrytyczną. Możliwe jest również powstawanie wydzieleń faz międzymetalicznych (FeCr, CrNi2) oraz węglików chromu (głównie typu Cr23C6), których obecność ma wpływ na umocnienie warstwy wierzchniej, podwyższenie jej twardości a w konsekwencji na wzrost trwałości eksploatacyjnej. W strefie przypowierzchniowej stali chromowanej stężenie Cr wzrosło do poziomu ok. 24% przy powierzchni, łagodnie zmniejszające się wgłąb materiału do poziomu zawartości Cr w materiale wyjściowym. Oceniono grubość strefy wzbogaconej istotnie w chrom na poziomie 1300 um. Twardość powierzchniowa wzrosła z ok. 160 HV do ok. 400 HV. Wzrost twardości powierzchni związany jest z umocnieniem roztworowym oraz obecnością wydzieleń. Efektem tego jest również powstanie określonego stanu naprężeń w warstwie wierzchniej. W artykule przedstawiono badania stanu naprężeń w warstwie wierzchniej chromowanej stali austenitycznej przeprowadzone metodą dyfrakcji rentgenowskiej. Wyniki badań potwierdziły istnienie stanu naprężeń ściskających o sumarycznej wartości na poziomie 300MPa.

EN

Formation of diffusion layers of chromium on austenitic stainless steel leads to structural changes as effect of dissolving of chromium in solid solution. The chromium equivalent is increased which leads to forming of two phase structure (y+l). Forming of intermetallic phases or carbides there are also possible which has an influence on strengthening of surface layer. In this paper there were presented effects of the chemical constitution modifications of austenitic steels surface layers to increase a corrosion and erosion resistance. Mechanisms of strengthening there were also discussed (Fig. 1). There were conducted researches of hardness and hardness distribution (Fig. 2) and value of stresses in surface layer obtained in X-ray diffraction method w-sin2y (Fig.3). Hardness of surface increased from 160HV to over 400HV as effect of chromizing and heat treatment. The X-ray diffraction research confirmed the existence of state of compression stresses with the value of over 300 MPa.

5

Mikrotwardość materiałów kompozytowych do wypełnień w zębach stałych

80%

Pałka K. , Niewczas A. , Bieniaś J.

|

tom Vol. 11, no. 77-80

36--38

6

In vitro evaluation of selected properties of new flow-type dental composite

80%

Pałka K. , Wysocka S. , Belcarz A.

|

tom Vol. 19, no. 138 spec. iss.

74

7

Microhardness of restorative composites after exposure in physiological solution

80%

Pałka K. , Bieniaś J. , Niewczas A. , Muzyka M.

|

tom R. 9, nr 1

49-52

EN

Restorative materials used in dentistry are required to have long-term durability in the oral cavity. In some cases the interaction of these materials with oral fluids may involve dissolution or degradation of surface layers. Such a fluid absorption may affect the mechanical properties of the materials and inflict damaging dimensional changes. This study was conducted to compare the effect of 4-week storage period in physiological solution on the surface microhardness measured in Vickers units, between materials with micro- and nanofillers. Vickers microhardness was assessed in two nanofiller materials: Filtek Supreme and Grandio and two of micro filler materials: Filtek Silorane and Gradia stored in physiological solution at 37°C for 4 weeks. Measurements were taken at 1st, 14th and 28th day. The statistical evaluation was done by one-way analysis of variance. Materials with nanofiller showed a higher microhardness at the beginning of the study as compared with the materials with microfillers. The microhardness of Filtek Supreme significantly diminished in the final stage of the study, whereas that of Grandio showed decreasing tendency but without significant difference. Similar changes were observed for Gradia, however, they exhibit a much lower microhardness throughout the study period. Filtek Silorane based on the new silorane resin manifested different changes of microhardness as compared with other materials tested. Microhardness of Filtek Silorane increased to 65.6 HV0,02 at 14 days of storage, then slightly decreased to 61.56 HV0.02 at the end of the test period. The results suggest that the amount of filler did not appear to improve the surface microhardness of materials. Restorative materials based on Bis-GMA matrix showed influence of storage time in physiological solution on microhardness value. Results obtained for Filtek Silorane showed the lack of microhardness reduction caused by stability of siloraneresin matrix in water environment. Keywords: restorative composite materials, micro and nanofillers, Vickers microhardness, storage

PL

Wymagania stawiane kompozytom stomatologicznym dotyczą dużej trwałości w warunkach panujących w jamie ustnej. W niektórych przypadkach interakcje ze środowiskiem jamy ustnej mogą wywołać degradację powierzchni kompozytowych materiałów wypełnień. Celem niniejszej pracy było określenie wpływu 4-tygodniowej ekspozycji w roztworze fizjologicznym na mikrotwardość materiałów kompozytowych. Do badań wytypowano materiały z mikrowypełniaczem - Filtek Silorane i Gradia oraz z nanowypełniaczem - Filtek Supreme i Grandio. Pomiary mikrotwardości wykonano metodą Vickersa przy obciążeniu 0,1962 N w 24 godz. po utwardzeniu oraz po 14 i 28 dniach ekspozycji w soli fizjologicznej w temperaturze 37°C. Wyniki oceniano statystycznie z zastosowaniem jednoelementowej analizy wariancji przy p < 0,05. Kompozyty z nanowypełniaczem wykazywały wyższą początkową twardość niż materiały z wypełniaczem mikro. Dla kompozytu Filtek Supreme obserwowano statystycznie istotne obniżenie twardości po 14 i 28 dniach w stosunku do mierzonej po utwardzaniu. Kompozyt Grando wykazuje również tendencję obniżania mikrotwardości, również istotną statystycznie po 14 i 28 dniach w stosunku do wartości początkowej. Materiały z mikrowypełniaczem wykazują niższą twardość oraz mniejsze zmiany mikrotwardości, jednakże odchylenia te nie są statystycznie istotne. Mikrotwardość kompozytu Filtek Silorane zwiększyła się do 65,6 HV0,02 po 14 dniach ekspozycji, a następnie nieznacznie obniżyła do 61,56 HV0,02 w ostatnim dniu testu. Uzyskane wyniki wskazują na brak jednoznacznej zależności wpływu ilości wypełniacza na mikrotwardość kompozytów stomatologicznych. Kompozyty na bazie żywicy Bis-GMA wykazują istotne zmiany mikrotwardości po ekspozycji w soli fizjologicznej. Wyniki uzyskane dla kompozytu Filtek Silorane wskazują na brak zmian w mikrotwardości, wynikający ze stabilności żywicy siloranowej w roztworach wodnych.

8

Wpływ regulacji pracy wentylatorów na równomierność rozkładu strumienia powietrza w tunelu aerodynamicznym

71%

Komarnicki P. , Romański L. , Bieniek J. , Dębowski M. , Pałka K.

|

tom R. 17, nr 2, t. 1

155--165

PL

W artykule przedstawiono badania eksperymentalne charakteru przepływu strumienia powietrza w otwartym tunelu aerodynamicznym z zamkniętą komorą pomiarową, w którym profil prędkości regulowano płynnie przez 9 niezależnych wentylatorów osiowych. Testowanie tunelu aerodynamicznego przeprowadzono dwuetapowo. W pierwszym etapie wyznaczono podstawowe parametry strumienia powietrza dla 8 bazowych częstotliwości pracy wentylatorów w tym ciśnienie dynamiczne, prędkość oraz wskaźniki jakościowe tunelu: rozkład równomierności prędkości oraz wskaźniki intensywności turbulencji, które odniesiono do średnich arytmetycznych prędkości. W drugim etapie zbadano wpływ regulacji pracy poszczególnych wentylatorów na rozkład pól prędkości w określonej strefie pomiarowej tunelu aerodynamicznego, w której umieszczona zostanie mini siłownia wiatrowa. Zarówno dla układu wyregulowanego jak i bez regulacji w zakresie wyższych prędkości strumienia około 15,80 m·s-1 wartość wskaźnika intensywności turbulencji oscylowała w granicach 1,5%. Regulacja wentylatorów pozwoliła ograniczyć przedziały rozpiętości wskaźników intensywności turbulencji, w całym zakresie prędkości, z 2,8-1,5% do 2,0-1,2%. Przedstawiona analiza wyników badań potwierdziła, że zaproponowane rozwiązanie sterowania pracą poszczególnych wentylatorów umożliwia uzyskanie dostatecznie jednorodnego strumienia powietrza, tak aby można było w nim badać rzeczywiste obiekty mini turbin wiatrowych.

EN

The paper presents experimental research on the character of air stream flow in an open aerodynamic tunnel with a closed measuring chamber, in which the velocity profile was regulated smoothly through 9 independent axial flow fans. Testing the aerodynamic tunnel was carried out in two stages. In the first stage basic parameters of the air stream were determined for 8 base frequencies of fans operation including dynamic pressure, velocity and quality indices of the tunnel: distribution of velocity uniformity and indices of turbulences intensity, which were referred to averages arithmetic velocities. In the second stage, the effect of regulation of particular fans operation on the distribution of velocities fields in a given measuring sphere of the aerodynamic tunnel, where a mini-wind power plant will be placed, were investigated. Both for a regulated as well as a non-regulated system within higher velocities of the stream approx. 15.80 m·s-1 the value of the turbulences intensity index was approx. 1.5%. Control of fans allowed limitation of the range of turbulences intensity indices for the whole range of velocities from 2.8-1.5% to 2.0-1.2%. The presented analysis of results proved that the suggested solution of control of particular fans allows obtaining sufficiently homogeneous air stream, such that real objects of mini - wind power turbines could be tested there.