Wyniki wyszukiwania - Biblioteka Nauki

1

Badanie uziarnienia pigmentów ceramicznych

100%

Dziubak C. , Taźbierski P.

|

tom nr 3-4

50--54

PL

W technologiach ceramicznych uziarnienie substratów – surowców i półproduktów – ma istotne znaczenie dla jakości wytwarzanych tworzyw. Zwłaszcza pomiar wielkości ziaren poniżej 100 μm nabiera szczególnego znaczenia. W przypadku pigmentów ceramicznych od uziarnienia zależą ich parametry barwy, a w konsekwencji walory estetyczne i cechy użytkowe dekorowanych wyrobów.

EN

In the ceramic substrate technology the particle size of raw materials and semi-finished products is essential for the quality of the produced materials. Especially the measurement of particle size less than 100 microns is of particular importance. In the case of ceramic pigments, the color parameters and, consequently, aesthetic and functional characteristics of decorated products depend on their grain size.

2

Badania nad technologią wytwarzania materiałów podsadzkowych (propantów) stosowanych przy wydobyciu gazu łupkowego. Cz.3 – Otrzymywanie propantów poprzez suszenie zawiesiny w suszarni rozpyłowej

80%

Jakubiuk T. , Łosiewicz A. , Taźbierski P.

|

tom R. 8, nr 23

39--48

PL

Do prób otrzymywania materiału podsadzkowego poprzez suszenie zawiesiny wodnej ujednorodnionych surowców mineralnych wykorzystano suszarnię rozpyłową D 20. Skład surowcowy zawiesiny ustalono po przeprowadzeniu badań właściwości fizykochemicznych wypalonych zestawów surowcowych wykonanych w skali mikro. Badano temperaturę spiekania, gęstość, porowatość, wytrzymałość mechaniczną i odporność chemiczną. Do sporządzenia zestawów jako surowiec podstawowy wykorzystano odpady powstające w elektrociepłowniach warszawskich, które domieszkowano glinami „Janina” i „Zapniów”. Badania poszczególnych właściwości prowadzono na beleczkach prasowanych pod niskim ciśnieniem w laboratoryjnej prasie hydraulicznej i wypalanych w piecu elektrycznym. Do prasowania próbek badawczych wykorzystywano granulat otrzymywany ręcznie poprzez posługiwanie się sitem. W oparciu o recepturę zestawu, który charakteryzował się niską temperaturą spiekania, dużą wytrzymałością i odpornością chemiczną, sporządzono zawiesinę do suszenia rozpyłowego. Podczas suszenia tak dobierano reologię zawiesiny i parametry suszenia, aby otrzymać maksymalną ilość granulatu w przedziale 0,2–0,7 mm. Otrzymany granulat wypalono w piecu rurowym w ustalonej wcześniej temperaturze spiekania i przekazano do Instytutu Nafty i Gazu w celu zbadania przydatności do wykorzystania go jako materiał podsadzkowy.

EN

The proppants were prepared by drying aqueous suspension of homogenous mineral material in spray dryer-D 20. The composition of raw materials was determined by conducting physicochemical test of fired specimen in a laboratory scale. Sintering temperature, density, porosity, mechanical strength and chemical resistance were investigated. Waste from Warsaw Power Plants with addition of „Janina” and „Zapniów” clays were used for preparation of specimen sets. Individual properties were determined on specimens pressed at law pressure in a laboratory hydraulic press and fired in an electric furnace. Test specimens were prepared from granulate sieved manually and pressed. Based on row materials composition, which showed low sintering temperature, high strength and high chemical resistance, a suspension for spray drying was prepared. During the drying process, both the rheology of the suspension and drying parameters, were being chosen so as to obtain the maximum amount of granulate in the range of 0,2–0,7 mm grain size. The final granulate was fired in a tube furnace at a predetermined sintering temperature and delivered to the Institute of Oil and Gas in order to investigate the suitability for use as a proppants.

3

Metoda obniżenia temperatury spiekania tworzyw alundowych zawierających powyżej 90% Al2O3

80%

Jakubiuk T. , Łosiewicz A. , Taźbierski P.

|

2014

|

tom R. 65, nr 2

10--12

PL

W artykule przedstawiono prace prowadzone w Instytucie Ceramiki i Materiałów Budowlanych nad obniżeniem temperatury spiekania tworzywa alundowego zawierającego 93% wagowych Al2O3, wykorzystywanego do produkcji mielników ceramicznych i wykładzin odpornych na ścieranie stosowanych w młynach kulowych i liniach przesyłowych transportu pneumatycznego. Przedstawiono sposób prowadzenia prac nad wytworzeniem, ustaleniem temperatury spiekania i badaniem właściwości otrzymanych materiałów ceramicznych. Właściwości te odnoszono do próbek formowanych z tworzywa wzorcowego Al93.

EN

The paper describes work carried out at the Institute of Ceramics and Building Materials on lowering the sintering temperature alumina material containing 93 wt% Al2O3, used for the production of ceramic grinding media and wear resistant linings used in ball mills and transmission lines of pneumatic transport systems. The way of conducting work on developing, fixing and testing the sintering temperature properties of the ceramic materials were presented. Obtained properties were compared to samples made of referenced material Al93.