Dye decomposition on P25 with enhanced adsorptivity

100%

Janus M. , Wawrzyniak B. , Tryba B. , Morawski A.

Polish Journal of Chemical Technology

2008

tom 10

nr 2

11-16

The preparation method and the activity of the TiO2-P25/N doped photocatalyst based on commercial titanium dioxide (TiO2 Aeroxide® P-25 Degussa, Germany) are presented. For the TiO2-P25/N preparation TiO2-P25 and gaseous ammonia were kept in a pressure reactor (10 bars) for 4 hours at the temperature of 200°C. This modification process changed the chemical structure of the TiO2 surface. The formation of NH4+ groups was confirmed by the FTIR measurements. Two bands in the range of ca. 1430 - 1440 cm-1 attributed to bending vibrations of NH4+ could be observed on the FTIR spectra of the catalysts modified with ammonia and the band attributed to the hydroxyl groups at 3300 - 3500 cm-1, which were not reduced after N-doping. The photocatalytic activity of the photocatalysts was checked through the decomposition of two dyes under visible light irradiation. The modified TiO2 thus prepared samples were more active than TiO2-P25 for the decomposition of dyes under visible light irradiation.

Preparation of the TiO2photocatalyst using pressurized ammonia

100%

Wawrzyniak B. , Janus M. , Grzmil B. , Morawski A.

Polish Journal of Chemical Technology

2007

tom 9

nr 1

51-56

The industrial hydrated amorphous titanium dioxide (TiO2ċ xH2O) was modified by treatment inside a chemical reactor under elevated pressure at low temperatures for 4 hours in an ammonia atmosphere. On the basis of the FTIR/DRS analysis the presence of nitrogen was confirmed. The XRD patterns of all of the catalysts exhibit mainly the diffraction lines of anatase phases. The photocatalytic activity of the modified photocatalysts was determined and compared to TiO2-P25 (Degussa, Germany). The high rate of phenol and dye degradation was obtained for the catalysts modified at 180°/15atm. TiO2-P25 showed similar activity in phenol decomposition like TiO2-15bar, whereas it was more active in dye decomposition.