Influence of the Yarn Fineness and Stitch Length of Polyester Knitted Fabric on the Dielectric Constant

100%

Liu Y. , Li W. , Zhao X.

|

2019

|

tom Vol. 27, no. 6 (138)

63--66

EN

The influence of the yarn fineness and stitch length of polyester knitted fabrics on the dielectric constant was investigated by the single factor test method. As a result of the investigation, polyester knitted fabric parameters were chosen so as to obtain a polyester knitted fabric with the maximum real part and imaginary part of the dielectric constant. The results show that when the yarn fineness is 59 tex and the mark of the stitch length is 75, the polyester knitted fabric displayed the maximum real part and imaginary part of the dielectric constant. Finally, the polyester knitted fabric with these parameters had good microwave absorbing properties.

PL

W pracy, metodą testu jednoczynnikowego, badano wpływ grubości przędzy i długości oczka dzianin poliestrowych na stałą dielektryczną. W wyniku badań dobrano parametry dzianiny poliestrowej, tak aby uzyskać dzianinę o maksymalnej stałej dielektrycznej. Wyniki pokazały, że przy grubości przędzy wynoszącej 59 tex i długości oczka 75, dzianina poliestrowa charakteryzowała się najwyższą stałą dielektryczną i miała dobre właściwości pochłaniania mikrofal.

2

Study on the Thermal Insulation Performance of PAN Pre-Oxidised Fibre Felts

100%

Zhao X. , Liu Y. , Liang T.

|

tom Vol. 28, no. 3 (141)

27--37

EN

In this paper, an orthogonal experiment of 3 factors and 3 levels was firstly designed to prepare PAN pre-oxidised fibre felts with good thermal insulation properties; the range method was used to analyse the result of the orthogonal experiment, and finally the tensile properties and thermal stability were tested. Finally, pre-oxidised fibre felt composites for the coating of silica aerogel were prepared using the coating process to compound silica aerogel on re-oxidised fibre felts. Firstly, the influence of the content of silica aerogel on the heat insulation performance of the coated composite materials was analysed, and then a test of the coefficient of thermal conductivity, an experiment on the back temperature, and characterisations of the tensile properties and thermal stability of the composite coating of pre-oxidised fibre felt composites of the coating of silica aerogel were carried out. Results showed that through analysis of the orthogonal experiment, we can state that the best preparation process of pre-oxidised fibre needled felts was as follows: needle number – 2, needle depth – 8 mm, and needle frequency – 140 times/min. The transverse tensile strength of PAN pre-oxidised fibre needled felts prepared by crossly webbing of PAN pre-oxidised fibres was superior to the longitudinal tensile strength; thermogravimetric analysis showed that the pre-oxidised fibre needled felts had excellent thermal stability. The coefficient of thermal conductivity of the aerogel coating of the composites firstly decreased and then increased with an increase in the content of aerogel. Coated composites had the lowest coefficient of thermal conductivity when the aerogel content was 4% wt. At temperatures of 100 °C, 150 °C and 200 °C, the heating rate of the transient-state back temperature and the steady-state average temperature were both the lowest when the aerogel content was 6% wt.

PL

W artykule zaprojektowano ortogonalny eksperyment z 3 czynnikami i 3 poziomami w celu przygotowania wstępnie utlenionych filców PAN o dobrych właściwościach termoizolacyjnych; do analizy wyników eksperymentu ortogonalnego zastosowano metodę zakresu, a na koniec przetestowano właściwości rozciągania i stabilność termiczną. Najpierw przeanalizowano wpływ zawartości aerożelu krzemionkowego na właściwości izolacji cieplnej powleczonych materiałów kompozytowych, a następnie wykonano test współczynnika przewodności cieplnej, przeanalizowano też charakterystykę właściwości rozciągania i stabilności termicznej powłoki kompozytowej wstępnie utlenionych kompozytów filcowych. Wyniki pokazały, że poprzez analizę eksperymentu ortogonalnego można stwierdzić, że najlepszy proces przygotowania filców igłowanych charakteryzuje się następującymi parametrami: liczba igły – 2, głębokość igły – 8 mm i częstotliwość igły – 140 razy/min. Wytrzymałość poprzeczna na rozciąganie igłowanych filców z włókien PAN była lepsza niż wytrzymałość na rozciąganie wzdłużne; analiza termograwimetryczna wykazała, że igłowane filce z wstępnie utlenionego włókna miały doskonałą stabilność termiczną. Współczynnik przewodności cieplnej powłoki aerożelowej kompozytów najpierw zmniejszył się, a następnie wzrósł wraz ze wzrostem zawartości aerożelu. Powlekane kompozyty miały najniższy współczynnik przewodności cieplnej, gdy zawartość aerożelu wynosiła 4% wag. W temperaturach 100, 150 i 200 °C szybkość ogrzewania i średnia temperatura w stanie ustalonym były najniższe, gdy zawartość aerożelu wynosiła 6% wag.

3

Influence of the Content of Nickel Powders on the Electromagnetic Properties of SingleLayer Coated Polyester-Cotton Plain Weave Fabric

88%

Liu Y. , Xue H. , Wang C. , Han X. , Zhao X.

|

tom Vol. 30, no. 5

47--52

EN

A coated composite was prepared on polyester-cotton plain weave fabric, using PU2540 polyurethane as the matrix. The influences of the content of nickel powders on the dielectric constant (the real and imaginary parts and loss tangent value), reflection loss and shielding effectiveness of single-layer coated composites were mainly investigated. The results showed that within the frequency range of 1-1000 MHz, the value of the real part of the dielectric constant of the coated composites was the largest, and the polarisation ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 15-225 MHz, the value of the imaginary part of the dielectric constant of the coated composites was the largest and the loss ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 250-800 MHz, the loss tangent value of the dielectric constant of coated composites was the largest, and the attenuation ability with regard to electromagnetic waves was the strongest when the content of nickel powders was 40%. Within the frequency range of 1220-3000 MHz, the reflection loss value was the smallest when the content of nickel powders was 40%, and its absorption ability with regard to electromagnetic waves was the strongest. Within the frequency range of 760-3000 MHz, the shielding effectiveness of the coated composite was the largest when the content of nickel powders was 40%.

4

Study of the Dielectric Properties and Conductivity of Double Coated Glass Fibre Felt Composites

75%

Liu Y. , Wang C. , Ma Y. , Liu Y. , Wu H. , Zhao X.

|

2021

|

tom Vol. 29, no. 4 (148)

75--80

EN

Graphite/talcum powder double-coated glass fibre felt composites were prepared using glass fibre felt as the base material, graphite as the surface absorbing agent, talcum powder as the underlying absorbing agent, epoxy resin E44 as the adhesive and low molecular 650 polyamide as the curing agent. The influences of the surface graphite content and underlying talcum powder content on the dielectric properties and conductivity of glass fibre felt composites were the main focus of the investigation. Results showed that when the frequency is less than 103 Hz, the values of the real and imaginary parts of the dielectric constant for double-coated glass fibre felt composites are largest when the surface graphite content is 50%. When the frequency is larger than 106 Hz, the value of the real part of the conductivity is largest when the graphite contents are 40% and 50%. When the frequency is less than 104Hz, the real part of the dielectric constant of the glass fiber mat composites is the largest when the talc content is 40%, and when talc content is 60%, the imaginary part of dielectric constant of glass fiber mat composites is the largest. The maximum loss tangent value for the composites occurs when the talcum powder content is 40%. When the frequency is larger, the value of the real part of the conductivity increases gradually.

PL

W pracy przygotowano podwójnie powlekane kompozyty filcu z włókna szklanego w postaci grafit/talk. Użyto filcu z włókna szklanego jako materiału bazowego, grafitu jako powierzchniowego środka pochłaniającego, talku jako podstawowego środka pochłaniającego, żywicy epoksydowej E44 jako kleju i poliamidu 650 o niskiej masie cząsteczkowej jako środek utwardzającego. Głównym przedmiotem badań było określenie wpływu zawartości grafitu powierzchniowego oraz zawartości proszku talku na właściwości dielektryczne i przewodność kompozytów z filcu z włókna szklanego. Wyniki wykazały, że gdy częstotliwość jest mniejsza niż 103 Hz, wartości części rzeczywistej i urojonej stałej dielektrycznej dla podwójnie powlekanych kompozytów z filcu z włókna szklanego są największe, gdy zawartość grafitu powierzchniowego wynosi 50%. Gdy częstotliwość jest większa niż 106 Hz, wartość rzeczywistej części przewodnictwa jest największa, gdy zawartość grafitu wynosi 40% i 50%. Maksymalna wartość tangensa strat dla kompozytów występuje, gdy zawartość talku wynosi 40%. Gdy częstotliwość jest większa, wartość rzeczywistej części przewodnictwa stopniowo wzrasta.