The Erosive Wear of Graphene Oxide Reinforced Epoxy Powder Coatings

100%

Grzelka J. , Radziejewska J.

|

tom nr 2

31--42

EN

Powder coatings are organic coatings that protect the metal substrate against corrosion and wear, and play a decorative role. The doping of paints with nanoparticles is intended to create a barrier to corrosive and chemical agents and to increase abrasion resistance. This work tested the erosion resistance of epoxy powder coating with graphene oxide flakes and polyethylene wax covered with a layer of micro diamonds. Two methods of testing resistance to abrasive wear were used, in which the conditions are similar to operating conditions: solid particle impingement (sandblasting) and barrel finisher with ceramic shapes. Mass loss due to erosion in a sandblaster using glass beads with a diameter of 200 µm for the paint with graphene was much lower than for the reference sample. The mass loss of the samples was tested after 15, 30, and 60 seconds of abrasive jet operation. The surface texture was analyzed during the process and after the test. The test in the barrel finisher was carried out twice for different times: for the first series weight loss was measured after 30, 90, and 210 minutes, for the second Vickers hardness at 40 g load after 90 and 210 minutes. The tests showed that the epoxy coating with the addition of graphene oxide has a much higher resistance to erosion under the influence of an abrasive stream than the reference paint, and a similar resistance to erosion in a container smoother. It was found that the paints showed a higher Vickers hardness after the wear test.

PL

Farby proszkowe są powłokami organicznymi zabezpieczającymi podłoże najczęściej metalowe przed korozją, zużyciem oraz pełnią rolę dekoracyjną. Domieszkowanie farb nanocząstkami ma na celu stworzenie bariery dla czynników korozyjnych i chemicznych oraz zwiększenie wytrzymałości na ścieranie. W niniejszej pracy zbadano odporność na erozję epoksydowych farb proszkowych z płatkami tlenku grafenu oraz woskiem polietylenowym pokrytym warstwą mikrodiamentów. Zastosowano dwie metody badań odporności na zużycie ścierne, w których warunki są zbliżone do eksploatacyjnych: strumieniowo-ścierną (piaskowanie) oraz w rotacyjnej wygładzarce z kształtkami ceramicznymi. Utrata masy pod wpływem erozji w piaskarce z użyciem kulek szklanych o średnicy 200 µm dla farby z grafenem była dużo niższa niż dla próbki odniesienia. Ubytek masy próbek badano po 15, 30 i 60 sekundach działania strumienia ściernego. Analizowano teksturę powierzchni w trakcie procesu oraz po teście. Test w wygładzarce przeprowadzono dwukrotnie dla różnych czasów: dla pierwszej serii zmierzono ubytek masy po 30, 90 i 210 minutach, dla drugiej twardość Vickersa przy obciążeniu 40 g po 90 i 210 minutach. Badania wykazały, że farba epoksydowa z dodatkiem tlenku grafenu wykazuje dużo wyższą niż farba odniesienia odporność na erozję pod wpływem strumienia ściernego oraz podobną odporność na erozję w wygładzarce pojemnikowej. Stwierdzono, że farby wykazują wyższą twardość Vickersa po próbie zużycia.

2

The influence of abrasive finishing conditions on the surface texture of Inconel 939 elements made using the 3D printing LPBF method

80%

Wojtiuk E. , Radziejewska J. , Marczak M.

Welding Technology Review

|

2024

|

tom R. 96

34--40

EN

The article presents research on finishing treatment applied to components made of Inconel through 3D printing by Laser Powder Bed Fusion method. Vibration-abrasive machining was carried out using a supporting fluid and various shapes of abrasive. The effects of the processing conditions were analysed based on the surface roughness of the samples and mass loss. The obtained collective results were subjected to comparative analysis with the effects of vibratory-abrasive processing without the use of a processing fluid, as presented in the article. The research has shown that using vibration-abrasive processing, it is possible to reduce the height of surface irregularities by more than three times after four hours of treatment. The intensity of processing was the highest in the first hour of the process. The lowest roughness heights Ra = 1.8 μm were obtained using ceramic balls in the presence of a supporting fluid.

3

Relation between material parameters and contact loading process.

80%

Bartoszewicz A. , Kucharski S. , Radziejewska J. , Starzyński G.

Archive of Mechanical Engineering

|

1999

|

tom Vol. XLVI, nr 3

201-220

EN

The experimental studies of contact deformation and geometrical structure of surfaces of samples of various metals, which had a similar microgeometry, were performed. The tested materials were submited to the contact deformation by the application of three different values of nominal pressure. The result led us to the conclusion that it is not reasonable to describe the behaviour of material during the contact loading process by means of one material parameter as it was proposed in some models presented by other outhors. It is necessary to know the whole stress - strain tension curve or at least the yield point and the yield strength of the tested material.

PL

W pracy przeprowadzono badania odkształceń kontaktowych i struktury geometrycznej powierzchni różnych stopów metali, o zbliżonej wstępnej mikrogeometrii powierzchniBadane próbki poddano odkształceniu kontaktowemu stosując trzy różne naciski nominalne. Analiza przebiegu krzywych zbliżenie - nacisk nominalny dla stopów metali kolorowych wykazała duże różnice wartości zbliżenia całkowitego oraz trwałego po odciążeniu, zgodnie z różnicami własności materiałowych badanych stopów metali. W przypadku stali różnice te nie były tak duże a ich przebiegu nie można było wyjaśnić na podstawie niewielkich różnic twardości. Wyniki badań prowadzą do wniosku, że nie jest możliwe opisywanie zachowania się materiału podczas odkształceń kontaktowych przy pomocy jednego parametru materiałowego, jak to było proponowane w niektórych modelach przedstawianych w literaturze. Do oceny potrzebna jest znajomość całego przebiegu krzywej rozciągania lub co najmniej granicy plastyczności oraz granicy wytrzymałości materiału. Podobnie jest z parametrami opisującymi mikrogeometrię. Zmiany standardowych wielkości są niewielkie, a najbardziej wrażliwym parametrem na odkształcenie i na różnicowanie materiałów odkształcanych jest parametr SR _sk_.